  • Importance of multimodal characterization and influence of residual Li 2 S impurity in amorphous Li 3 PS 4 inorganic electrolytes
Title: Importance of multimodal characterization and influence of residual Li 2 S impurity in amorphous Li 3 PS 4 inorganic electrolytes
Amorphous Li 3 PS 4 (LPS) solid-state electrolytes are promising for energy-dense lithium metal batteries. LPS glass, synthesized from a 3 : 1 mol ratio of Li 2 S and P 2 S 5 , has high ionic conductivity and can be synthesized by ball milling or solution processing. Ball milling has been attractive because it provides the easiest route to access amorphous LPS with a conductivity of 3.5 × 10 −4 S cm −1 (20 °C). However, achieving the complete reaction of precursors via ball milling can be difficult, and most literature reports use X-ray diffraction (XRD) or Raman spectroscopy to confirm sample purity, both of which have limitations. Furthermore, the effect of residual precursors on ionic conductivity and lithium metal cycling is unknown. In this work, we illustrate the importance of multimodal characterization to determine LPS phase and chemical purity. To determine the residual Li 2 S content in LPS, we show that (1) XRD and 31 P solid state nuclear magnetic resonance (ssNMR) are insufficient and (2) Raman loses sensitivity at concentrations below 12 mol% Li 2 S. Most importantly, we show that 7 Li ssNMR is highly sensitive. Using 7 Li ssNMR, we investigate the effect of ball milling parameters and develop a robust and highly reproducible procedure for pure LPS synthesis. We find that as the residual Li 2 S precursor content increases, LPS conductivity decreases and lithium metal batteries exhibit higher overpotentials and poor cycle life. Our work reveals the importance of multimodal characterization techniques for amorphous solid-state electrolyte characterization and will enable better synthetic strategies for highly conductive electrolytes for efficient energy-dense solid-state lithium metal batteries.  more » « less
Award ID(s):
2011854
NSF-PAR ID:
10313828
Author(s) / Creator(s):
; ; ;
Date Published:
Journal Name:
Journal of Materials Chemistry A
Volume:
9
Issue:
35
ISSN:
2050-7488
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ( , Journal of The Electrochemical Society)

    Hybrid sulfide-polymer composite electrolytes are promising candidates to enable lithium metal batteries because of their high ionic conductivity and flexibility. These composite materials are primarily prepared through solution casting methods to obtain a homogenous distribution of polymer within the inorganic. However, little is known about the influence of the morphology of the polymer and the inorganic on the ionic conductivity and electrochemical behavior of these hybrid systems. In this study, we assess the impact of processing methodology, either solution processing or solvent-free ball milling, on overall performance of hybrid electrolytes containing amorphous Li3PS4(LPS) and non-reactive polyethylene (PE). We demonstrate that using even non-polar, non-reactive solvents can alter the LPS crystalline structure, leading to a lower ionic conductivity. Additionally, we show that ball milling leads to a non-homogenous distribution of polymer within the inorganic, which leads to a higher ionic conductivity than samples processed via solution casting. Our work demonstrates that the morphology of the polymer and the sulfide plays a key role in the ionic conductivity and subsequent electrochemical stability of these hybrid electrolytes.

     
    more » « less
  2. ; ; ( , Journal of Materials Chemistry A)
    Li 2 S is the key precursor for synthesizing thio-LISICON electrolytes employed in solid state batteries. However, conventional synthesis techniques such as carbothermal reduction of Li 2 SO 4 aren't suitable for the generation of low-cost, high-purity Li 2 S. Metathesis, in which LiCl is reacted with Na 2 S in ethanol, is a scalable synthesis method conducted at ambient conditions. The NaCl byproduct is separated from the resulting Li 2 S solution, and the solvent is removed by evaporation and thermal annealing. However, the annealing process reveals the presence of oxygenated impurities in metathesis Li 2 S that are not usually observed when recovering Li 2 S from ethanol. In this work we investigate the underlying mechanism of impurity formation, finding that they likely derive from the decomposition of alkoxide species that originate from the alcoholysis of the Na 2 S reagent. With this mechanism in mind, several strategies to improve Li 2 S purity are explored. In particular, drying the metathesis Li 2 S under H 2 S at low temperature was most effective, resulting in high-purity Li 2 S while retaining a beneficial nanocrystal morphology (∼10 nm). Argyrodite electrolytes synthesized from this material exhibited essentially identical phase purity, ionic conductivity (3.1 mS cm −1 ), activation energy (0.19 eV), and electronic conductivity (6.4 × 10 −6 mS cm −1 ) as that synthesized from commercially available battery-grade Li 2 S. 
    more » « less
  3. ; ; ; ; ; ( , Advanced Energy Materials)
    Abstract

