Title: Platinum and cobalt intermetallic nanoparticles confined within MIL-101(Cr) for enhanced selective hydrogenation of the carbonyl bond in α,β-unsaturated aldehydes: synergistic effects of electronically modified Pt sites and Lewis acid sites
Precious metals have been shown to play a vital role in the selective hydrogenation of α,β-unsaturated aldehydes, but still suffer from challenges to control selectivity. Herein, we have advanced the design of catalysts made out of Pt–Co intermetallic nanoparticles (IMNs) supported on a MIL-101(Cr) MOF (3%Pt y %Co/MIL-101(Cr)), prepared by using a polyol reduction method, as an effective approach to enhance selectivity toward the production of α,β-unsaturated alcohol, the desired product. XRD, N 2 adsorption–desorption, FTIR spectroscopy, SEM, TEM, XPS, CO adsorption, NH 3 -TPD, XANES and EXAFS measurements were used to investigate the structure and surface properties of our 3%Pt y %Co/MIL-101(Cr) catalysts. It was found that the Co-modified 3%Pt y %Co/MIL-101(Cr) catalysts can indeed improve the hydrogenation of cinnamaldehyde (CAL) to cinnamyl alcohol (COL), reaching a higher selectivity under mild conditions than the monometallic Pt/MIL-101(Cr) catalysts: 95% conversion of CAL with 91% selectivity to COL can be reached with 3%Pt3%Co/MIL-101(Cr). Additionally, high conversion of furfural (97%) along with high selectivity to furfural alcohol (94%) was also attained with the 3%Pt3%Co/MIL-101(Cr) catalyst. The enhanced activity and selectivity toward the unsaturated alcohols are attributed to the electronic and geometric effects derived from the partial charge transfer between Co and Pt through the formation of uniformly dispersed Pt–Co IMNs. Moreover, various characterization results revealed that the addition of Co to the IMPs can promote the Lewis acid sites that facilitate the polarization of the charge-rich CO bonds and their adsorption via their oxygen atom, and also generate new interfacial acid sites.  more » « less
Award ID(s):
1953843
NSF-PAR ID:
10320428
Author(s) / Creator(s):
; ; ; ;
Date Published:
Journal Name:
Catalysis Science & Technology
Volume:
11
Issue:
7
ISSN:
2044-4753
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Isostructural Cr and Fe nanoporous MIL-101, synthesized without mineralizing agents, are investigated for styrene oxidation utilizing aqueous hydrogen peroxide to yield valuable oxygenates for chemical synthesis applications. Styrene conversion rates and oxygenate product distributions both depend on metal identity, as MIL-101(Fe) is more reactive for total styrene oxidation and is more pathway selective, preferring aldehyde (benzaldehyde) formation at the α-carbon to the aromatic ring, where MIL-101(Cr) sustains epoxide (styrene oxide) production at the same α-carbon. These pathways often involve hydrogen peroxide derived radical intermediates (O, –HOO˙, –HO − ˙) and metallocycle transition states. We postulate that the higher reactivity of one of these surface intermediates, Fe( iv )O relative to Cr( iv )O, leads to higher styrene oxidation rates for MIL-101(Fe), while higher electrophilicity of Cr( iii )–OOH intermediates translates to the higher styrene oxide selectivity observed for MIL-101(Cr). Secondary styrene oxide and benzaldehyde conversions are observed over both analogs, but the former is more prevalent over MIL-101(Fe) due to higher Lewis/Brønsted acid site density and strength compared to MIL-101(Cr). Recyclability experiments combined with characterization via XRD, SEM/EDXS, and FT-IR and UV-vis spectroscopies show that the nature of MIL-101(Fe) sites does not change significantly with each cycle, whereas MIL-101(Cr) suffers from metal leaching, which impacts styrene conversion rates and product distribution. Both catalysts require active site regeneration, though MIL-101(Fe) sites are more susceptible to reactivation, even under mild conditions. Finally, examination of styrene conversion for three unique synthesized phases of MIL-101(Cr) rationalizes that nodal defects are largely responsible for observed reactivity and selectivity but predispose the framework to metal leaching as a predominant deactivation mechanism. 
    more » « less
  2. Abstract

