Diamond offers good optical properties and hosts bright color centers with long spin coherence times. Recent advances in angled-etching of diamond, specifically with reactive ion beam angled etching (RIBAE), have led to successful demonstration of quantum photonic devices operating at visible wavelengths. However, larger devices operating at telecommunication wavelengths have been difficult to fabricate due to the increased mask erosion, arising from the increased size of devices requiring longer etch times. We evaluated different mask materials for RIBAE of diamond photonic crystal nanobeams and waveguides, and how their thickness, selectivity, aspect ratio and sidewall smoothness affected the resultant etch profiles and optical performance. We found that a thick hydrogen silesquioxane (HSQ) layer on a thin alumina adhesion layer provided the best etch profile and optical performance. The techniques explored in this work can also be adapted to other bulk materials that are not available heteroepitaxially or as thin films-on-insulator.
In this study, we demonstrate a tolerant and durable Cr/Ni bilayer metal etch mask that allows us to realize approximately 150:1 etch selectivity to diamond. This result is achieved through the use of a very thin initial Cr layer of <10 nm thickness as part of the bilayer metal mask, which results in five to ten times improved selectivity than thick single metal layer masks or bilayer masks with thicker combinations. A finite element analysis was employed to design and understand the physics and working mechanism of the bilayer metal masks with different thicknesses. Raman spectroscopy and energy-dispersive x-ray spectroscopy on the diamond surface were also performed to investigate the changes in diamond quality before and after the deep diamond etching and found that no noticeable etch damage or defects were formed. Overall, this mask strategy offers a viable way to realize deep diamond etching using a high heat and chemistry tolerant and durable bilayer metal etching mask. It also offers several technological benefits and advantages, including various deposition method options, such as sputtering and physical vapor deposition, that can be used and the total thinness of the bilayer metal mask required given the higher selectivity allows us to realize fine diamond etching or high-aspect ratio etching, which is a critical fabrication process for future power, RF, MEMS, and quantum device applications.
more » « less- Award ID(s):
- 1809077
- PAR ID:
- 10363924
- Publisher / Repository:
- American Vacuum Society
- Date Published:
- Journal Name:
- Journal of Vacuum Science & Technology B
- Volume:
- 40
- Issue:
- 2
- ISSN:
- 2166-2746
- Page Range / eLocation ID:
- Article No. 022210
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
The epitaxial growth of SrTiO 3 on Si(100) substrates that have been lithographically patterned to realize deposition-last, lithographically defined oxide devices on Si is explored. In contrast to traditional deposition-last techniques which create a physical hard mask on top of the substrate prior to epitaxial growth, a pseudomask is instead created by texturing the Si substrate surface itself. The Si is textured through a combination of reactive ion etching and wet-etching using a tetramethylammonium hydroxide solution. Desorbing the native SiO x at high temperatures prior to epitaxial growth in ultrahigh vacuum presents no complications as the patterned substrate is comprised entirely of Si. The inverted profile in which the epitaxial oxide device layer is above the textured pseudomask circumvents shadowing during deposition associated with conventional hard masks, thereby opening a pathway for highly scaled devices to be created.more » « less
-
null (Ed.)Electroless etching of semiconductors has been elevated to an advanced micromachining process by the addition of a structured metal catalyst. Patterning of the catalyst by lithographic techniques facilitated the patterning of crystalline and polycrystalline wafer substrates. Galvanic deposition of metals on semiconductors has a natural tendency to produce nanoparticles rather than flat uniform films. This characteristic makes possible the etching of wafers and particles with arbitrary shape and size. While it has been widely recognized that spontaneous deposition of metal nanoparticles can be used in connection with etching to porosify wafers, it is also possible to produced nanostructured powders. Metal-assisted catalytic etching (MACE) can be controlled to produce (1) etch track pores with shapes and sizes closely related to the shape and size of the metal nanoparticle, (2) hierarchically porosified substrates exhibiting combinations of large etch track pores and mesopores, and (3) nanowires with either solid or mesoporous cores. This review discussed the mechanisms of porosification, processing advances, and the properties of the etch product with special emphasis on the etching of silicon powders.more » « less
-
For continual scaling in microelectronics, new processes for precise high volume fabrication are required. Area-selective atomic layer deposition (ASALD) can provide an avenue for self-aligned material patterning and offers an approach to correct edge placement errors commonly found in top-down patterning processes. Two-dimensional transition metal dichalcogenides also offer great potential in scaled microelectronic devices due to their high mobilities and few-atom thickness. In this work, we report ASALD of MoS2 thin films by deposition with MoF6 and H2S precursor reactants. The inherent selectivity of the MoS2 atomic layer deposition (ALD) process is demonstrated by growth on common dielectric materials in contrast to thermal oxide/ nitride substrates. The selective deposition produced few layer MoS2 films on patterned growth regions as measured by Raman spectroscopy and time-of-flight secondary ion mass spectrometry. We additionally demonstrate that the selectivity can be enhanced by implementing atomic layer etching (ALE) steps at regular intervals during MoS2 growth. This area-selective ALD process provides an approach for integrating 2D films into next-generation devices by leveraging the inherent differences in surface chemistries and providing insight into the effectiveness of a supercycle ALD and ALE process.more » « less
-
more » « less
Abstract A 12‐h hands‐on processing protocol for a nanofabrication lab module is developed with the intention of teaching high school to college undergraduate students major fabrication techniques. The nanofabrication techniques employed are thin film deposition, direct‐write lithography, conventional UV lithography with a mask aligner, etch, dicing, and characterization. The lab module protocol concludes with the student fabricating their own microletter silicon chip with a personalized message with letters and images through hands‐on processing. For academic discussion, the light interference in thin film, deposition and etch rate, and etch selectivity are studied during the lab module.