Current methods for modeling hybrid additive manufacturing are computationally inefficient for use in optimization algorithms. An analytical tool is needed to understand how cycling thermal and mechanical loads via 3D printing and cold working reshapes cumulative residual stress within a build volume. A novel analytical model was developed that couples beam theory and superposition to rapidly predict cumulative residual stress. Modeling results were experimentally validated on AlSi10Mg after laser shock peening prescribed layers during powder bed fusion. Results demonstrated a vertically translating heat-affected zone, and the use of beam-based superposition accurately accounted for residual stress redistribution from cyclic printing and peening.
more »
« less
Modeling thermal and mechanical cancellation of residual stress from hybrid additive manufacturing by laser peening
Additive manufacturing (AM) of metals often results in parts with unfavorable mechanical properties. Laser peening (LP) is a high strain rate mechanical surface treatment that hammers a workpiece and induces favorable mechanical properties. Peening strain hardens a surface and imparts compressive residual stresses improving the mechanical properties of a material. This work investigates the role of LP on layer-by-layer processing of 3D printed metals using finite element analysis. The objective is to understand temporal and spatial residual stress development after thermal and mechanical cancellation caused by cyclically coupling printing and peening. Results indicate layer peening frequency is a critical process parameter affecting residual stress redistribution and highly interdependent on the heat generated by the printing process. Optimum hybrid process conditions were found to exists that favorably enhance mechanical properties. With this study, hybrid-AM has ushered in the next evolutionary step in AM and has the potential to profoundly change the way high value metal goods are manufactured.
more »
« less
- PAR ID:
- 10589288
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- Nanotechnology and Precision Engineering
- Volume:
- 2
- Issue:
- 2
- ISSN:
- 1672-6030
- Format(s):
- Medium: X Size: p. 49-60
- Size(s):
- p. 49-60
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract In this research, a room temperature multicycle nanoindentation technique was implemented to evaluate the effects of the laser peening (LP) process on the surface mechanical behavior of additively manufactured (AM) Inconel 625. Repetitive deformation was introduced by loading-unloading during an instrumented nanoindentation test on the as-built (No LP), 1-layer, and 4-layer laser peened (1LP and 4LP) conditions. It was observed that laser-peened specimens had a significantly higher resistance to penetration of the indenter and lower permanent deformation. This is attributed to the pre-existing dislocation density induced by LP in the material which affects the dislocation interactions during the cyclic indentation. Moreover, high levels of compressive stresses, which are greater in the 4LP specimen than the 1LP specimen, lead to more effective improvement of surface fatigue properties. The transition of the material response from elastic-plastic to almost purely elastic in 4LP specimens was initiated much earlier than it did in the No LP, and 1LP specimens. In addition to the surface fatigue properties, hardness and elastic modulus were also evaluated and compared.more » « less
-
null (Ed.)Additive manufactured (AM) magnesium alloys corrode rapidly due to tensile stress and coarse microstructures. Cyclically combining (hybridizing) additive manufacturing with interlayer ultrasonic peening was proposed as a solution to improve corrosion resistance of additive manufactured magnesium WE43 alloy through strengthening mechanisms and compressive residual stress. Applying interlayer peening work hardened discrete layers and formed a glocal integrity of regional grain refinement and subsurface compressive residual stress barriers. Tensile residual stress that typically accelerates corrosion decreased 90%. Results showed time-resolved control over corrosion was attainable by interlayer peening, and local corrosion within print cells decreased 57% with respect to as-printed WE43.more » « less
-
Abstract A novel high‐temperature laser shock peening (HT‐LSP) process was applied to polycrystalline α‐SiC to improve the mechanical performance. HT‐LSP prevents microcrack formation on the surface while induces plastic deformation in the form of dislocation slip on the basal planes, which may be caused by the combination of high shock pressure and a lower critical resolved shear stress at 1000℃. A maximum compressive residual stress of 650 MPa, measured with Raman spectroscopy, was introduced into the surface of α‐SiC by HT‐LSP, which can increase the nanohardness and in‐plane fracture toughness of α‐SiC by 8% and 36%, respectively. This work presents a fundamental base for the promising applications of HT‐LSP to brittle ceramics to increase their plasticity and mechanical properties.more » « less
-
Single crystal Ni-based superalloys are often used to create gas turbine engine blades for their high strength under intense thermo-mechanical loading. Though they are remarkably capable under these conditions, a particular class of premature failure mechanisms known as surface-initiated damage mechanisms can lead to the early fracture of an otherwise healthy blade. This review paper discusses the current progress of post-processing techniques that can greatly mitigate the potency of surface-initiated damage mechanisms. In particular, laser peening (LP) is of significant interest due to the relatively low amount of cold work it induces, greater depth of compressive residual stresses than other cold working methods, ability to accommodate complex part geometries, and the minuscule effect it has on surface roughness. The residual stresses imparted by LP can greatly hinder crack growth and consequently allow for enhanced fatigue life. Given that turbine blades (constructed with single crystal Ni-based superalloys) are prone to fail by these mechanisms, LP could be a worthy choice for increasing their service lives. For this reason, initiative has been taken to better understand the mechanical and microstructural modifications imparted by LP on single crystal Ni-based superalloys and a summary of these investigations are presented in this review. Results from several works show that this class of alloy responds well to LP treatment with improvements such as ~30–50% increase in microhardness, 72% increase in low cycle fatigue life, and elevated resistance to hot corrosion. The primary objective of this review is to provide insight into current state-of-the-art LP techniques and summarize the findings of numerous works which have utilized LP for increasing the service lives of single crystal Ni-based superalloy components.more » « less