Abstract This work investigates the application of poly(3,4‐ethylenedioxythiophene) polystyrenesulfonate (PEDOT:PSS) with polyethylene oxide (PEO) in lithium batteries (LIBs). This composite film comprising PEDOT:PSS and PEO was 3D printed onto a carbon nanofiber (CNF) substrate to serve as a layer between the polypropylene (PP) separator and the lithium anode in LIBs. The resulting CNF‐PEDOT:PSS‐PEO film exhibited superior mechanical and thermal properties compared to conventional PP separators. Mechanical tests revealed a high Young's modulus and puncture strength for the composite film. Thermal stability tests indicated that the CNF‐PEDOT:PSS‐PEO film remained stable at higher temperatures compared to the commercial PP separator, and combustion tests confirmed its superior fire‐resistance properties. In terms of conductivity, the composite film maintained comparable ionic conductivity to the commercial PP separator. Electrochemical tests demonstrated that LIBs incorporating the CNF‐PEDOT:PSS‐PEO film exhibited slight improvement in cycling performance, with a 7.9 % increase in long‐term cycling capacity compared to LIBs using only the commercial PP separator. These findings indicate that the developed CNF‐PEDOT:PSS‐PEO composite film holds promise to improve safety, while maintaining the electrochemical performance of LIBs by reducing dendrite formation and enhancing thermal stability.
more »
« less
Coagulation Bath‐Assisted 3D Printing of PEDOT:PSS with High Resolution and Strong Substrate Adhesion for Bioelectronic Devices
Abstract Poly(3,4‐ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) is a promising material because of its favorable electrical and mechanical properties, stability in ambient environments, and biocompatibility. It finds broad application in energy storage, flexible electronics, and bioelectronics. Additive manufacturing opens a plethora of new avenues to form and shape PEDOT:PSS, allowing for the rapid construction of customized geometries. However, there are difficulties in printing PEDOT:PSS while maintaining its attractive properties. A 3D printing method for PEDOT:PSS using a room‐temperature coagulation bath‐based direct ink writing technique is reported. This technique enables fabrication of PEDOT:PSS into parts that are of high resolution and high conductivity, while maintaining stable electrochemical properties. The coagulation bath can be further modified to improve the mechanical properties of the resultant printed part via a one‐step reaction. Furthermore, it is demonstrated that a simple post‐processing step allows the printed electrodes to strongly adhere to several substrates under aqueous conditions, broadening their use in bioelectronics. Employing 3D printing of PEDOT:PSS, a cortex‐wide neural interface is fabricated, and intracranial electrical stimulation and simultaneous optical monitoring of mice brain activity with wide field calcium imaging are demonstrated. This reported 3D‐printing technique eliminates the need for cumbersome experimental setups while offering desired material properties.
