Abstract Visualizing the network of a solvent‐swollen polymer gel remains problematic. To address this challenge, open transmission electron microscopy (TEM) was applied to thin gel films permeated by a nonvolatile ionic liquid. The targeted physical gels were prepared by cooling concentrated solutions of poly(ethylene glycol) in 1‐ethyl‐3‐methyl imidazolium ethyl sulfate [EMIM][EtSO4]. During the cooling, gelation occurred by a frustrated crystallization of the dissolved polymer, leading to a percolated, solvent‐permeated semicrystalline network in which nanoscale polymer crystals acted as crosslinks. Crystalline features ranging from ~5 to ~200 nm were observed, with the visible network strands dominantly consisting of long curvilinear crystallites of ~15–20 nm diameter. Nascent spherulites irregularly decorated the network, creating a complex structural hierarchy that complicated analyses. Lacking diffraction contrast, TEM did not visualize the many disordered, fully solvated PEG chains present in the voids between crystals. Recognizing that a network's three dimensionality is ambiguous when assessed through two‐dimensional microscopy projections, a small gel region was studied by TEM tomography, revealing a nearly isotropic three‐dimensional arrangement of the curvilinear crystallites, which displayed remarkably uniform cylindrical cross sections.
more »
« less
In Situ Electron Microscopy of Poly(ethylene glycol) Crystals Grown in Thin Ionic Liquids Films
ABSTRACT Crystals of poly(ethylene glycol) grown in thin films of the room temperature ionic liquid (IL) 1‐ethyl‐3‐methylimidazolium ethyl sulfate were examined by electron microscopy as a first step toward exploiting nonvolatile liquids for nanoscale imaging of solvated/dissolved polymeric materials. The crystals were generated by cooling supported (over surfaces of varied polarity) and freestanding solution films to room temperature. This “open,” that is, without liquid cell, microscopy was performed on unstained, as‐grown crystals in the presence of the IL. A variety of nearly two‐dimensional crystal morphologies were observed, including rods, fibers, spherulites, compact faceted single crystals, and interconnected networks, with characteristic sizes ranging from tens of nanometers to tens of microns. Electron diffraction patterns for the rods and fibers revealed single crystal‐like long‐range order. The nature of the IL support little affected the morphology, but film thickness and cooling rate proved important. To assess the role of solvent polarity, crystals were also grown from 1‐ethyl‐3‐methylimidazolium ethyl sulfate mixed with the second IL, the less polar ethyl‐tributyl‐phosphonium diethyl phosphate; here, although the morphologies were similar to those made with pure IL, fibrillar morphologies were more prevalent. © 2020 Wiley Periodicals, Inc. J. Polym. Sci.2020,58, 478–486
more »
« less
- Award ID(s):
- 1807255
- PAR ID:
- 10459339
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Journal of Polymer Science
- Volume:
- 58
- Issue:
- 3
- ISSN:
- 2642-4150
- Page Range / eLocation ID:
- p. 478-486
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The phenomenon of ionic liquid (IL) nanoconfinement within a copolymer/IL membrane reportedly enhances membrane selectivity, solubility, and transport in gas separations. Also, the copolymer/IL membrane morphology has been found to affect IL stability at high transmembrane pressures. In this work, a combined mesoscopic dynamics simulation and hybrid grand canonical Monte Carlo/molecular dynamics (GCMC-MD) simulations were carried out to investigate the morphologies, as well as CO2/CH4 gas diffusivities, solubilities, and selectivities of polystyrene-b-poly(ethylene oxide) (PS-b-PEO)/1-Ethyl-3-methylimidazolium thiocyanate ([EMIM][SCN]) and PS-b-PEO/1-Ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide ([EMIM][Tf2N]) membranes. The latter simulations focused on nanoconfined ILs in the copolymer/IL phase boundaries at 2.5 and 5 nm confinement lengths. The investigated systems were four nanoconfined ILs, i.e., PS/[EMIM][SCN]/PEO (the IL forming a separate microphase, denoted IL-Micro), PS/[EMIM][Tf2N]/PEO, PS/[EMIM][SCN]-PEO/PS (the IL distributed in the PEO phase, denoted IL-PEO), and PS/[EMIM][Tf2N]-PEO/PS, and five control systems, i.e., PS/PEO/PS, bulk PS, bulk PEO, bulk [EMIM][SCN], and bulk [EMIM][Tf2N]. Based on the mesoscopic dynamics simulation results, the dominant membrane morphologies at IL loadings of <50 vol % were lamellar or cylindrical (favorable for both IL stability at high transmembrane pressures if the bedding planes are horizontal, i.e. at 90° to the nominal direction of the transmembrane pressure gradient) with the IL-PEO or IL-Micro phases. Also, there was an overall 50% match between the observed PS-b-PEO/[EMIM][SCN] and PS-b-PEO/[EMIM][Tf2N] membrane morphologies. Based