Title: Adaptable Eu-containing polymeric films with dynamic control of mechanical properties in response to moisture
Self-healing polymers often have a trade-off between healing efficiency and mechanical stiffness. Stiff polymers that sacrifice their chain mobility are slow to repair upon mechanical failure. We herein report adaptable polymer films with dynamically moisture-controlled mechanical and optical properties, therefore having tunable self-healing efficiency. The design of the polymer film is based on the coordination of europium (Eu) with dipicolylamine (DPA)-containing random copolymers of poly( n -butyl acrylate- co -2-hydroxy-3-dipicolylamino methacrylate) (P( n BA- co -GMADPA)). The Eu–DPA complexation results in the formation of mechanically robust polymer films. The coordination of Eu–DPA has proven to be moisture-switchable given the preferential coordination of lanthanide metals to O over N, using nuclear magnetic resonance and fluorescence spectroscopy. Water competing with DPA to bind Eu 3+ ions can weaken the cross-linking networks formed by Eu–DPA coordination, leading to the increase of chain mobility. The in situ dynamic mechanical analysis and ex situ rheological studies confirm that the viscofluid and the elastic solid states of Eu-polymers are switchable by moisture. Water speeds up the self-healing of the polymer film by roughly 100 times; while it can be removed after healing to recover the original mechanical stiffness of polymers.  more » « less
Award ID(s):
1705566
PAR ID:
10175085
Author(s) / Creator(s):
; ; ; ;
Date Published:
Journal Name:
Soft Matter
Volume:
16
Issue:
9
ISSN:
1744-683X
Page Range / eLocation ID:
2276 to 2284
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; (, Polymers)
    Perovskite solar cells (PSCs) have emerged as a rising next-generational photovoltaic technology due to low fabrication costs through solution processing as compared to traditional silicon solar cells and high-power conversion efficiency. However, the poor long-term operational stability due to environmental and mechanical degradation remains a hindrance to commercialization. Herein, self-healing polymer additives are utilized by researchers to enhance the photovoltaic performance of PSCs by enabling self-restorative behavior from physical damage or chemical degradation. This review explores the design and application of self-healing polymers in both flexible and rigid PSCs, contrasting the two main reversible bonding mechanisms: physical bonds, such as hydrogen bonds, and chemical bonds, such as dynamic covalent disulfide bonds. Physical bonds provide passive healing at ambient conditions; meanwhile, chemical bonds offer a stronger restoration under external stimuli such as heat or light. These polymers are exceptionally effective at mitigating mechanical stress and cracks in flexible PSCs and combating moisture-induced degradation in rigid PSCs. The applications of self-healing polymers are categorized based on substrate type, healing mechanism, and perovskite composition, with the benefits and limitations of each approach highlighted. Additionally, the review explores the potential of multifunctional self-healing polymers to passivate defects at the grain boundaries and on surface of perovskite films, thereby enhancing the overall photovoltaic performance. 
    more » « less
  2. (, Journal of Polymer Science)
    ABSTRACT Polymer thin films are critical for many applications, including water filtration and gas separation membranes. In these applications, polymer films can experience elevated temperatures, elevated pressures/pressure gradients, and varying liquid/gas environments. However, the majority of work on the mechanical properties of ultrathin polymer films has focused on the impact of thickness at ambient conditions. In contrast, less work has focused on the effect of non‐ambient environmental conditions. This perspective reviews the bulk and thin film literature on how environmental conditions can influence the solid mechanics of glassy polymers, highlighting the unresolved questions that remain. We focus on two dense polymer thin film membrane applications: water desalination and CO2capture. These applications will benefit from investigating the influence of environmental operating conditions on their mechanical properties. To accomplish these studies, tensile testers for ultrathin films will need to be modified to measure the impact of temperature (heating stage), liquid interactions (liquid support layer), and gas interactions (instrument enclosure). Measuring the influence of hydraulic pressure on the thin film mechanical properties will require a creative approach in the future. Modifying these instruments will yield future studies on the impact of the surrounding environment on the solid mechanics of ultrathin polymer films. 
