Ru(0001) and Co(0001) films with thickness d ranging from 5 to 300 nm are sputter deposited onto Al2O3(0001) substrates in order to quantify and compare the resistivity size effect. Both metals form epitaxial single crystal layers with their basal planes parallel to the substrate surface and exhibit a root-mean-square roughness < 0.4 nm for Ru and < 0.9 nm for Co. Transport measurements on these layers have negligible resistance contributions from roughness and grain boundary scattering which allows direct quantification of electron surface scattering. The measured resistivity ρ vs d is well described by the classical Fuchs-Sondheimer model, indicating a mean free path for transport within the basal plane of λ = 6.7 ± 0.3 nm for Ru and λ = 19.5 ± 1.0 nm for Co. Bulk Ru is 36% more resistive than Co; in contrast, Ru(0001) layers with d ≤ 25 nm are more conductive than Co(0001) layers, which is attributed to the shorter λ for Ru. The determined λ-values are utilized in combination with the Fuchs-Sondheimer and Mayadas-Shatzkes models to predict and compare the resistance of polycrystalline interconnect lines, assuming a grain boundary reflection coefficient R = 0.4 and accounting for the thinner barrier/adhesion layers available to Ru and Co metallizations. This results in predicted 10 nm half-pitch line resistances for Ru, Co, and Cu of 1.0, 2.2, and 2.1 kΩ/µm, respectively.
more »
« less
Electron scattering at interfaces in Ru(0001)/Co(0001) multilayers
Electron transport measurements on 60-nm-thick multilayers containing N = 2–58 individual Ru and Co layers are employed to quantify the specific resistance of Ru/Co interfaces. Sputter deposition on Al2O3(0001) at Ts = 400 °C leads to a 0001 preferred orientation with x-ray diffraction (XRD) Ru and Co 0002 peaks that shift closer to each other with increasing N, suggesting interfacial intermixing. The intermixing is quantified by x-ray reflectivity (XRR) and confirmed by an XRD Ru/Co alloy peak that develops during in situ synchrotron annealing as well as for deposition at a higher Ts = 600 °C. The room-temperature resistivity increases from 15.0 to 47.5 μΩ cm with decreasing superlattice period Λ = 60–2 nm. This is attributed to increasing electron scattering at the intermixed metal interfaces. The transport data are well described by a parallel conductor model that treats metal layers and the intermixed alloy as parallel resistors, where the resistivity of the intermixed alloy of 60.4 μΩ cm is determined from a co-deposited Ru/Co sample. Data fitting provides values for the effective thickness of the intermixed interface of 16.8 nm, in good agreement with the XRR value, yielding a Ru/Co contact resistance of 8.5 × 10−15 Ω m2 for interfaces deposited at 400 °C. The overall results show that the Ru/Co contact resistance is dominated by a high-resistivity interfacial alloy and, therefore, is a strong function of the deposition process, particularly the processing temperature.
more »
« less
- Award ID(s):
- 2328906
- PAR ID:
- 10593668
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- Journal of Applied Physics
- Volume:
- 137
- Issue:
- 2
- ISSN:
- 0021-8979
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Epitaxial W–Mo multilayers are employed as a model system to demonstrate how resistivity measurements parallel to metal–metal interfaces can be used to quantify the specific interface resistance without sub-10-nm patterning that would be required for direct transport measurements across the interface. 50-nm-thick epitaxial multilayer stacks containing 2–60 individual W(001) and Mo(001) layers are deposited on MgO(001) substrates and their resistivity ρ measured as a function of superlattice period Λ at 293 and 77 K. The measured room temperature ρ increases from 7.10 to 8.62 μΩ cm with decreasing Λ = 50–1.7 nm, which is attributed to the increasing electron-interface scattering. The semiclassical Fuchs–Sondheimer model for surface scattering dramatically overestimates the resistivity, which is attributed to coherent electron transmission across multiple interfaces. A new Boltzmann transport model treats each interface as a boundary condition where electrons either scatter diffusely or traverse without momentum loss with a probability T for the first encountered interface and with 100% transmission at subsequent interfaces until they are relaxed by a bulk scattering event. This model has a single unknown parameter T, which becomes the fitting parameter for experimental data analysis, yielding a temperature-independent T = 0.8 ± 0.1 and a corresponding contact resistance at the W(001)–Mo(001) interface of 2.6 × 10−16 Ω m2.more » « less
