Vitrimers have the characteristics of shape-reforming and surface-welding, and have the same excellent mechanical properties as thermosets; so vitrimers hold the promise of a broad alternative to traditional plastics. Since their initial introduction in 2011, vitrimers have been applied to many unique applications such as reworkable composites and liquid crystal elastomer actuators. A series of experiments have investigated the effects of reprocessing conditions (such as temperature, time, and pressure) on recycled materials. However, the effect of particle size on the mechanical properties of recycled materials has not been reported. In this paper, we conducted an experimental study on the recovery of epoxy-acid vitrimers of different particle sizes. Epoxy-acid vitrimer powders with different particle size distributions were prepared and characterized. The effects of particle size on the mechanical properties of regenerated epoxy-acid vitrimers were investigated by dynamic mechanical analysis and uniaxial tensile tests. In addition, other processing parameters such as temperature, time, and pressure are discussed, as well as their interaction with particle size. This study helped to refine the vitrimer reprocessing condition parameter toolbox, providing experimental support for the easy and reliable control of the kinetics of the bond exchange reaction.
more »
« less
Influences of processing conditions on mechanical properties of recycled epoxy‐anhydride vitrimers
Abstract The chemically crosslinked network structures make epoxies, the most common thermosets, unable or hard to be recycled, causing environmental problems and economic losses. Epoxy‐based vitrimers, polymer networks deriving from epoxy resins, can be thermally malleable according to bond exchange reactions (BERs), opening the door to recycle epoxy thermosets. Here a series of experiments were carried out to study the effects of processing conditions (such as particle size distributions, temperature, time, and pressure) on recycling of an epoxy‐anhydride vitrimer. Polymer powders from the epoxy‐anhydride vitrimer with different size distributions were prepared and characterized, and the influence of particle size on the mechanical performance of recycled epoxy‐anhydride vitrimers was investigated by dynamic mechanical analysis and uniaxial tensile test. Experimental results demonstrated that finer polymer powders can increase the contacting surfaces of recycled materials and thus result in high quality of recycled materials. In addition, the influences of other treating parameters, such as temperature, time, and pressure, were also discussed in this study. Adjusting these treating parameters can help the design of an optimized reprocessing procedure to meet practical engineering applications.
more »
« less
- Award ID(s):
- 1901807
- PAR ID:
- 10455706
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Journal of Applied Polymer Science
- Volume:
- 137
- Issue:
- 41
- ISSN:
- 0021-8995
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Vitrimers with bond exchange reactions (BERs) are a class of covalent adaptable network (CAN) polymers at the forefront of recent polymer research. They exhibit malleable and self-healable behaviors and combine the advantages of easy processability of thermoplastics and excellent mechanical properties of thermosets. For thermally sensitive vitrimers, a molecular topology melting/frozen transition is triggered when the BERs are activated to rearrange the network architecture. Notable volume expansion and stress relaxation are accompanied, which can be used to identify the BER activation temperature and rate as well as to determine the malleability and interfacial welding kinetics of vitrimers. Existing works on vitrimers reveal the rate-dependent behaviors of the nonequilibrium network during the topology transition. However, it remains unclear what the quantitative relationship with heating rate is, and how it will affect the macroscopic stress relaxation. In this paper, we study the responses of an epoxy-based vitrimer subjected to a change in temperature and mechanical loading during the topology transition. Using thermal expansion tests, the thermal strain evolution is shown to depend on the temperature-changing rate, which reveals the nonequilibrium states with rate-dependent structural relaxation. The influences of structural relaxation on the stress relaxation behaviors are examined in both uniaxial tension and compression modes. Assisted by a theoretical model, the study reveals how to tune the material and thermal-temporal conditions to promote the contribution of BERs during the reprocessing of vitrimers.more » « less
-
The development of vitrimers with dynamic covalent bonds enables reprocessability in crosslinked networks, offering a sustainable alternative to conventional thermosets. In this work, a thiol-acrylate vitrimer was synthesized from lignin-derivable (bis)phenols (guaiacol and bisguaiacol F) and compared to a control derived from petroleum-based precursors (phenol and bisphenol F) to investigate the effect of structural differences on network properties and thermal reprocessing. The presence of methoxy groups in the lignin-derivable vitrimer promoted intermolecular interactions by serving as additional hydrogen bonding acceptors during curing, leading to a denser network, as evidenced by a higher rubbery storage modulus (∼2.4 MPa vs. ∼1.4 MPa) and glass transition temperature (∼34 °C vs. ∼28 °C). The lignin-derivable vitrimer exhibited a slightly higher elongation-at-break (∼170% vs. ∼130%) and improved mechanical robustness, including a nearly two-fold increase in Young's modulus (∼6.9 MPa vs. ∼3.4 MPa) and toughness (∼750 kJ m−3vs. ∼390 kJ m−3). The similar stress relaxation behavior and activation energy of viscous flow indicated comparable bond exchange dynamics between the two vitrimers, while the lignin-derivable system demonstrated higher thermal healing efficiency with improved recovery of tensile properties after reprocessing. These findings highlight the potential of lignin-based aromatics in designing mechanically robust and sustainable vitrimers, aligning with efforts to develop renewable and reprocessable polymeric materials.more » « less
-
Thermoset polymer composites, known for their outstanding thermal, mechanical, and chemical properties, have found applications in diverse fields, including aerospace and automotive industries. These polymers, once cured, cannot be recycled, making the end-of-life management of these composites very difficult and posing an environmental challenge. Conventional recycling methods are unsuitable for thermosets, forcing their accumulation in landfills and raising environmental concerns. One possible solution to overcome this concern is to use resins or curing agents, or both, made from biodegradable materials. This study explores the fabrication and characterization of polymer composites using a commercially available green curing agent made from biomass. The composite laminates were fabricated using HVARTM (Heated Vacuum Assisted Resin Transfer Molding) process. In this process, heat pads are used to increase the temperature of both the epoxy resin and the plain weave carbon fiber laminate to a desired temperature, providing ease of flow to the resin. Small coupons were cut from the laminate using a water jet machine to study the flexural behavior of the composite in accordance with ASTM testing standards and compared with composite coupons fabricated using conventional epoxy resin.more » « less
-
Abstract Dynamic bond exchanging vitrimers have emerged recently due to their malleability, self‐heal ability, recyclability, and mechanical stability. Likewise, 3D printing is consciously introduced at different platforms for ease of fabrication, high throughput, cost‐effectiveness, and waste reduction. These two distinctive techniques have recently made their consensus performance, resulting from a phenomenal change in the printing field. Conventionally, thermoplastic inks have been primarily used in 3D printing, owing to their effortless processability. At the same time, thermosets were utilized for their superior mechanical strength. However, these two essential properties have been required to be presented in the printed material. In that scenario, thermoset vitrimer materials have been introduced in 3D printing, where malleability and mechanical stability have been observed in the same material. Thus, this article details the recent vitrimer material included with the different 3D printing system systems with their reported results to understand and make them widespread. Eventually, the outlook and perspectives could be helpful to understand and enhance this specific field.more » « less