    more » « less
  3. ; ; ; (, Journal of Polymer Science)
    Abstract Conjugated polymers consist of complex backbone structures and side‐chain moieties to meet various optoelectronic and processing requirements. Recent work on conjugated polymers has been devoted to studying the mechanical properties and developing new conjugated polymers with low modulus and high‐crack onset strain, while the thin film mechanical stability under long‐term external tensile strain is less investigated. Here we performed direct mechanical stress relaxation tests for both free‐standing and thin film floated on water surface on both high‐Tgand low‐Tgconjugated polymers, as well as a reference nonconjugated sample, polystyrene. We measured thin films with a range of film thickness from 38 to 179 nm to study the temperature and thickness effect on thin film relaxation, where an apparent enthalpy–entropy compensation effect for glassy polymer PS and PM6 thin films was observed. We also compared relaxation times across three different conjugated polymers and showed that both crystalline morphology and higher modulus reduce the relaxation rate besides higher glass transition temperature. Our work provides insights into the mechanical creep behavior of conjugated polymers, which will have an impact on the future design of stable functional organic electronics. 
    more » « less
  4. ; ; ; ; ; (, Macromolecules)
    Side-chain sequence enabled regioisomeric acceptors, bearing different side-chain sequences on the same conjugated backbone, are herein reported. Two regioregular polymers PTBI-1 and PTBI-2 and one regiorandom polymer PTBI-3 were synthesized from these two regioisomeric acceptors for a comparative study. UV–vis–NIR absorption spectroscopy and electrochemical study confirmed similar frontier molecular orbital levels of the three polymers in their solid state. More intriguingly, absorption profiles suggest that the sequence of side chains greatly governs the aggregation behaviors. Furthermore, the PTBI-2 film shows larger ordered domains than PTBI-1 and PTBI-3 films, as supported by AFM and GIWAXS measurements. As a result, PTBI-2-based FET devices achieved an average hole mobility of 1.37 cm2 V–1 s–1, much higher than the two polymers with other side-chain sequences. The regiorandom PTBI-3 exhibited the lowest average hole mobility of 0.27 cm2 V–1 s–1. This study highlights the significant impact of side-chain sequence regioisomerism on aggregation behaviors, morphologies, and subsequently charge transport properties of donor–acceptor type conjugated polymers. 
    more » « less
  5. ; ; ; (, Journal of Materials Chemistry A)
    This work evaluates the degradation capabilities of transient carboxylic acid-based dopants (CABDs), focusing on 1,2,4-benzene tricarboxylic acid (BA), citric acid (CA), and diphenic acid (DA). The stretchable electronic polymer complex is composed of polyaniline (PANI), poly(2-acrylamido-2-methyl-1-propanesulfonic acid) (PAAMPSA), and CABDs. The film is synthesized through the oxidative polymerization of aniline while PAAMPSA acts as a template to guide the PANI polymerization. Structural variations among the dopants—including acidity, aromaticity, and rigidity—significantly influenced conductivity, mechanical properties, water retention, and self-healing efficiency. The PANI/PAAMPSA/BA composite exhibited the highest conductivity (0.0063 S m−1), while PANI/PAAMPSA/CA demonstrated exceptional stretchability (elongation at break of 3823%), the greatest water retention (15.1%), and a complete conductivity self-healing efficiency (100%). The degradation tests were carried out under soil burial and aqueous conditions. Interestingly, the films completely dissolved in distilled water, tap water and river water within 10 minutes. In addition, the dissolved solution could be recast to develop new functional sensors, indicating the reusability of the sensors. Soil degradation tests further demonstrated the degradation of the film within 24 hours. These findings confirm the potential of carboxylic acid-doped polymeric sensors as sustainable, eco-friendly materials for sensing applications that combine efficient degradability with re-processibility to minimize environmental impact. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Text Encoded Conversion
  • XML
  • Save / Share this Record
  • Send to Email