    Dilute alloy CuPt and NiPt catalysts are studied in the hydrogenation of citral, a model α,β‐unsaturated aldehyde.In situandex situcharacterization is used to demonstrate that the Pt species within these nanoparticles are well dispersed and approach a single atom alloy structure. The distribution of Pt varies between the two host metal systems; under a hydrogen environment, the nanoparticle surface and near‐surface region of the NiPt nanoparticles is Pt rich, while the Pt is more uniformly distributed throughout the CuPt nanoparticles. When used for citral hydrogenation reactions, a rate enhancement is observed upon the addition of Pt to the Cu or Ni host catalysts, however this enhancement is determined to be due to the presence of additional metal and not a synergistic effect of the two metals. The Pt structure does, nonetheless, influence the observed selectivity trends. NiPt/SiO2catalysts have high selectivity to the unsaturated aldehyde citronellal while the CuPt/SiO2catalysts have increased selectivity to unsaturated alcohol products. This increased selectivity is attributed to a combination of hydrogen dissociation over Pt sites and a decrease in size of Cu ensembles due to the presence of Pt, which favors binding and hydrogenation of C=O rather than C=C bonds.

     
    more » « less
  3. Abstract

    Using microwave irradiation, PtCo alloy nanoparticles were deposited within a few minutes on COOH‐functionalized MWCNT supports. The obtained catalysts were used for selective hydrogenation of cinnamaldehyde, a reaction whose products are widely used in various fields. In the selective cinnamaldehyde hydrogenation to cinnamyl alcohol, microwave‐prepared catalysts (generically, PtxCoy‐MW) outperformed a catalyst prepared by the conventional method (Pt1Co2‐con). The highest selective hydrogenation to cinnamyl alcohol, 89%, was obtained using Pt1Co2‐MW, while Pt1Co2‐con showed a selectivity of 76%. Characterization results confirmed that the microwave prepared samples had a stronger interaction between Pt and Co than that in the Pt1Co2‐con sample. The alloyed Co altered the electronic structure of Pt, leading to favorable adsorption of the C=O bond by the lone‐pair electrons of its oxygen atom. Moreover, the Pt1Co2‐MW sample showed neglectable change in catalytic performance (e. g., cinnamaldehyde conversion and selective hydrogenation to cinnamyl alcohol) during recycling experiments.

     
    more » « less
  4. The catalytic properties of monometallic and bimetallic Ru and Mo phosphides were evaluated for their ability to selectively hydrogenate furfural to furfuryl alcohol. Monometallic MoP showed high selectivity (98%) towards furfuryl alcohol, while RuP and Ru 2 P exhibited lower selectivity at comparable conversion. Bimetallic promotional effects were observed with Ru 1.0 Mo 1.0 P, as the pseudo-first order reaction rate constant for furfural hydrogenation to furfuryl alcohol, k 1 , was at least 5× higher than MoP, RuP, and Ru 2 P, while maintaining a 99% selectivity. Composition-directed catalytic studies of Ru x Mo 2−x P (0.8 < x < 1.2) provided evidence that Ru rich compositions positively influence k 1 , but not the selectivity. The rate constant ratio k 1 /( k 2 + k 3 ) for furfuryl alcohol production compared to methyl furan ( k 2 ) and tetrahyrofurfuryl alcohol ( k 3 ) followed the trend of Ru 1.0 Mo 1.0 P > Ru 1.2 Mo 0.8 P > MoP > Ru 0.8 Mo 1.2 P > RuP > Ru 2 P. Diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) was used to examine the configuration of adsorbed furfural on the synthesized catalysts, but the results were inconclusive and no correlation could be found with the selectivity due to the possible IR inactive surface modes with furfural adsorption. However, gas phase density functional theory calculations suggested the x = 1.0 material in Ru x Mo 2−x P (0.8 < x < 1.2) had the most favorable furfural adsorption energy. Experimentally, we also observed that the solvent greatly influenced both the conversion and selectivity, where isopropanol provided the highest selectivity to furfuryl alcohol. Finally, recycling experiments showed a 12% decrease in k 1 after 3 cycles without any regeneration, but the activity could be fully recovered through a re-reduction step. 
    more » « less
  5. Abstract

    Effective control on chemoselectivity in the catalytic hydrogenation of C=O over C=C bonds is uncommon with Pd‐based catalysts because of the favored adsorption of C=C bonds on Pd surface. Here we report a unique orthorhombic PdSn intermetallic phase with unprecedented chemoselectivity toward C=O hydrogenation. We observed the formation and metastability of this PdSn phase in situ. During a natural cooling process, the PdSn nanoparticles readily revert to the favored Pd3Sn2phase. Instead, using a thermal quenching method, we prepared a pure‐phase PdSn nanocatalyst. PdSn shows an >96 % selectivity toward hydrogenating C=O bonds of various α,β‐unsaturated aldehydes, highest in reported Pd‐based catalysts. Further study suggests that efficient quenching prevents the reversion from PdSn‐ to Pd3Sn2‐structured surface, the key to the desired catalytic performance. Density functional theory calculations and analysis of reaction kinetics provide an explanation for the observed high selectivity.

     
    more » « less