    The performance of all‐solid‐state batteries (ASSBs) relies on the Li+transport and stability characteristics of solid electrolytes (SEs). Li3PS4is notable for its stability against lithium metal, yet its ionic conductivity remains a limiting factor. This study leverages local structural disorder via O substitution to achieve an ionic conductivity of 1.38 mS cm−1with an activation energy of 0.34 eV for Li3PS4−xOx(x = 0.31). Optimal O substitution transforms Li+transport from 2D to 3D pathways with increased ion mobility. Li3PS3.69O0.31exhibits improvements in the critical current density and stability against Li metal and retains its electrochemical stability window compared with Li3PS4. The practical implementation of Li3PS3.69O0.31in ASSBs half‐cells, particularly when coupled with TiS2as the cathode active material, demonstrates substantially enhanced capacity and rate performance. This work elucidates the utility of introducing local structural disorder to ameliorate SE properties and highlights the benefits of strategically combining the inherent strengths of sulfides and oxides via creating oxysulfide SEs.

     
    more » « less
  4. ; ; ( , Angewandte Chemie)
    Abstract

    Polymer–ceramic composite electrolytes are emerging as a promising solution to deliver high ionic conductivity, optimal mechanical properties, and good safety for developing high‐performance all‐solid‐state rechargeable batteries. Composite electrolytes have been prepared with cubic‐phase Li7La3Zr2O12(LLZO) garnet and polyethylene oxide (PEO) and employed in symmetric lithium battery cells. By combining selective isotope labeling and high‐resolution solid‐state Li NMR, we are able to track Li ion pathways within LLZO‐PEO composite electrolytes by monitoring the replacement of7Li in the composite electrolyte by6Li from the6Li metal electrodes during battery cycling. We have provided the first experimental evidence to show that Li ions favor the pathway through the LLZO ceramic phase instead of the PEO‐LLZO interface or PEO. This approach can be widely applied to study ion pathways in ionic conductors and to provide useful insights for developing composite materials for energy storage and harvesting.

     
    more » « less
  5. ; ; ; ( , Advanced Functional Materials)
    Abstract

    To enhance Li+transport in all‐solid‐state batteries (ASSBs), harnessing localized nanoscale disorder can be instrumental, especially in sulfide‐based solid electrolytes (SEs). In this investigation, the transformation of the model SE, Li3PS4, is delved into via the introduction of LiBr.31P nuclear magnetic resonance (NMR)unveils the emergence of a glassy PS43−network interspersed with Br−.6Li NMR corroborates swift Li+migration between PS43−and Br−, with increased Li+mobility indicated by NMR relaxation measurements. A more than fourfold enhancement in ionic conductivity is observed upon LiBr incorporation into Li3PS4. Moreover, a notable decrease in activation energy underscores the pivotal role of Br−incorporation within the anionic lattice, effectively reducing the energy barrier for ion conduction and transitioning Li+transport dimensionality from 2D to 3D. The compatibility of Li3PS4with Li metal is improved through LiBr incorporation, alongside an increase in critical current density from 0.34 to 0.50 mA cm−2, while preserving the electrochemical stability window. ASSBs with 3Li3PS4:LiBr as the SE  showcase robust high‐rate and long‐term cycling performance. These findings collectively indicate the potential of lithium halide incorporation as a promising avenue to enhance the ionic conductivity and stability of SEs.

     
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email