This study develops two (2) simple but effective techniques for enhancing buckling resistance of welded steel moment connections (WSMCs). The ANSI/AISC 358-10 prequalified connections satisfy the 4% interstory drift requirement, however experimental studies have shown that their strength degradation may initiate as early as 3% drift. This strength degradation has been observed to be initiated by buckling of the beam web which is followed by buckling of the beamflange and twisting of the beam. Consequently, buildings with the prequalified connections may sustain significant buckling damages under severe earthquakes and it is questionable as to whether these connections are capable of resisting gravity loads or lateral loads from strong aftershocks following a severe earthquake. To improve upon these shortcomings, two (2) performance enhancing techniques are proposed and investigated through finite element analysis (FEA). The more promising of the two involves reinforcing the beam web in the expected plastic hinge with a web reinforcement plate. Finite element analysis demonstrated that this reinforcement enhances the beam buckling resistance of WSMCs and thereby significantly reduces the beam buckling damages even at 5% interstory drift. The potential of this technique is analytically and experimentally demonstrated for the recently developed heat-treated beam section (HBS) WSMC. Test results confirm that the web reinforcement plate was effective in reducing local buckling damage and associated strength degradation, thereby improving the performance of HBS WSMCs. Areas for application and future development of the proposed techniques are identified.
more »
« less
An innovative seismic performance enhancement technique for steel building moment resisting connections
This study develops and experimentally validates an innovative technique for enhancing the seismic performance of steel beam to column moment connections. The technique involves reducing the strength of specified regions of the beam flanges by exposing them to high temperatures followed by slow cooling. Analogous to the reduced beam section (RBS) connection, yielding and plastic hinge formation is promoted in the heat-treated beam section (HBS). Moreover, because the elastic and inelastic modulus of the steel is unmodified by the heat-treatment and the beam cross section is not altered, an HBS connection does not sacrifice elastic stiffness or buckling resistance as does the RBS. Design of the HBS connection was performed through detailed finite element analysis and material testing. Two large scale connections modified with the HBS technique were tested in this study. The test program showed that the proposed heat-treatment technique was successful in the promotion of yielding and plastic hinge development in the heat-treated regions with specimens attaining interstory drifts as high as 6% without weld or near weld fracture. Strength degradation due to beam buckling within the HBS was the observed failure mechanism in both specimens. Detail analyses of strain and beam deformation data are presented to explain the HBS connection plastic hinge formation and gradual strength degradation. Broader applications of the technique to other structural components are identified.
more »
« less
- Award ID(s):
- 0936547
- PAR ID:
- 10026084
- Date Published:
- Journal Name:
- Journal of constructional steel research
- Volume:
- 109
- ISSN:
- 1873-5983
- Page Range / eLocation ID:
- 34-46
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Introductory steel design courses focus on the analysis and design of primary members, which typically include tension members and connections, compression members, flexural members, and beam-columns. Introducing structural steel design concepts to students presents its fair share of challenges. First, it is difficult for students to visualize and accurately predict the potential failure modes of a tension member: yielding of the gross section, rupture of the net section, and block shear. Second, it is also difficult for students to visualize the buckling modes of steel columns, which vary with shape and type of bracing. Students particularly struggle with the determination of buckling modes between strong and weak axes based on effective lengths. Third, flexural failure modes of steel beams are very difficult for students to visualize and understand when each mode controls. The failure modes are complex and fall into three categories for compact shapes: yielding of the cross section, inelastic lateral torsional buckling, and elastic lateral torsional buckling, which is dependent on the unbraced length of the compression flange. Non-compact sections also include local buckling of the flange or web, but identifying the relationship between the unbraced length and beam span and how the unbraced length affects the flexural capacity tends to be the most difficult concept for students to grasp. This paper provides a detailed