Title: Selective laser melting of metal structures onto graphite substrates via a low melting point interlayer alloy
We demonstrate a process to selective laser melt a metal alloy directly onto graphite. The heat trans- fer applications of metal features printed onto annealed pyrolytic graphite are compelling, as pyrolytic graphite has the second highest in-plane thermal conductivity ( > 1500 W/m-K at room temperature) of any bulk material. While the bonding of metal alloys commonly used in selective laser melting (SLM) with graphite is relatively weak, the proper interlayer material drastically improves the wetting and bond- ing. The challenge is the alloys that typically bond to graphite require extended bonding times at elevated temperatures (minutes to hours), while the SLM process delivers only brief exposures to high tempera- tures ( ∼100 μs). In this paper, we employ a Sn3Ag4Ti alloy that rapidly forms a nanometer-thin layer of TiC, as verified by transmission electron microscopy. The influence of graphite thermal properties on interfacial bond strength is shown by mechanical testing and simulations of selective laser melting.  more » « less
Award ID(s):
1905422
NSF-PAR ID:
10331709
Author(s) / Creator(s):
Date Published:
Journal Name:
Applied materials today
Volume:
26
ISSN:
2352-9415
Page Range / eLocation ID:
101334
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Selective laser melting (SLM) is one of the most widely used additive manufacturing technologies. Fabricating nickel-based superalloys with SLM has garnered significant interest from the industry and the research community alike due to the excellent high temperature properties and thermal stability exhibited by the alloys. Haynes-282 alloy, a γ′-phase strengthened Ni-based superalloy, has shown good high temperature mechanical properties comparable to alloys like R-41, Waspaloy, and 263 alloy but with better fabricability. A study and comparison of the effect of different heat-treatment routes on microstructure and mechanical property evolution of Haynes-282 fabricated with SLM is lacking in the literature. Hence, in this manuscript, a thorough investigation of microstructure and mechanical properties after a three-step heat treatment and hot isostatic pressing (HIP) has been conducted. In-situ heat-treatment experiments were conducted in a transmission electron microscopy (TEM) to study γ′ precipitate evolution. γ′ precipitation was found to start at 950 °C during in-situ heat-treatment. Insights from the in-situ heat-treatment were used to decide the aging heat-treatment for the alloy. The three-step heat-treatment was found to increase yield strength (YS) and ultimate tensile strength (UTS). HIP process enabled γ′ precipitation and recrystallization of grains of the as-printed samples in one single step. 
    more » « less
  2. We previously demonstrated how the Sn3Ag4Ti alloy can robustly bond onto silicon via selective laser melting (SLM). By employing this technology, thermal management devices (e.g., micro-channels, vapor chamber evaporators, heat pipes) can be directly printed onto the electronic package (silicon die) without using thermal interface materials. Under immersion two-phase cooling (pool boiling), we compare the performance of three chip cooling methods (conventional heat sink, bare silicon die and additively manufactured metal micro-fins) under high heat flux conditions (100 W/cm2 ). Heat transfer simulations show a significant reduction in the chip temperature for the silicon micro-fins. Reduction of the chip operating temperature or increase in clock speed are some of the advantages of this technology, which results from the elimination of thermal interface materials in the electronic package. Performance and reliability aspects of this technology are discussed through experiments and computational models. 
    more » « less
  3. Advances in selective laser melting (SLM) of metals in the past two decades have made metals additive manufacturing more accessible for industrial adoption. Despite printing process improvements, post- processing of SLM components has not improved much, resulting in considerable costs, delay, and design limitations. Building upon recent advances in sensitization-based self-terminating etching processes, this work details a new set iodine-based sensitization and etching chemistries that simplify the post-processing of copper (Cu) alloy components fabricated using SLM. This work demonstrates that iodine can be used to ‘‘sensitize’’ the surface of copper alloy components to form soluble copper iodide salt that can be then dissolved in common solvents, such as acetonitrile. This process removes a predefined amount of material from all interior and exterior surfaces in a self-terminating manner, enabling facile removal of internal and external supports, removal of any trapped powder, and the smoothing of interior and exterior surfaces. We demonstrate this process on GRCop (Cu-chromium-niobium) alloys due to their widespread use by the rocket propulsion industry along with a demonstration in copper (110) for applications in heat exchangers and electromagnetic transmitters/receivers. Our results provide the first systematic study on the effect of iodi- zation temperature and duration on the thickness of the iodide region in GRCop-84 components. Additionally, the surface roughness before and after each iodization–dissolution was also quantified for GRCop-84 and showed 70% reduction in Ra roughness from a high of 10 lm as-printed to a low of 3 lm after four iodization-dissolution cycles. 
    more » « less
  4. An increasing desire for higher application temperatures and complex geometries for metallic materials has spurred significant development in additive manufacturing (AM) of metal-ceramic composites; however, limited process-microstructure-properties relationships exist for these materials and processing strategies. Herein we investigate the processing window and high-temperature oxidation performance of an in situ reactive, oxidation-resistant titanium metal-matrix composite reinforced with boron nitride (BN) and boron carbide (B4C) via selective laser melting (SLM) to understand the effects of processing parameters on the in situ reactive characteristics and their effects on build reliability and high-temperature oxidation performance. SLM processing required a 50% decrease in overall energy density relative to titanium's optimal parameters to avoid processing failure due to the high in situ reactivity and exothermic reaction between feedstock materials. A precise balance was necessary to combine decreasing the input energy to avoid cracking due to in situ reactivity while simultaneously providing enough input energy to keep the bulk density as high as possible to limit porosity that contributes to processing inconsistencies at low input energy. Process optimization resulted in composites with as high as 98.3% relative density, comparable to some of the best composites reported in the literature, and high-temperature oxidation testing revealed a 39% decrease in oxidation mass gain compared to Ti6Al4V, owing directly to ceramic reinforcement. Our results indicate that control of SLM processing parameters can yield advanced composites with enhanced properties and characteristics compared to the base material, revealing an array of design possibilities for researchers and engineers in many fields. 
    more » « less
  5. Abstract

    Additive manufacturing promises a major transformation of the production of high economic value metallic materials, enabling innovative, geometrically complex designs with minimal material waste. The overarching challenge is to design alloys that are compatible with the unique additive processing conditions while maintaining material properties sufficient for the challenging environments encountered in energy, space, and nuclear applications. Here we describe a class of high strength, defect-resistant 3D printable superalloys containing approximately equal parts of Co and Ni along with Al, Cr, Ta and W that possess strengths in excess of 1.1 GPa in as-printed and post-processed forms and tensile ductilities of greater than 13% at room temperature. These alloys are amenable to crack-free 3D printing via electron beam melting (EBM) with preheat as well as selective laser melting (SLM) with limited preheat. Alloy design principles are described along with the structure and properties of EBM and SLM CoNi-base materials.

     
    more » « less