Nanoscale metallic material composites consisting of bilayer and trilayer systems of two and three different metallic alternating layers show significant gains in hardness over monolithic single phase films. One of the main applications of these composites can be as protective coatings to technical components to increase their lifespan acting as a mechanical barrier to the carriers of permanent deformation. In this work, we study the strength of bilayer structures made of alternating layers of niobium (Nb) and copper–nickel (Cu–Ni) alloys. The effect of the layer size and composition on strength and hardening as well as the effect of the metal–alloy interface on the dislocation motion is investigated. The simulations reveal a close relationship between the atomic composition of the alloy and the hardening of the film. The results are also compared with experimental findings on nanopillars made of similar structures, and strong similarities are revealed and discussed.
more »
« less
Determination and Calculations of Mercury Vapor Concentration and Energy Released from Freshly Condensed Dental Amalgams Having Various Copper Percentages within the Alloy
Dental amalgam is an alloy consisting of a mixture of fine metallic powder of silver, tin, zinc, copper, and a trace amount of palladium in combination with about fifty percent elemental mercury that forms a matrix phase. Dental amalgams consisting of a high-copper content are the most common types of alloys currently utilized for the restoration of decayed, broken, and fractured posterior human teeth. The present research objective was primarily to improve the material properties by determining and analyzing the amount of mercury vapor released from dental amalgam received from eight different commercial brands. The mechanical hardness of the alloys was found to increase with an increase in copper content in the amalgam. The effect of copper addition on material aging was also studied. During the release of mercury vapor, the corresponding energies associated with the release of mercury vapor from each sample were determined for each successive measurement. The results indicated that increasing the copper content of the amalgam counters the release of mercury vapor from posterior teeth and improves the hardness properties.
more »
« less
- Award ID(s):
- 2122067
- PAR ID:
- 10421515
- Date Published:
- Journal Name:
- Materials
- Volume:
- 16
- Issue:
- 9
- ISSN:
- 1996-1944
- Page Range / eLocation ID:
- 3452
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Teeth tell the tale of interactions between predator and prey. If a dental battery is made up of teeth that look similar, they are morphologically homodont, but if there is an unspecified amount of regional specialization in size or shape, they are morphologically heterodont. These are vague terms with no useful functional implication because morphological homodonty does not necessarily equal functional homodonty. Teeth that look the same may not function the same. Conical teeth are prevalent in fishes, superficially tasked with the simple job of puncture. There is a great deal of variation in the shape and placement of conical teeth. Anterior teeth may be larger than posterior ones, larger teeth may be surrounded by small ones, and patches of teeth may all have the same size and shape. Such variations suggest that conical dentitions might represent a single morphological solution for different functional problems. We are interested in the concept of homodonty and using the conical tooth as a model to differentiate between tooth shape and performance. We consider the stress that a tooth can exert on prey as stress is what causes damage. To create a statistical measure of functional homodonty, stress was calculated from measurements of surface area, position, and applied force. Functional homodonty is then defined as the degree to which teeth along the jaw all bear/exert similar stresses despite changes in shape. We find that morphologically heterodont teeth are often functionally homodont and that position is a better predictor of performance than shape. Furthermore, the arrangement of teeth affects their function, such that there is a functional advantage to having several smaller teeth surrounding a singular large tooth. We demonstrate that this arrangement of teeth is useful to grab, rather than tear, prey upon puncture, with the smaller teeth dissipating large stress forces around the larger tooth. We show that measurements of how shape affects stress distribution in response to loading give us a clearer picture of the evolution of conically shaped teeth.more » « less
-
Tooth replacement rates of polyphyodont cartilaginous and bony fishes are hard to determine because of a lack of obvious patterning and maintaining specimens long enough to observe replacement. Pulse-chase is a fluorescent technique that differentially colours developing mineralized tissue. We present in situ tooth replacement rate and position data for the oral and pharyngeal detentions of Ophiodon elongatus (Pacific lingcod). We assessed over 10 000 teeth, in 20 fish, and found a daily replacement rate of about two teeth (3.6% of the dentition). The average tooth is in the dental battery for 27 days. The replacement was higher in the lower pharyngeal jaw (LPJ). We found no difference between replacement rates of feeding and non-feeding fish, suggesting feeding was not a driver of tooth replacement. Lingcod teeth have both a size and location fate; smaller teeth at one spot will not grow into larger teeth, even if a large tooth nearby is lost. We also found increased rates of replacement at the posterior of the LPJ relative to the anterior. We propose that lingcod teeth do not migrate in the jaw as they develop; their teeth are fated in size and location, erupting in their functional position.more » « less
-
The microstructure, Vickers hardness, and compressive properties of novel low-activation VCrFeTaxWx (x = 0.1, 0.2, 0.3, 0.4, and 1) high-entropy alloys (HEAs) were studied. The alloys were fabricated by vacuum-arc melting and the characteristics of these alloys were explored. The microstructures of all the alloys exhibited a typical morphology of dendritic and eutectic structures. The VCrFeTa0.1W0.1 and VCrFeTa0.2W0.2 alloys are essentially single phase, consisting of a disordered body-centered-cubic (BCC) phase, whereas the VCrFeTa0.2W0.2 alloy contains fine, nanoscale precipitates distributed in the BCC matrix. The lattice parameters and compositions of the identified phases were investigated. The alloys have Vickers hardness values ranging from 546 HV0.2 to 1135 HV0.2 with the x ranging from 0.1 to 1, respectively. The VCrFeTa0.1W0.1 and VCrFeTa0.2W0.2 alloys exhibit compressive yield strengths of 1341 MPa and 1742 MPa, with compressive plastic strains of 42.2% and 35.7%, respectively. VCrFeTa0.1W0.1 and VCrFeTa0.2W0.2 alloys have excellent hardness after annealing for 25 h at 600–1000 °C, and presented compressive yield strength exceeding 1000 MPa with excellent heat-softening resistance at 600–800 °C. By applying the HEA criteria, Ta and W additions into the VCrFeTaW are proposed as a family of candidate materials for fusion reactors and high-temperature structural applications.more » « less
-
Synopsis Teeth lie at the interface between an animal and its environment and, with some exceptions, act as a major component of resource procurement through food acquisition and processing. Therefore, the shape of a tooth is closely tied to the type of food being eaten. This tight relationship is of use to biologists describing the natural history of species and given the high instance of tooth preservation in the fossil record, is especially useful for paleontologists. However, correlating gross tooth morphology to diet is only part of the story, and much more can be learned through the study of dental biomechanics. We can explore the mechanics of how teeth work, how different shapes evolved, and the underlying forces that constrain tooth shape. This review aims to provide an overview of the research on dental biomechanics, in both mammalian and non-mammalian teeth, and to synthesize two main approaches to dental biomechanics to develop an integrative framework for classifying and evaluating dental functional morphology. This framework relates food material properties to the dynamics of food processing, in particular how teeth transfer energy to food items, and how these mechanical considerations may have shaped the evolution of tooth morphology. We also review advances in technology and new techniques that have allowed more in-depth studies of tooth form and function.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.3390/ma16093452