overview of the design, fabrication, and implementation of three large-scale experiential learning modules for an undergraduate steel design course. The first module focuses on the tension connections by providing physical models of various failure types including yielding of the gross section, rupture of the net section, and block shear; the second module focuses on the capacity of columns with different amounts of lateral bracing about the weak axis; and the third module focuses on the flexural strength of a beam with different unbraced lengths to illustrate the difference between lateral torsional buckling and flange local buckling/yielding of the gross section. The three modules were used throughout the steel design course at Saint Louis University and Rose-Hulman Institute of Technology to illustrate the failure mechanisms associated with the design of steel structures.more » « less
-
This study addresses the limitations of cross weld tensile testing (CWTT) in quantifying local mechanical properties across microstructural and compositional gradients in dissimilar– and matching–filler metal welds. A digital image correlation (DIC) methodology was validated for application in CWTT by direct comparison of stress-strain curves generated using conventional and virtual DIC extensometers in tensile testing of homogeneous steel samples. DIC-instrumented CWTT of dissimilar weld metal Alloy 625 filler metal on F65 steel demonstrated capability in quantifying the local yield strength, strain-hardening kinetics, and strain at failure in the base metal, heat-affected zone (HAZ), fusion boundary (FB) region, and weld metal in dissimilar and matching filler metal welds. It was shown that the high strain-hardening capacity in Alloy 625 weld metal led to base metal failure in CWTT despite the lower Alloy 625 weld metal yield strength. It was also shown that DIC-instrumented CWTT can be used for determining weld metal undermatching and overmatching conditions in compositionally matching- and dissimilar-metal welds. Furthermore, by quantifying local strain distribution (both elastic and plastic) in the HAZ, FB region, and weld metal, DIC-instrumented CWTT provides an additional method for evaluating hydrogen-assisted cracking susceptibility in dissimilar-metal welds.more » « less
-
The local yielding behavior in base metal, heat-affected zone, fusion boundary region, and weld metal of low-alloy steel/Alloy 625 filler metal welds was quantified using digital image correlation instrumented cross-weld tensile test. The tested welds exhibited undermatching, matching, or overmatching weld metal yield strength with significant gradients in the local yielding behavior. An undermatching weld yielded at 69 MPa below the base metal yield stress, accumulating to 0.72% total strain. The base metal in an overmatching weld had 110 MPa lower yield strength than the weld metal. The strong strain hardening response in the Alloy 625 weld metal, within the uniform elongation range, and its constraining effect on the fusion boundary region and heat affected zone, led to extensive strain accumulation, necking, and final failure in the base metal of all tested welds. The yielding behavior of the tested welds was compared to stress-based criteria, utilizing minimum specified and as-delivered yield and ultimate tensile strength, and to strain-based criteria. The capability of digital image correlation instrumented cross-weld tensile testing to quantify local yielding and strain accumulation demonstrates potential application in proving conformity to stress-based and strain-based design criteria of dissimilar and matching filler metal welds.more » « less
-
Capillary forces acting at the interfaces of soft materials lead to deformations over the scale of the elastocapillary length. When surface stresses exceed a material's yield stress, a plastocapillary effect is expected to arise, resulting in yielding and plastic deformation. Here, we explore the interfacial instabilities of 3D-printed fluid and elastic beams embedded within viscoelastic fluids and elastic solid support materials. Interfacial instabilities are driven by the immiscibility between the paired phases or their solvents. We find that the stability of an embedded structure is predicted from the balance between the yield stress of the elastic solid, τ y , the apparent interfacial tension between the materials, γ ′, and the radius of the beam, r , such that τ y > γ ′/ r . When the capillary forces are sufficiently large, we observe yielding and failure of the 3D printed beams. Furthermore, we observe new coiling and buckling instabilities emerging when elastic beams are embedded within viscous fluid support materials. The coiling behavior appear analogous to elastic rope coiling whereas the buckling instability follows the scaling behavior predicted from Euler–Bernoulli beam theory.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/http://dx.doi.org/10.1016/j.jcsr.2015.02.010