Ge1−x−ySixSny alloys were grown on Ge buffers via reactions of SnH4 and GeH3Cl. The latter is a new CVD source designed for epitaxial development of group-IV semiconductors under low thermal budgets and CMOS-compatible conditions. The Ge1−x−ySixSny films were produced at very low temperatures between 160 and 200 °C with 3%–5% Si and ∼5%–11% Sn. The films were characterized using an array of structural probes that include Rutherford backscattering, x-ray photoelectron spectroscopy, high-resolution x-ray diffraction, scanning transmission electron microscopy, and atomic force microscopy. These studies indicate that the films are strained to Ge and exhibit defect-free microstructures, flat surfaces, homogeneous compositions, and sharp interfaces. Raman was used to determine the compositional dependence of the vibrational modes indicating atomic distributions indistinguishable from those obtained when using high-order Ge hydrides. For a better understanding of the growth mechanisms, a parallel study was conducted to investigate the GeH3Cl applicability for synthesis of binary Ge1−ySny films. These grew strained to Ge, but with reduced Sn compositions and lower thicknesses relative to Ge1−x−ySixSny. Bypassing the Ge buffers led to Ge1−ySny-on-Si films with compositions and thicknesses comparable to Ge1−ySny-on-Ge; but their strains were mostly relaxed. Efforts to increase the concentration and thickness of Ge1−ySny-on-Si resulted in multiphase materials containing large amounts of interstitial Sn. These outcomes suggest that the incorporation of even small Si amounts in Ge1−x−ySixSny might compensate for the large Ge–Sn mismatch by lowering bond strains. Such an effect reduces strain energy, enhances stability, promotes higher Sn incorporation, and increases critical thickness.
more »
« less
Ultra-low temperature synthesis of Ge-based optical materials and devices on Si using GeH 3 Cl
We describe an alternative strategy to the fabrication of Ge–Sn based materials on Si by using chlorogermane (GeH 3 Cl) instead of the specialty Ge hydrides (Ge 2 H 6 , Ge 3 H 8 , Ge 4 H 10 ) currently employed as ultra-low temperature sources of Ge. This simpler and potentially more practical chlorinated derivative is obtained in high yields and in research-grade purity by direct reactions of commercial GeH 4 and SnCl 4 and exhibits favorable physical and chemical properties that make it an effective source of Ge for a wide range of chemical vapor deposition (CVD) processing conditions. As a proof-of concept, we have employed GeH 3 Cl to demonstrate deposition of pure Ge and GeSn hetero-structures on large-area Si wafers, at conditions compatible with current specialty methods for next generation technologies but with higher deposition efficiency, ensuring an optimal use of the Ge feedstock. In the case of pure Ge, GeH 3 Cl has enabled growth of thick and uniform Ge layers with flat surfaces and relaxed microstructures at 330–360 °C, exhibiting lower residual doping than obtained by alternate Ge hydride methods. GeH 3 Cl allows for in situ doping with the same facility as the Ge hydrides, and this has enabled the design and fabrication of homo-structure pin photodetectors exhibiting low dark current densities and closer to ideal optical collection efficiencies when compared to devices produced by other Ge-on-Si approaches. In the case of GeSn, the high reactivity of GeH 3 Cl toward Sn hydrides has enabled the formation of mono-crystalline alloy layers at ultra-low temperatures between 200–300 °C and conditions akin to molecular beam epitaxy (MBE). Combined, these results suggest an intriguing potential for this new CVD process in the device-application space. The deployment of GeH 3 Cl as a highly reactive low-temperature Ge-source could not only improve on the current wasteful methods that use GeH 4 , but also eliminate the need for the higher-cost polygermanes.
