We report on a novel TaNbZrHfTi-based high entropy alloy (HEA) which demonstrates distinctive dual-phase superconductivity. The HEA was synthesized under high pressures and high temperatures starting from a ball milled mixture of elemental metals in a large-volume Paris–Edinburgh cell with P ≈ 6 GPa and T = 2300 K. The synthesized HEA is a phase mixture of BCC (NbTa)0.45(ZrHfTi)0.55 with Tc1 = 6 K and FCC (NbTa)0.04(ZrHfTi)0.96 with Tc2 = 3.75 K. The measured magnetic field parameters for the HEA are lower critical field, Hc1(0) = 31 mT, and a relatively high upper critical field, Hc2(0) = 4.92 T. This dual-phase system is further characterized by the presence of a second magnetization peak, or the fishtail effect, observed in the virgin magnetization curves. This phenomenon, which does not distort the field-dependent magnetization hysteresis loops, suggests intricate pinning mechanisms that could be potentially tuned for optimized performance. The manifestation of these unique features in HEA superconductivity reinforces phase-dependent superconductivity and opens new avenues in the exploration of novel superconducting materials.
more »
« less
Superconductivity and phase stability of a high-entropy (NbTa)0.55(HfTiZr)0.45 alloy under high pressures
High-entropy alloys (HEAs) are a class of multi-element materials that exhibit unique structural and functional properties. This study reports on the synthesis and characterization of a superconducting HEA, (NbTa)0.55(HfTiZr)0.45 fabricated using the vacuum arc melting technique. Scanning electron microscopy and energy-dispersive x-ray spectroscopy were employed to analyze the material's morphology and composition. X-ray diffraction analysis revealed a single-phase body-centered cubic (BCC) structure with a measured nanoindentation hardness of 6.4 GPa and Young's modulus of 132 GPa. This HEA superconductor was investigated by x-ray diffraction at Beamline 13BM-C, Advanced Photon Source, and the BCC phase was stable to the highest pressure of 50 GPa. Superconductivity was characterized by four-probe resistivity measurements in a quantum design physical property measurement system, yielding a superconducting transition temperature (Tc) of 7.2 K at ambient pressure and reaching a maximum of 10.1 K at the highest applied pressure of 23.6 GPa. The combination of high structural stability enhanced superconducting performance under pressure and superior mechanical properties highlights (NbTa)0.55(HfTiZr)0.45 as a promising superconductor under extreme environments.
more »
« less
- PAR ID:
- 10596706
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- Journal of Applied Physics
- Volume:
- 137
- Issue:
- 21
- ISSN:
- 0021-8979
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
At ambient conditions, the high-entropy alloy superconductor Re0.6(NbTiZrHf)0.4 exhibits exceptional mechanical properties among high-entropy alloys, with its hexagonal phase achieving nanoindentation hardness of 18.5 GPa. We report on a unique pressure-induced structural transformation from a hexagonal phase to a body-centered cubic (BCC) phase, revealed by synchrotron x-ray diffraction measurements up to 70 GPa. This first-order transition, accompanied by a 6.1% volume collapse, occurs at 44 GPa and results in a BCC structure with random site occupancy by the five constituent elements, which is remarkably retained upon decompression to ambient conditions. The transformation proceeds via a martensiticlike, diffusionless mechanism without elemental segregation, enabled by pressure-induced electronic redistribution and atomic-scale disorder. These findings demonstrate a rare case of metastable phase retention in a chemically complex alloy and offer new insights into structure-stability relationships under pressure.more » « less
-
null (Ed.)X-ray diffraction indicates that the structure of the recently discovered carbonaceous sulfur hydride (C-S-H) room temperature superconductor is derived from previously established van der Waals compounds found in the H2S-H2 and CH4-H2 systems. Crystals of the superconducting phase were produced by a photochemical synthesis technique leading to the superconducting critical temperature Tc of 288 K at 267 GPa. X-ray diffraction patterns measured from 124 to 178 GPa, within the pressure range of the superconducting phase, are consistent with an orthorhombic structure derived from the Al2Cu-type determined for (H2S)2H2 and (CH4)2H2 that differs from those predicted and observed for the S-H system to these pressures. The formation and stability of the C-S-H compound can be understood in terms of the close similarity in effective volumes of the H2S and CH4 components, and denser carbon-bearing S-H phases may form at higher pressures. The results are crucial for understanding the very high superconducting Tc found in the C-S-H system at megabar pressures.more » « less
-
Transition-metal and rare-earth borides are of considerable interest due to their electronic, mechanical, and magnetic properties as well as their structural stability under extreme conditions. Here, we report on a series of high-pressure Raman and x-ray diffraction experiments on the cubic rare-earth hexaboride EuB6 to an ultrahigh pressure of 187 GPa in a diamond anvil cell. In EuB6, divalent europium ions occupy the corners of the cubic structure, which encloses a rigid boron-bonded cage. So far, no structural phase transitions have been reported, while the nanoindentation studies indicate amorphization in nanoscale shear bands during plastic deformation. Our x-ray diffraction studies have revealed that the ambient cubic phase of EuB6 shows broadening and splitting of diffraction peaks starting at 72 GPa and the broadening continuing to 187 GPa. The high-pressure phase is recovered on decompression, and the Raman spectroscopy of the recovered sample from 187 GPa shows a downward frequency shift and broadening of T2g, Eg, and A1g modes of boron octahedron. The density functional theory simulations of EuB6 at 100 GPa have identified five possible lowest energy crystal structures. The experimental x-ray diffraction data at high pressures is compared with the theoretical predictions and the role of structural distortions induced by shear stresses is also discussed.more » « less
-
In this study, phase transitions (structural and magnetic) and associated magnetocaloric properties of stoichiometric MnCoGe have been investigated as a function of annealing pressure. Metastable phases were generated by annealing at 800 °C followed by rapid cooling under pressures up to 6.0 GPa. The x-ray diffraction results reveal that the crystal cell volume of the metastable phases continuously decreases with increasing thermal processing pressure, leading to a decrease in the structural transition temperature. The magnetic and structural transitions merge and form a first-order magnetostructural transition between the ferromagnetic orthorhombic and paramagnetic hexagonal phases over a broad temperature range (>80 K) spanning room temperature, yielding considerable magnetic entropy changes. These findings demonstrate the utility of thermal processing under high pressure, i.e., high-pressure annealing, to control the magnetostructural transitions and associated magnetocaloric properties of MnCoGe without altering its chemical composition.more » « less