The recent demonstration of W mm−1output power at 94 GHz in AlN/GaN/AlN high‐electron‐mobility transistors (HEMTs) has established AlN as a promising platform for millimeter‐wave electronics. The current state‐of‐art AlN HEMTs using ex situ‐deposited silicon nitride (SiN) passivation layers suffer from soft gain compression due to trapping of carriers by surface states. Reducing surface state dispersion in these devices is thus desired to access higher output powers. Herein, a potential solution using a novel in situ crystalline AlN passivation layer is provided. A thick, 30+ nm‐top AlN passivation layer moves the as‐grown surface away from the 2D electron gas (2DEG) channel and reduces its effect on the device. Through a series of metal‐polar AlN/GaN/AlN heterostructure growths, it is found that pseudomorphically strained 15 nm thin GaN channels are crucial to be able to grow thick AlN barriers without cracking. The fabricated recessed‐gate HEMTs on an optimized heterostructure with 50 nm AlN barrier layer and 15 nm GaN channel layer show reduction in dispersion down to compared with in current state‐of‐art ex situ SiN‐passivated HEMTs. These results demonstrate the efficacy of this unique in situ crystalline AlN passivation technique and should unlock higher mm‐wave powers in next‐generation AlN HEMTs.
more »
« less
2.2 W/mm at 94 GHz in AlN/GaN/AlN High‐Electron‐Mobility Transistors on SiC
Aluminum nitride (AlN) offers novel potential for electronic integration and performance benefits for high‐power, millimeter‐wave amplification. Herein, load‐pull power performance at 30 and 94 GHz for AlN/GaN/AlN high‐electron‐mobility transistors (HEMTs) on silicon carbide (SiC) is reported. When tuned for peak power‐added efficiency (PAE), the reported AlN/GaN/AlN HEMT shows PAE of 25% and 15%, with associated output power () of 2.5 and 1.7 W mm−1, at 30 and 94 GHz, respectively. At 94 GHz, the maximum generated is 2.2 W mm−1, with associated PAE of 13%.
more »
« less
- Award ID(s):
- 1719875
- PAR ID:
- 10419306
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- physica status solidi (a)
- Volume:
- 220
- Issue:
- 16
- ISSN:
- 1862-6300
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Gallium nitride (GaN)-based high electron mobility transistors (HEMTs) are essential components in modern radio frequency power amplifiers. In order to improve both the device electrical and thermal performance (e.g., higher current density operation and better heat dissipation), researchers are introducing AlN into the GaN HEMT structure. The knowledge of thermal properties of the constituent layers, substrates, and interfaces is crucial for designing and optimizing GaN HEMTs that incorporate AlN into the device structure as the barrier layer, buffer layer, and/or the substrate material. This study employs a multi-frequency/spot-size time-domain thermoreflectance approach to measure the anisotropic thermal conductivity of (i) AlN and GaN epitaxial films, (ii) AlN and SiC substrates, and (iii) the thermal boundary conductance for GaN/AlN, AlN/SiC, and GaN/SiC interfaces (as a function of temperature) by characterizing GaN-on-SiC, GaN-on-AlN, and AlN-on-SiC epitaxial wafers. The thermal conductivity of both AlN and GaN films exhibits an anisotropy ratio of ∼1.3, where the in-plane thermal conductivity of a ∼1.35 μm thick high quality GaN layer (∼223 W m−1 K−1) is comparable to that of bulk GaN. A ∼1 μm thick AlN film grown by metalorganic chemical vapor deposition possesses a higher thermal conductivity than a thicker (∼1.4 μm) GaN film. The thermal boundary conductance values for a GaN/AlN interface (∼490 MW m-2 K−1) and AlN/SiC interface (∼470 MW m−2 K−1) are found to be higher than that of a GaN/SiC interface (∼305 MW m−2 K−1). This work provides thermophysical property data that are essential for optimizing the thermal design of AlN-incorporated GaN HEMT devices.more » « less
-
We present a compositional dependence study of electrical characteristics of AlxGa1−xN quantum well channel-based AlN/AlGaN/AlN high electron mobility transistors (HEMTs) with x=0.25,0.44, and 0.58. This ultra-wide bandgap heterostructure is a candidate for next-generation radio frequency and power electronics. The use of selectively regrown n-type GaN Ohmic contacts results in contact resistance that increases as the Al content of the channel increases. The DC HEMT device characteristics reveal that the maximum drain current densities progressively reduce from 280 to 30 to 1.7 mA/mm for x=0.25,0.44, and 0.58, respectively. This is accompanied by a simultaneous decrease (in magnitude) in threshold voltage from −5.2 to −4.9 to −2.4 V for the three HEMTs. This systematic experimental study of the effects of Al composition x on the transistor characteristics provides valuable insights for engineering AlGaN channel HEMTs on AlN for extreme electronics at high voltages and high temperatures.more » « less
-
Polarization-induced two-dimensional electron gases (2DEGs) in AlN/GaN/AlN quantum well high-electron-mobility transistors on ultrawide bandgap AlN substrates offer a promising route to advance microwave and power electronics with nitride semiconductors. The electron mobility in thin GaN quantum wells embedded in AlN is limited by high internal electric field and the presence of undesired polarization-induced two-dimensional hole gases (2DHGs). To enhance the electron mobility in such heterostructures on AlN, previous efforts have resorted to thick, relaxed GaN channels with dislocations. In this work, we introduce n-type compensation δ-doping in a coherently strained single-crystal (Xtal) AlN/GaN/AlN heterostructure to counter the 2DHG formation at the GaN/AlN interface, and simultaneously lower the internal electric field in the well. This approach yields a δ-doped XHEMT structure with a high 2DEG density of ∼3.2×1013 cm−2 and a room temperature (RT) mobility of ∼855 cm2/Vs, resulting in the lowest RT sheet resistance 226.7 Ω/□ reported to date in coherently strained AlN/GaN/AlN HEMT heterostructures on the AlN platform.more » « less
-
Abstract Gallium nitride high-electron-mobility transistors (GaN HEMTs) are at a point of rapid growth in defense (radar, SATCOM) and commercial (5G and beyond) industries. This growth also comes at a point at which the standard GaN heterostructures remain unoptimized for maximum performance. For this reason, we propose the shift to the aluminum nitride (AlN) platform. AlN allows for smarter, highly-scaled heterostructure design that will improve the output power and thermal management of III-nitride amplifiers. Beyond improvements over the incumbent amplifier technology, AlN will allow for a level of integration previously unachievable with GaN electronics. State-of-the-art high-current p-channel FETs, mature filter technology, and advanced waveguides, all monolithically integrated with an AlN/GaN/AlN HEMT, is made possible with AlN. It is on this new AlN platform that nitride electronics may maximize their full high-power, high-speed potential for mm-wave communication and high-power logic applications.more » « less