more »
« less
- Award ID(s):
- 2119583
- PAR ID:
- 10447840
- Date Published:
- Journal Name:
- Journal of Materials Chemistry C
- Volume:
- 10
- Issue:
- 36
- ISSN:
- 2050-7526
- Page Range / eLocation ID:
- 13107 to 13116
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Germanium alloyed with α-tin (GeSn) transitions to a direct bandgap semiconductor of significance for optoelectronics. It is essential to localize the carriers within the active region for improving the quantum efficiency in a GeSn based laser. In this work, epitaxial GeSn heterostructure material systems were analyzed to determine the band offsets for carrier confinement: (i) a 0.53% compressively strained Ge 0.97 Sn 0.03 /AlAs; (ii) a 0.81% compressively strained Ge 0.94 Sn 0.06 /Ge; and (iii) a lattice matched Ge 0.94 Sn 0.06 /In 0.12 Al 0.88 As. The phonon modes in GeSn alloys were studied using Raman spectroscopy as a function of Sn composition, that showed Sn induced red shifts in wavenumbers of the Ge–Ge longitudinal optical phonon mode peaks. The material parameter b representing strain contribution to Raman shifts of a Ge 0.94 Sn 0.06 alloy was determined as b = 314.81 ± 14 cm −1 . Low temperature photoluminescence measurements were performed at 79 K to determine direct and indirect energy bandgaps of E g,Γ = 0.72 eV and E g,L = 0.66 eV for 0.81% compressively strained Ge 0.94 Sn 0.06 , and E g,Γ = 0.73 eV and E g,L = 0.68 eV for lattice matched Ge 0.94 Sn 0.06 epilayers. Chemical effects of Sn atomic species were analyzed using X-ray photoelectron spectroscopy (XPS), revealing a shift in Ge 3d core level (CL) spectra towards the lower binding energy affecting the bonding environment. Large valence band offset of Δ E V = 0.91 ± 0.1 eV and conduction band offset of Δ E C,Γ–X = 0.64 ± 0.1 eV were determined from the Ge 0.94 Sn 0.06 /In 0.12 Al 0.88 As heterostructure using CL spectra by XPS measurements. The evaluated band offset was found to be of type-I configuration, needed for carrier confinement in a laser. In addition, these band offset values were compared with the first-principles-based calculated Ge/InAlAs band alignment, and it was found to have arsenic up-diffusion limited to 1 monolayer of epitaxial GeSn overlayer, ruling out the possibility of defects induced modification of band alignment. Furthermore, this lattice matched GeSn/InAlAs heterostructure band offset values were significantly higher than GeSn grown on group IV buffer/substrates. Therefore, a lattice matched GeSn/InAlAs material system has large band offsets offering superior carrier confinement to realize a highly efficient GeSn based photonic device.more » « less
-
Core–shell Ge/GeSn nanowires provide a route to dislocation-free single crystal germanium-tin alloys with desirable light emission properties because the Ge core acts as an elastically compliant substrate during misfitting GeSn shell growth. However, the uniformity of tin incorporation during reduced pressure chemical vapor deposition may be limited by the kinetics of mass transfer to the shell during GeSn growth. The balance between Sn precursor flux and available surfaces for GeSn nucleation and growth determines whether defects are formed and their type. On the one hand, when the Sn precursor delivery is insufficient, local variations in Sn arrival rate at the nanowire surfaces during GeSn growth produce asymmetries in shell growth that induce wire bending. This inhomogeneous elastic dilatation due to the varying composition occurs via deposition of Sn-poor regions on some of the {112} sidewall facets of the nanowires. On the other hand, when the available nanowire surface area is insufficient to accommodate the arriving Sn precursor flux, Sn-rich precipitate formation results. Between these two extremes, there exists a regime of growth conditions and nanowire densities that permits defect-free GeSn shell growth.more » « less
-
The π-hole above the plane of the X 2 T′Y molecule (T′ = Si, Ge, Sn; X = F, Cl, H; Y = O, S) was allowed to interact with the TH hydride of TH(CH 3 ) 3 (T = Si, Ge, Sn). The resulting TH⋯T′ tetrel bond is quite strong, with interaction energies exceeding 30 kcal mol −1 . F 2 T′O engages in the strongest such bonds, as compared to F 2 T′S, Cl 2 T′O, or Cl 2 T′S. The bond weakens as T′ grows larger as in Si > Ge > Sn, despite the opposite trend in the depth of the π-hole. The reverse pattern of stronger tetrel bond with larger T is observed for the Lewis base TH(CH 3 ) 3 , even though the minimum in the electrostatic potential around the H is nearly independent of T. The TH⋯T′ arrangement is nonlinear which can be understood on the basis of the positions of the extrema in the molecular electrostatic potentials of the monomers. The tetrel bond is weakened when H 2 O forms an O⋯T′ tetrel bond with the second π-hole of F 2 T′O, and strengthened if H 2 O participates in an OH⋯O H-bond.more » « less
-
Two distinct ultra-thin Ge1−xSnx (x ≤ 0.1) epilayers were deposited on (001) Si substrates at 457 and 313 °C through remote plasma-enhanced chemical vapor deposition. These films are considered potential initiation layers for synthesizing thick epitaxial GeSn films. The GeSn film deposited at 313 °C has a thickness of 10 nm and exhibits a highly epitaxial continuous structure with its lattice being compressed along the interface plane to coherently match Si without mismatch dislocations. The GeSn film deposited at 457 °C exhibits a discrete epitaxial island-like morphology with a peak height of ∼30 nm and full-width half maximum (FWHM) varying from 20 to 100 nm. GeSn islands with an FWHM smaller than 20 nm are defect free, whereas those exceeding 25 nm encompass nanotwins and/or stacking faults. The GeSn islands form two-dimensional modulated superlattice structures at the interface with Si. The GeSn film deposited at 457 °C possesses a lower Sn content compared to the one deposited at lower temperature. The potential impact of using these two distinct ultra-thin layers as initiation layers for the direct growth of thicker GeSn epitaxial films on (001) Si substrates is discussed.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1039/d2tc02862j