more »
« less
- Award ID(s):
- 2011924
- PAR ID:
- 10368826
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Materials Technologies
- Volume:
- 7
- Issue:
- 7
- ISSN:
- 2365-709X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Hydrogels are candidate building blocks in a wide range of biomaterial applications including soft and biohybrid robotics, microfluidics, and tissue engineering. Recent advances in embedded 3D printing have broadened the design space accessible with hydrogel additive manufacturing. Specifically, the Freeform Reversible Embedding of Suspended Hydrogels (FRESH) technique has enabled the fabrication of complex 3D structures using extremely soft hydrogels, e.g., alginate and collagen, by assembling hydrogels within a fugitive support bath. However, the low structural rigidity of FRESH printed hydrogels limits their applications, especially those that require operation in nonaqueous environments. In this study, we demonstrated long-fiber embedded hydrogel 3D printing using a multihead printing platform consisting of a custom-built fiber extruder and an open-source FRESH bioprinter with high embedding fidelity. Using this process, fibers were embedded in 3D printed hydrogel components to achieve significant structural reinforcement (e.g., tensile modulus improved from 56.78 ± 8.76 to 382.55 ± 25.29 kPa and tensile strength improved from 9.44 ± 2.28 to 45.05 ± 5.53 kPa). In addition, we demonstrated the versatility of this technique by using fibers of a wide range of sizes and material types and implementing different 2D and 3D embedding patterns, such as embedding a conical helix using electrochemically aligned collagen fiber via nonplanar printing. Moreover, the technique was implemented using low-cost material and is compatible with open-source software and hardware, which facilitates its adoption and modification for new research applications.more » « less
-
Abstract Integration of conductive electrodes with 3D tissue models can have great potential for applications in bioelectronics, drug screening, and implantable devices. As conventional electrodes cannot be easily integrated on 3D, polymeric, and biocompatible substrates, alternatives are highly desirable. Graphene offers significant advantages over conventional electrodes due to its mechanical flexibility and robustness, biocompatibility, and electrical properties. However, the transfer of chemical vapor deposition graphene onto millimeter scale 3D structures is challenging using conventional wet graphene transfer methods with a rigid poly (methyl methacrylate) (PMMA) supportive layer. Here, a biocompatible 3D graphene transfer method onto 3D printed structure using a soft poly ethylene glycol diacrylate (PEGDA) supportive layer to integrate the graphene layer with a 3D engineered ring of skeletal muscle tissue is reported. The use of softer PEGDA supportive layer, with a 105times lower Young's modulus compared to PMMA, results in conformal integration of the graphene with 3D printed pillars and allows electrical stimulation and actuation of the muscle ring with various applied voltages and frequencies. The graphene integration method can be applied to many 3D tissue models and be used as a platform for electrical interfaces to 3D biological tissue system.more » « less
-
null (Ed.)Three-dimensional (3D) extrusion printing of cellular/acellular structures with biocompatible materials has been widely investigated in recent years. However, the requirement of suitable solidification rate of printable ink materials constrains the utilization of extrusion-based 3D printing technique. In this study, the yield-stress nanoclay suspension-enabled extrusion-based 3D printing system has been investigated and demonstrated to overcome solidification rate constraints during printing. Utilizing the liquid-solid transition property of nanoclay suspension, two fabrication approaches, including nanoclay support bath-enabled printing and nanoclay-enabled direct printing, have been proposed. For the former approach, nanoclay (Laponite EP) has been used as a support bath material to fabricate alginate-based tympanic membrane patches. The constituents of alginate-based ink have been investigated to have the desired mechanical property of alginate-based tympanic membrane patches and facilitate the printing process. For the latter approach, nanoclay (Laponite XLG) has been used as an internal scaffold material to help print poly (ethylene glycol) diacrylate (PEGDA)-based neural chambers, which can be further cross-linked in air. Mechanical stress analysis has been performed to explore the geometric limitation of printable Laponite XLG-PEGDA neural chambers.more » « less
-
Dielectric electroactive polymers are materials capable of mechanically adjusting their volume in response to an electrical stimulus. However, currently these materials require multi-step manufacturing processes which are not additive. This paper presents a novel 3D printed flexible dielectric material and characterizes its use as a dielectric electroactive polymer (DEAP) actuator. The 3D printed material was characterized electrically and mechanically and its functionality as a dielectric electroactive polymer actuator was demonstrated. The flexible 3-D printed material demonstrated a high dielectric constant and ideal stress-strain performance in tensile testing making the 3-D printed material ideal for use as a DEAP actuator. The tensile stress- strain properties were measured on samples printed under three different conditions (three printing angles 0°, 45° and 90°). The results demonstrated the flexible material presents different responses depending on the printing angle. Based on these results, it was possible to determine that the active structure needs low pre-strain to perform a visible contractive displacement when voltage is applied to the electrodes. The actuator produced an area expansion of 5.48% in response to a 4.3 kV applied voltage, with an initial pre-strain of 63.21% applied to the dielectric material.more » « less