Carbon fiber reinforced polymer (CFRP) composites have been increasingly used to replace metal parts in many industries such as aerospace, marine, automotive, and sporting goods. The CFRP parts compared with their metallic counter parts have the advantages of lightweight, significantly higher tensile strength, stiffer, and corrosion resistant. On the other hand, compared with many metal parts, the CFRP parts have many well-known disadvantages including the lower toughness, lower through-thickness tensile and shear strengths, lower thermal conductivity, lower electrical conductivity, and lower operating temperature. These disadvantages have made the conversion from metal parts into CFRP parts challenging and costly to design, manufacture, and maintain.
The use of nanoparticles in polymer has been studied in the recent two decades. Carbon nanotubes (CNTs) and carbon nanofibers (CNFs) have been dispersed in various thermoset and thermoplastic polymers and improved the mechanical, electrical, and thermal properties; however, the properties were not comparable to CFRP. Later, researchers tried to infuse CNTs or CNFs into either carbon fiber preforms [1] or glass fiber preforms [2] for improving the mechanical properties. But the results were marginal and with great uncertainty due to the challenges of nanoparticle dispersion, filtering, and alignment while being infused through the fiber preform. The glass fiber preform experiments ended with relatively more consistent improvement than the carbon fiber preform experiments since that the glass fiber preform has significantly larger pores than the carbon fiber preform' s. The small pore size presented a great challenge for infusing millions of unaligned long CNTs or CNFs through the carbon fiber preform without being filtered.
To infuse long CNFs or CNTs through the carbon fiber preform and achieve reliable improvements, especially for 55% or higher carbon fiber volume fraction with increasingly tighter pores, an innovative plan for the processing and nano-reinforcing strategy is necessary. The z-threading strategy [3, 4, 5] has been reported to have consistent experimental successes in achieving the statistically meaningful improvement in multifunctional properties. The manufacturing steps of the CNF z-threaded CFRP (ZT-CFRP) are: (1) disperse the CNFs in a resin, (2) use a strong electrical field to align the CNFs in either the B-stage epoxy film or a CNF/resin impregnated sponge layer, whereas the CNFs are aligned in the through-thickness direction of the film or sponge layer. (3) place the resin film or sponge layer on a preheated dry carbon fiber fabric and press the resin film into the hot carbon fabric and allow the resin flow to carry the well-aligned CNFs to thread through the pores in the carbon fabric. (4) cool down the resin saturated and CNF z-threaded carbon fiber fabric to obtain the ZT-CFRP prepreg. (5) use the ZT-CFRP prepreg to make the ZT-CFRP laminate. Compared with the traditional CFRP, the ZT-CFRP laminates were reported of having improvement in the Mode-I delamination toughness, interlaminar shear strength, longitudinal compressive strength, through-thickness electrical conductivity, through-thickness thermal conductivity, and can reach the carbon fiber volume fraction of 55-80%. It is an effective approach to achieve a multifunctional CFRP for potentially expanding CFRP's applications.
more »
« less
Fabrication and Mechanical Properties of POSS Coated CNTs Reinforced Expancel foam core Sandwich Structures
Background:: Sandwich structures are progressively being used in various engineering applications due to the superior bending-stiffness-to-weight ratio of these structures. We adapted a novel technique to incorporate carbon nanotubes (CNTs) and polyhedral oligomeric silsesquioxanes (POSS) into a sandwich composite structure utilizing a sonochemical and high temperature vacuum assisted resin transfer molding technique. Objective:: The objective of this work was to create a sandwich composite structure comprised of a nanophased foam core and reinforced nanophased face sheets, and to examine the thermal and mechanical properties of the structure. To prepare sandwich structure, POSS nanoparticles were sonochemically attached to CNTs and dispersed in a high temperature resin system to make the face sheet materials and also coated on expandable thermoplastic microspheres for the fabrication of foam core materials. Method:: The nanophased foam core was fabricated with POSS infused thermoplastic microspheres (Expancel) using a Tetrahedron MTP-14 programmable compression molder. The reinforced nanophased face sheet were fabricated by infusing POSS coated CNT in epoxy resin and then curing into a compression stainless steel mold. Result:: Thermal analysis of POSS-infused thermoplastic microspheres foam (TMF) showed an increase in thermal stability in both nitrogen and oxygen atmospheres, 19% increase in thermal residue were observed for 4 wt% GI-POSS TMF compared to neat TMF. Quasi-static compression results indicated significant increases (73%) in compressive modulus, and an increase (5%) in compressive strength for the 1 wt% EC-POSS/CNTs resin system. The nanophased sandwich structure constructed from the above resin system and the foam core system displayed an increase (9%) in modulus over the neat sandwich structure. Conclusion:: The incorporation of POSS-nanofillier in the foam core and POSS-coated nanotubes in the face sheet significantly improved the thermal and mechanical properties of sandwich structure. Furthermore, the sandwich structure that was constructed from nanophased resin system showed an increase in modulus, with buckling in the foam core but no visible cracking.