-
This work outlines conditions suitable for the heteroepitaxial growth of Cr2O3(0001) films (1.5–20 nm thick) on a Ru(0001)-terminated substrate. Optimized growth is achieved by sputter deposition of Cr within a 4 mTorr Ar/O2 20% ambient at Ru temperatures ranging from 450 to 600 °C. The Cr2O3 film adopts a 30° rotated honeycomb configuration with respect to the underlying Ru(0001) substrate and exhibits a hexagonal lattice parameter consistent with that for bulk Cr2O3(0001). Heating to 700 °C within the same environment during film preparation leads to Ru oxidation. Exposure to temperatures at or above 400 °C in a vacuum, Ar, or Ar/H2 3% leads to chromia film degradation characterized by increased Ru 3d XPS intensity coupled with concomitant Cr 2p and O 1s peak attenuations when compared to data collected from unannealed films. An ill-defined but hexagonally well-ordered RuxCryOz surface structure is noted after heating the film in this manner. Heating within a wet Ar/H2 3% environment preserves the Cr2O3(0001)/Ru(0001) heterolayer structure to temperatures of at least 950 °C. Heating an Ru–Cr2O3–Ru heterostacked film to 950 °C within this environment is shown by cross-sectional scanning/transmission electron microscopy (S/TEM) to provide clear evidence of retained epitaxial bicrystalline oxide interlayer structure, interlayer immiscibility, and epitaxial registry between the top and bottom Ru layers. Subtle effects marked by O enrichment and O 1s and Cr 2p shifts to increased binding energies are noted by XPS in the near-Ru regions of Cr2O3(0001)/Ru(0001) and Ru(0001)/Cr2O3(0001)/Ru(0001) films after annealing to different temperatures in different sets of environmental conditions.more » « less
-
Thin (40–150 nm), highly doped n+ (1019–1020 cm−3) Ga2O3 layers deposited using pulsed laser deposition (PLD) were incorporated into Ti/Au ohmic contacts on (001) and (010) β-Ga2O3 substrates with carrier concentrations between 2.5 and 5.1 × 1018 cm−3. Specific contact resistivity values were calculated for contact structures both without and with a PLD layer having different thicknesses up to 150 nm. With the exception of a 40 nm PLD layer on the (001) substrate, the specific contact resistivity values decreased with increasing PLD layer thickness: up to 8× on (001) Ga2O3 and up to 16× on (010) Ga2O3 compared with samples without a PLD layer. The lowest average specific contact resistivities were achieved with 150 nm PLD layers: 3.48 × 10−5 Ω cm2 on (001) Ga2O3 and 4.79 × 10−5 Ω cm2 on (010) Ga2O3. Cross-sectional transmission electron microscopy images revealed differences in the microstructure and morphology of the PLD layers on the different substrate orientations. This study describes a low-temperature process that could be used to reduce the contact resistance in Ga2O3 devices.more » « less
-
CuTi layers are co-sputter deposited on 20-nm-SiO2/Si(001) wafers at 350 ℃ to quantify their stability in direct contact with a dielectric and to explore the potential of CuTi as barrier- and liner-free interconnect metal. X-ray diffraction pole figures indicate a preferred 001 out-of-plane crystalline orientation and Rutherford backscattering confirms a stoichiometric composition. Vacuum annealing tests at 450 ℃ of CuTi layers indicate considerably higher thermal stability than for pure Cu layers, including negligible dewetting observed by scanning electron microscopy and negligible intermixing with the oxide substrate quantified by photoelectron spectroscopy. Four-point bend tests show a 25% higher interfacial toughness for CuTi/SiO2 than Cu/SiO2 interfaces. CuTi/SiO2 samples also exhibit a 300-times longer failure time than Cu/SiO2 during time-dependent dielectric breakdown tests using an externally applied 3 MV/cm electric field. The higher stability of CuTi in comparison to Cu is attributed to a higher cohesive energy in combination with an atomically thin self-limiting Ti oxide layer at the CuTi/SiO2 interface.more » « less