We demonstrate the epitaxial growth of the first two members, and the n=∞ member of the homologous Ruddlesden–Popper series of Ban+1InnO2.5n+1 of which the n=1 member was previously unknown. The films were grown by suboxide molecular-beam epitaxy where the indium is provided by a molecular beam of indium-suboxide [In2O (g)]. To facilitate ex situ characterization of the highly hygroscopic barium indate films, a capping layer of amorphous SiO2 was deposited prior to air exposure. The structural quality of the films was assessed by x-ray diffraction, reflective high-energy electron diffraction, and scanning transmission electron microscopy.
more »
« less
Synthesis of metastable Ruddlesden–Popper titanates, ( A TiO3) n A O, with n ≥ 20 by molecular-beam epitaxy
We outline a method to synthesize (ATiO3)nAO Ruddlesden–Popper phases with high-n, where the A-site is a mixture of barium and strontium, by molecular-beam epitaxy. The precision and consistency of the method described is demonstrated by the growth of an unprecedented (SrTiO3)50SrO epitaxial film. We proceed to investigate barium incorporation into the Ruddlesden–Popper structure, which is limited to a few percent in bulk, and we find that the amount of barium that can be incorporated depends on both the substrate temperature and the strain state of the film. At the optimal growth temperature, we demonstrate that as much as 33% barium can homogeneously populate the A-site when films are grown on SrTiO3 (001) substrates, whereas up to 60% barium can be accommodated in films grown on TbScO3 (110) substrates, which we attribute to the difference in strain. This detailed synthetic study of high n, metastable Ruddlesden–Popper phases is pertinent to a variety of fields from quantum materials to tunable dielectrics.
more »
« less
- Award ID(s):
- 2104918
- PAR ID:
- 10594639
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- APL Materials
- Volume:
- 10
- Issue:
- 9
- ISSN:
- 2166-532X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Homologous series are layered phases that can have a range of stoichiometries depending on an index n. Examples of perovskite-related homologous series include (ABO3)nAO Ruddlesden–Popper phases and (Bi2O2) (An−1BnO3n+1) Aurivillius phases. It is challenging to precisely control n because other members of the homologous series have similar stoichiometry and a phase with the desired n is degenerate in energy with syntactic intergrowths among similar n values; this challenge is amplified as n increases. To improve the ability to synthesize a targeted phase with precise control of the atomic layering, we apply the x-ray diffraction (XRD) approach developed for superlattices of III–V semiconductors to measure minute deviations from the ideal structure so that they can be quantitatively eradicated in subsequent films. We demonstrate the precision of this approach by improving the growth of known Ruddlesden–Popper phases and ultimately, by synthesizing an unprecedented n = 20 Ruddlesden–Popper phase, (ATiO3)20AO where the A-site occupancy is Ba0.6Sr0.4. We demonstrate the generality of this method by applying it to Aurivillius phases and the Bi2Sr2Can–1CunO2n+4 series of high-temperature superconducting phases.more » « less
-
GdFe₀.₅Cr₀.₅O₃ (GFCO) is a single-phase magnetoelectric multiferroic at temperatures close to ambient. Epitaxial thin films of this orthorhombic perovskite would offer the possibility of tuning its electrical and magnetic properties through control of strain and interface effects. Here, 200 nm thick GFCO thin films have been grown on (001) SrTiO3 substrates by solution synthesis and the microstructures have been investigated by cross-sectional transmission electron microscopy. The GFCO films are epitaxial but exhibit a mixture of three different orientation relationships in the form of domains ≈50 nm in diameter. Geometric analyses of the lattice matching show that the misfits for these domains would be tensile with magnitudes of less than 2 %. Pockets of a SrCrO4 reaction product form at the film/substrate interface and do not exhibit any simple orientation with the adjacent phases. The product morphology indicates that the outward diffusion of Sr is more rapid than the inward diffusion of Cr, and this is related to the microstructures of the surrounding phases. These data show that epitaxial films of GFCO can be obtained via this route, but careful control of process parameters would be required to produce single-domain films, and alternate substrates or buffer layers would be needed to inhibit SrCrO4 formation.more » « less
-
We combine state-of-the-art oxide epitaxial growth by hybrid molecular beam epitaxy with transport, x-ray photoemission, and surface diffraction, along with classical and first-principles quantum mechanical modeling to investigate the nuances of insulating layer formation in otherwise high-mobility homoepitaxial n-SrTiO3(001) films. Our analysis points to charge immobilization at the buried n-SrTiO3/undoped SrTiO3(001) interface as well as within the surface contamination layer resulting from air exposure as the drivers of electronic dead-layer formation. As Fermi level equilibration occurs at the surface and the buried interface, charge trapping reduces the sheet carrier density (n2D) and renders the n-STO film insulating if n2D falls below the critical value for the metal-to-insulator transition.more » « less
-
We report on the dielectric response of epitaxial BaSnO3 films grown on Nb-doped SrTiO3 (001) substrates using a hybrid molecular beam epitaxy approach. Metal-insulator-metal capacitors were fabricated to obtain frequency- and temperature-dependent dielectric constant and loss. Irrespective of film thickness and cation stoichiometry, the dielectric constant obtained from Ba1−xSn1−yO3 films remained largely unchanged at 15-17 and was independent of frequency and temperature. A loss tangent of ∼1 × 10−3 at 1 kHz < f < 100 kHz was obtained for stoichiometric films, which increased significantly with non-stoichiometry. Using density functional theory calculations, these results are discussed in the context of point defect complexes that can form during film synthesis.more » « less