on the MD simulation results, both CO2 and CH4 diffusivities were the smallest in the bulk PS (control) and highest in the PS/[EMIM][Tf2N]/PEO system (IL-Micro between the PS and PEO phases) at both confinement lengths. The CO2 diffusivities were, on average, larger when the confinement length increased to 5 nm. The GCMC-MD results indicated that the CO2 solubility in the IL-Micro phases was higher than in the corresponding bulk ILs at both confinement lengths, with the PS/[EMIM][Tf2N]/PEO system exhibiting the highest CO2 solubility, followed by the PS/[EMIM][SCN]/PEO system. Additionally, the permselectivities of the nanoconfined IL systems were, on average, 40–50% larger than those of the bulk systems, with the highest permselectivity observed for PS/[EMIM][Tf2N]/PEO at the confinement length of 5 nm. Overall, the IL nanoconfinement between the PS and PEO phases (IL-Micro) leads to significant improvements in the CO2/CH4 permselectivities, suggesting that strategies to create nanoconfined IL morphologies in the copolymer/IL membranes are very promising for optimizing the membrane gas separation performance.more » « less
-
In this paper, the solubility properties of the ionic liquid (IL), 1-ethyl-3-methylimidazolium tetrafluoroborate ([EMIM][BF4]) were studied using a high-pressure, high-temperature set-up employing the pressure-drop technique. [EMIM][BF4] was selected for study because it is used as the sweep liquid in a membrane reactor (MR)-based methanol synthesis (MR-MeS) process recently proposed and studied by our group. The MR-MeS studies indicated high methanol (MeOH) solubilities in the IL under typical MeS reaction conditions, which then motivated this study to measure such solubilities directly under non-reactive conditions to validate the findings of the MR study. In addition, during the MR-MeS studies a concern existed about the solubility of CO2 in [EMIM][BF4], since it is a reactant in the MeS process and its dissolution in the sweep liquid would be detrimental for reactor performance. Studies, therefore, were also carried out to investigate the solubility of CO2, in addition to MeOH, in the IL. Our investigation indicates that though CO2 solubilities in the [EMIM][BF4] are high at room temperature, they become negligible at the typical MeS operating conditions (i.e., temperatures above 200 ⁰C).more » « less
-
Atomic layer deposition (ALD) is a technologically important method to grow thin films with high conformality and excellent thickness control from vapor phase precursors. The development of new thermal ALD processes can be limited by precursor reactivity and stability: reaction temperature and precursor design are among the few variables available to achieve higher reactivity, unlike in solution synthesis where the use of solvent and/or a catalyst can promote a desired reaction. To bridge this synthesis gap between vapor and solution, we demonstrate the use of an ultrathin coating layer of a vapor-phase compatible solvent—an ionic liquid (IL)— onto our growth substrate to perform ALD of SnO. Successful SnO deposition is achieved using tin acetylacetonate and water, a process that otherwise would require a stronger counter-reactant such as ozone. The layer of IL allows a solvent-mediated reaction mechanism to take place on the growth substrate. We report a growth per cycle of 0.67 Å/cycle at a deposition temperature of 100 °C in an IL comprised of 1-ethyl-3-methylimidazolium hydrogen sulfate. Characterization of the ALD films confirms the SnO film composition, and 1H and 13C NMR are used to probe the solvent-mediated ALD reaction, suggesting a solvent-mediated addition-elimination type mechanism forming acetone and acetate. Density functional theory calculations show that the ionic liquid solvent is beneficial to the proposed solvent-mediated mechanism by lowering the C-C bond cleavage energetics of acetylacetonate compared to the vapor phase. A general class of ligand-modification reactions for thermal ALD is thus introduced in this work.more » « less
-
Abstract Boron nitride nanotubes (BNNTs) have attracted attention for their predicted extraordinary properties; yet, challenges in synthesis and processing have stifled progress on macroscopic materials. Recent advances have led to the production of highly pure BNNTs. Here we report that neat BNNTs dissolve in chlorosulfonic acid (CSA) and form birefringent liquid crystal domains at concentrations above 170 ppmw. These tactoidal domains merge into millimeter-sized regions upon light sonication in capillaries. Cryogenic electron microscopy directly shows nematic alignment of BNNTs in solution. BNNT liquid crystals can be processed into aligned films and extruded into neat BNNT fibers. This study of nematic liquid crystals of BNNTs demonstrates their ability to form macroscopic materials to be used in high-performance applications.more » « less