more »
« less
- Award ID(s):
- 1735971
- NSF-PAR ID:
- 10255468
- Date Published:
- Journal Name:
- Current Applied Polymer Science
- Volume:
- 04
- ISSN:
- 2452-2716
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)During this study, full-size wood composite sandwich panels, 1.2 m by 2.4 m (4 ft by 8 ft), with a biaxial corrugated core were evaluated as a building construction material. Considering the applications of this new building material, including roof, floor, and wall paneling, sandwich panels with one and two corrugated core(s) were fabricated and experimentally evaluated. Since primary loads applied on these sandwich panels during their service life are live load, snow load, wind, and gravity loads, their bending and compression behavior were investigated. To improve the thermal characteristics, the cavities within the sandwich panels created by the corrugated geometry of the core were filled with a closed-cell foam. The R-values of the sandwich panels were measured to evaluate their energy performance. Comparison of the weight indicated that fabrication of a corrugated panel needs 74% less strands and, as a result, less resin compared to a strand-based composite panel, such as oriented strand board (OSB), of the same size and same density. Bending results revealed that one-layer core sandwich panels with floor applications under a 4.79 kPa (100 psf) bending load are able to meet the smallest deflection limit of L/360 when the span length (L) is 137.16 cm (54 in) or less. The ultimate capacity of two-layered core sandwich panels as a wall member was 94% and 158% higher than the traditional walls with studs under bending and axial compressive loads, respectively. Two-layered core sandwich panels also showed a higher ultimate capacity compared to structural insulated panels (SIP), at 470% and 235% more in bending and axial compression, respectively. Furthermore, normalized R-values, the thermal resistance, of these sandwich panels, even with the presence of thermal bridging due to the core geometry, was about 114% and 109% higher than plywood and oriented strand board, respectively.more » « less
-
Additive manufacturing such as vat photopolymerization allows to fabricate intricate geometric structures than conventional manufacturing techniques. However, the manufacturing of lightweight sandwich structures with integrated core and facesheet is rarely fabricated using this process. In this study, photoactivatable liquid resin was used to fabricate sandwich structures with various intricate core topologies including the honeycomb, re-entrant honeycomb, diamond, and square by a vat photopolymerization technique. Uniaxial compression tests were performed to investigate the compressive modulus and strength of these lightweight structures. Sandwich cores with the diamond structure exhibited superior compressive and weight-saving properties whereas the re-entrant structures showed high energy absorption capacity. The fractured regions of the cellular cores were visualized by scanning electron microscopy. Elastoplastic finite element analyses showed the stress distribution of the sandwich structures under compressive loading, which are found to be in good agreement with the experimental results. Dynamic mechanical analysis was performed to compare the behavior of these structures under varying temperatures. All the sandwich structures exhibited more stable thermomechanical properties than the solid materials at elevated temperatures. The findings of this study offer insights into the superior structural and thermal properties of sandwich structures printed by a vat photopolymerization technique, which can benefit a wide range of engineering applications.more » « less
-
null (Ed.)Carbon fiber (CF)-reinforced thermoplastic composites have been widely used in different structural applications due to their superior thermal and mechanical properties. The big area additive manufacturing (BAAM) system, developed at Oak Ridge National Laboratory’s Manufacturing Demonstration Facility, has been used to manufacture several composite components, demonstration vehicles, molds, and dies. These components have been designed and fabricated using various CF-reinforced thermoplastics. In this study, the dynamic rheological and mechanical properties of a material commonly used in additive manufacturing, 20 wt% CF-acrylonitrile butadiene styrene (ABS), as well as three CF-reinforced high-temperature polymers, 25 wt% CF-polyphenylsulfone (PPSU), 35 wt% CF-polyethersulfone (PES), and 40 wt% CF-polyphenylene sulfide (PPS), used to print molds were investigated. The viscoelastic properties, namely storage modulus, loss modulus, tan delta, and complex viscosity, of these composites were studied, and the rheological behavior was related to the BAAM extrusion and bead formation process. The results showed 20 wt% CF-ABS and 40 wt% CF-PPS to display a more dominant elastic component at all frequencies tested while 25 wt% CF-PPSU and 35 wt% CF-PES have a more dominant viscous component. This viscoelastic behavior is then used to inform the deposition and bead formation process during extrusion on the BAAM system.more » « less
-
Novel multifunctional construction materials are needed to promote resilient infrastructure in the face of climate change and extreme weather. Nanostructured materials such as geopolymer reinforced with carbon-based nanomaterials are a promising way to reach that goal. In recent years, several studies have investigated the influence of nanomaterials on the physical properties of geopolymer composites such as compressive strength and fracture toughness. Yet, a fundamental understanding of the influence of nanomaterials on the nanoscale and micron-scale structure has been elusive so far. Our research objective is to understand how multiwalled carbon nanotubes (MWCNT) can help tailor the microstructure of geopolymers to yield architected multifunctional nanocomposites. We synthesized geopolymer nanocomposites reinforced with 50-nm thick multiwalled carbon nanotubes with mass fractions in the range of 0.1 wt%, 0.2 wt%, and 0.5 wt%. Our major finding is that MWCNTs act as hard templates that promote geopolymer formation via self-assembly. Geopolymer nanoparticle growth is observed along the walls of MWCNTs. A refinement in grain size is observed: increasing the fraction of MWCNTs by 0.5 wt% leads to a reduction in grain size by 54%. Similarly, increasing the mass fraction of MWCNTs leads to a densification of the geopolymer matrix as demonstrated by the Fourier transform infrared spectroscopy results and the statistical deconvolution analysis. Mercury intrusion porosimetry shows a nanoscale tailoring of the pore size distribution: a 26% decrease in porosity is observed as the fraction of MWCNTs is increased to 0.5 wt%. As a result of these nanoscale structural changes, a greater resistance to long-term deformation is observed for MWCNT-reinforced geopolymers, as the creep modulus increases both locally and macroscopically. At the macroscopic level, a 42% increase in the macroscopic logarithmic creep modulus is observed as the fraction of MWCNTs is increased to 0.5 wt%. These findings and the supporting methodology are important to understand how to manipulate matter below 100 nm. This research also paves the way for the design of resilient infrastructure materials with tailored microstructure and mechanical properties.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.2174/2452271604999201123193149