Randomly distributed anti-reflective nanostructures were fabricated on both surfaces of cylindrical lenses and freeform optical elements using a plasma-assisted reactive-ion etching technique. An average spectral transmission of 98% was measured across the wavelength range from 340 to 800 nm. Mid-band full-angle directional scatter measurements show a difference of six orders of magnitude in transmission intensity between specular and off-specular angles. Measurements before and after the etching process show little to no wavefront distortion for the cylindrical lenses. The enhanced transmission optics were used as part of the dual-unit arrayed wide-field astronomical camera system tested on the Harlan J. Smith telescope at the McDonald Observatory, and their performance was contrasted with conventional thin film coated component performance.
more »
« less
Scratch-resistant sapphire nanostructures with anti-glare, anti-fogging, and anti-dust properties
Although there has been significant interest in the novel material properties of bio-inspired nanostructures, engineering them to become mechanically durable remains a significant challenge. This work demonstrates the fabrication of sapphire nanostructures with anti-glare, anti-fogging, anti-dust and scratch-resistant properties. The fabricated nanostructures demonstrated a period of 330 nm and an aspect ratio of 2.1, the highest reported for sapphire thus far. The nanostructured sapphire sample exhibited broadband and omnidirectional antireflection properties, with an enhanced transmission of up to 95.8% at a wavelength of 1360 nm. The sapphire nanostructures also exhibited enhanced wetting performance and could mitigate fogging from water condensation or repel water droplets. Furthermore, owing to their sharp features, the fabricated structures could prevent particulate adhesion and maintain a 98.7% dust-free surface area solely using gravity. Furthermore, nanoindentation and scratch tests indicated that the sapphire nanostructures have an indentation modulus and hardness of 182 GPa and 3.7 GPa, respectively, which are similar to those of bulk glass and scratch-resistant metals such as tungsten. These sapphire nanostructures can be fabricated using high-throughput nanomanufacturing techniques and can find applications in scratch-resistant optics for photonics, electronic displays, and protective windows.
more »
« less
- Award ID(s):
- 2314268
- PAR ID:
- 10585490
- Publisher / Repository:
- Royal Society of Chemistry
- Date Published:
- Journal Name:
- Materials Horizons
- Volume:
- 12
- Issue:
- 6
- ISSN:
- 2051-6347
- Page Range / eLocation ID:
- 1796 to 1807
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Novel tetrafluoro-λ6-sulfanyl-containing oligomers prepared by visible light-promoted addition of 1,4-(bis-chlorotetrafluoro-λ6-sulfanyl) benzene or 1,3-(bis-chlorotetrafluoro-λ6-sulfanyl) benzene to either 1,4-diethynyl benzene or the 1,3-diethynyl isomers form hard, stress resistant thin films on spin casting. The isomeric oligomers were utilized to establish a structure-function relationship for the mechanical properties of films prepared from the oligomers. The Young’s moduli of 145-nm-thick cured films could reach 60 GPa. The measured hardnesses, between 1.57 and 2.77 GPa, were more than double those of polymethyl methacrylate (PMMA) films. Curing of the tetrafluoro-λ6-sulfanyl-containing polymer films by UV irradiation resulted in coatings that exhibited remarkable hardness and modulus with good surface adhesion to silicon.more » « less
-
With the advances in nanofabrication technology, horizontally aligned and well-defined nitrogen-doped ultrananocrystalline diamond nanostripes can be fabricated with widths in the order of tens of nanometers. The study of the size-dependent electron transport properties of these nanostructures is crucial to novel electronic and electrochemical applications. In this paper, 100 nm thick n-type ultrananocrystalline diamond thin films were synthesized by microwave plasma-enhanced chemical vapor deposition method with 5% N2 gas in the plasma during the growth process. Then the nanostripes were fabricated using standard electron beam lithography and reactive ion etching techniques. The electrical transport properties of the free-standing single nanostripes of different widths from 75 to 150 nm and lengths from 1 to 128 μm were investigated. The study showed that the electrical resistivity of the n-type ultrananocrystalline diamond nanostripes increased dramatically with the decrease in the nanostripe width. The nanostripe resistivity was nearly doubted when the width was reduced from 150 nm to 75 nm. The size-dependent variability in conductivity could originate from the imposed diffusive scattering of the nanostripe surfaces which had a further compounding effect to reinforce the grain boundary scattering.more » « less
-
ABSTRACT Multidrug-resistant (MDR) bacteria pose a significant public health challenge, underscoring the urgent need for innovative antibacterial strategies. Bacteriophages (phages), viruses that specifically target bacteria, offer a promising alternative; however, bacterial immune defenses often limit their effectiveness. Developing small-molecule inhibitors of these defenses can facilitate mechanistic studies and serve as adjuvants to enhance phage therapy. Here, we identify novel inhibitors targeting the bacterial cyclic oligonucleotide-based anti-phage signaling system (CBASS) effector Cap5. Cap5 is an HNH endonuclease activated by a cyclic nucleotide to degrade genomic DNA in virally infected cells, leading to cell death through abortive infection. Guided by the crystal structure of the Cap5 SAVED domain bound to its activating ligand, we performed structure-guided virtual screening to identify candidate inhibitors. Biochemical assays revealed that approximately 16% of the top docking hits exhibited inhibitory activity. Further cellular assays demonstrated that one potent compound could enterE. colicells and inhibit Cap5 activity. Our integrated approach—combining structure-based virtual screening with biochemical validation—provides a robust framework for discovering small-molecule inhibitors of bacterial immune defenses to advance adjunctive therapies and deepen our understanding of phage-bacteria interactions.more » « less
-
Abstract Sapphire is an attractive material that stands to benefit from surface functionalization effects stemming from micro/nanostructures. Here we investigate the use of ultrafast lasers for fabricating sapphire nanostructures by exploring the relationship between irradiation parameters, morphology change, and selective etching. In this approach a femtosecond laser pulse is focused on the substrate to change the crystalline morphology to amorphous or polycrystalline, which is characterized by examining different vibrational modes using Raman spectroscopy. The irradiated regions are removed using a subsequent hydrofluoric acid etch. Laser confocal measurements quantify the degree of selective etching. The results indicate a threshold laser pulse intensity required for selective etching. This process was used to fabricate hierarchical sapphire nanostructures over large areas with enhanced hydrophobicity, with an apparent contact angle of 140 degrees, and a high roll-off angle, characteristic of the rose petal effect. Additionally, the structures have high broadband diffuse transmittance of up to 81.8% with low loss, with applications in optical diffusers. Our findings provide new insights into the interplay between the light-matter interactions, where Raman shifts associated with different vibrational modes can predict selective etching. These results advance sapphire nanostructure fabrication, with applications in infrared optics, protective windows, and consumer electronics.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1039/d4mh01844c