We report electron transport measurements in dual-gated monolayer WS2 encapsulated in hexagonal boron-nitride. Using gated Ohmic contacts that operate from room temperature down to 1.5 K, we measure the intrinsic conductivity and carrier density as a function of temperature and gate bias. Intrinsic electron mobilities of 100 cm2/(V s) at room temperature and 2000 cm2/(V s) at 1.5 K are achieved. The mobility shows a strong temperature dependence at high temperatures, consistent with phonon scattering dominated carrier transport. At low temperature, the mobility saturates due to impurity and long-range Coulomb scattering. First-principles calculations of phonon scattering in monolayer WS2 are in good agreement with the experimental results, showing we approach the intrinsic limit of transport in these two-dimensional layers.
We report the effect of remote surface optical (RSO) phonon scattering on carrier mobility in monolayer graphene gated by ferroelectric oxide. We fabricate monolayer graphene transistors back-gated by epitaxial (001) Ba0.6Sr0.4TiO3 films, with field effect mobility up to 23 000 cm2 V−1 s−1 achieved. Switching ferroelectric polarization induces nonvolatile modulation of resistance and quantum Hall effect in graphene at low temperatures. Ellipsometry spectroscopy studies reveal four pairs of optical phonon modes in Ba0.6Sr0.4TiO3, from which we extract RSO phonon frequencies. The temperature dependence of resistivity in graphene can be well accounted for by considering the scattering from the intrinsic longitudinal acoustic phonon and the RSO phonon, with the latter dominated by the mode at 35.8 meV. Our study reveals the room temperature mobility limit of ferroelectric-gated graphene transistors imposed by RSO phonon scattering.
more » « less- NSF-PAR ID:
- 10375940
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- Journal of Applied Physics
- Volume:
- 132
- Issue:
- 15
- ISSN:
- 0021-8979
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
Charge transport in ferroelectric (FE) gated graphene far from the Dirac point (DP) was studied in the temperature range 300 K < T < 350 K. A non-monotonic/monotonic/non-monotonic behavior in the conductivity [σ(T)] was observed as one moved away from the DP. As the gate polarization increased, additional impurity charges were compensated, which reduced charge scattering. The uncompensated charges doped graphene and σ(T) switched to a monotonic increase with increasing T. However, far from the DP, the polarization reached saturation, which resulted in still lower impurity charge scattering. The carrier concentration increased, and a non-monotonic response in σ(T) reappeared, which was attributed to phonon scattering. A theoretical model is presented that combined impurity charge and phonon scattering conduction mechanisms. The top gate polarizable FE provided a novel approach to investigate charge transport in graphene via controlled compensation of impurity charges, and in the process revealed non-monotonic behavior in σ(T) not previously seen in SiO 2 back gated graphene devices.more » « less
-
more » « less
Abstract The first experimental realization of the intrinsic (not dominated by defects) charge conduction regime in lead‐halide perovskite field‐effect transistors (FETs) is reported. The advance is enabled by: i) a new vapor‐phase epitaxy technique that results in large‐area single‐crystalline cesium lead bromide (CsPbBr3) films with excellent structural and surface properties, including atomically flat surface morphology, essentially free from defects and traps at the level relevant to device operation; ii) an extensive materials analysis of these films using a variety of thin‐film and surface probes certifying the chemical and structural quality of the material; and iii) the fabrication of nearly ideal (trap‐free) FETs with characteristics superior to any reported to date. These devices allow the investigation of the intrinsic FET and (gated) Hall‐effect carrier mobilities as functions of temperature. The intrinsic mobility is found to increase on cooling from ≈30 cm2V−1s−1at room temperature to ≈250 cm2V−1s−1at 50 K, revealing a band transport limited by phonon scattering. Establishing the intrinsic (phonon‐limited) mobility provides a solid test for theoretical descriptions of carrier transport in perovskites, reveals basic limits to the technology, and points to a path for future high‐performance perovskite electronic devices.
-
Controlling the Dirac point voltage of graphene is essential for realizing various practical applications of graphene. Here, control of the doping state is achieved in flexible graphene field effect transistors (GFETs) by applying mechanical bending stress. By gradually increasing the bending strain (the decrease of upward/downward bending radius), the Dirac point ( V Dirac ) linearly shifts to left/right, which is induced by the flexoelectric effect of the ferroelectric Pb 0.92 La 0.08 Zr 0.52 Ti 0.48 O 3 (PLZT) gate. In addition, a superior mechanical antifatigue character is obtained in the flexible GFETs, and the doping effect is recoverable. The sensitivity to strain and high bending stability not only offer an easy, controllable and nonintrusive method to obtain a specific doping level in graphene for flexible electric devices, but also highlight the enormous potential of the flexible ferroelectric PLZT-gated GFETs as wearable sensors.more » « less
-
more » « less
Abstract The superior size and power scaling potential of ferroelectric-gated Mott transistors makes them promising building blocks for developing energy-efficient memory and logic applications in the post-Moore’s Law era. The close to metallic carrier density in the Mott channel, however, imposes the bottleneck for achieving substantial field effect modulation via a solid-state gate. Previous studies have focused on optimizing the thickness, charge mobility, and carrier density of single-layer correlated channels, which have only led to moderate resistance switching at room temperature. Here, we report a record high nonvolatile resistance switching ratio of 38,440% at 300 K in a prototype Mott transistor consisting of a ferroelectric PbZr0.2Ti0.8O3gate and an
R NiO3(R : rare earth)/La0.67Sr0.33MnO3composite channel. The ultrathin La0.67Sr0.33MnO3buffer layer not only tailors the carrier density profile inR NiO3through interfacial charge transfer, as corroborated by first-principles calculations, but also provides an extended screening layer that reduces the depolarization effect in the ferroelectric gate. Our study points to an effective material strategy for the functional design of complex oxide heterointerfaces that harnesses the competing roles of charge in field effect screening and ferroelectric depolarization effects.