TBF 1180 steel was plastically deformed under different strain paths in order to study both the ductility and RA transformation rates. Specimens were prepared from a 1 mm thick sheet and then tested incrementally under uniaxial tension, plane-strain tension, and biaxial tension. The retained austenite (RA) levels were measured, as a function of the plastic strain, using electron backscatter diffraction (EBSD). The plane-strain tension specimens had the fastest rate of RA transformation as a function of strain, followed by uniaxial tension, and then biaxial tension. The forming limits were measured for each strain path, yielding major limit strains of 0.12 under uniaxial tension, 0.09 under plane-strain tension, and 0.16 under biaxial tension. These results were compared to prior work on a 1.2 mm Q&P 1180 steel sheet, which had a similar yield and ultimate tensile strength, but exhibited slightly greater forming limits than the TBF material. The visual inspection of the micrographs appeared to show an equiaxed RA morphology in the Q&P 1180 steel and a mixture of equiaxed and lamellar RA grains in the TBF 1180 steel. However, the statistics generated by EBSD revealed that both alloys had RA grains with essentially the same aspect ratios. The average RA grain size in the Q&P alloy was found to be about three times larger than that of the TBF alloy. As such, the small but consistent formability advantage exhibited by the Q&P 1180 alloy along all three strain paths can be attributed to its larger average RA grain size, where larger RA grain sizes correlated with a more gradual transformation rate.
more »
« less
Characterization of the Factors Influencing Retained Austenite Stability in Q&P Steels via In Situ EBSD
The current work studies the correlations between microstructure and retained austenite (RA) transformation, in a single-quenched and partitioned (Q&P) 1180 steel microstructure, through in situ tensile tests combined with electron backscatter diffraction (EBSD) analysis. This allows the study of RA stability across a limited range of morphological characteristics to be studied in the absence of confounding factors introduced by varying the entire steel microstructure. Among the microstructural attributes of interest, RA grain aspect ratio is found to have the largest influence on transformation rate, where globular-shaped grains transform more slowly than those with a more lenticular shape. Furthermore, by tracking individual grains during deformation, it is apparent that larger grains transformed more slowly than smaller grains; a purely statistical study of grain size vs strain might conclude that smaller grains are more stable, but in reality, the smaller grains transform faster and are simply statistically replaced by partially transformed larger grains. These conclusions are in contrast to relationships that might be inferred from previous studies where the entire steel microstructure was varied, along with the morphology of the RA.
more »
« less
- Award ID(s):
- 1926662
- PAR ID:
- 10488167
- Publisher / Repository:
- Springer
- Date Published:
- Journal Name:
- Metallurgical and Materials Transactions A
- Volume:
- 54
- Issue:
- 4
- ISSN:
- 1073-5623
- Page Range / eLocation ID:
- 1355 to 1363
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
ABSTRACT We study the linear growth and non-linear saturation of the ‘acoustic Resonant Drag Instability’ (RDI) when the dust grains, which drive the instability, have a wide, continuous spectrum of different sizes. This physics is generally applicable to dusty winds driven by radiation pressure, such as occurs around red-giant stars, star-forming regions, or active galactic nuclei. Depending on the physical size of the grains compared to the wavelength of the radiation field that drives the wind, two qualitatively different regimes emerge. In the case of grains that are larger than the radiation’s wavelength – termed the constant-drift regime – the grain’s equilibrium drift velocity through the gas is approximately independent of grain size, leading to strong correlations between differently sized grains that persist well into the saturated non-linear turbulence. For grains that are smaller than the radiation’s wavelength – termed the non-constant-drift regime – the linear instability grows more slowly than the single-grain-size RDI and only the larger grains exhibit RDI-like behaviour in the saturated state. A detailed study of grain clumping and grain–grain collisions shows that outflows in the constant-drift regime may be effective sites for grain growth through collisions, with large collision rates but low collision velocities.more » « less
-
Microstructure refinement strategies in simulated carburized microstructures were evaluated because of their potential for improving the fatigue performance of case carburized components. Commercial 52100 steel was used to simulate the high carbon content in the case. Specimens were subjected to various thermal treatments in a quenching dilatometer. Reheating cycles to austenitizing temperatures were evaluated with respect to both prior austenite grain size (PAGS) and associated martensite and retained austenite (RA) refinement. Quantitative stereological measurements were performed to evaluate the micro-geometry of plate martensite and the size distribution of RA regions. Decreasing the reheating temperature resulted in finer PAGS, and multiple reheating cycles resulted in a more narrow PAGS distribution. Refinement in PAGS led to a reduction in martensite plate size and finer distribution of RA. Additionally, interrupted quenching below MS temperature was evaluated. This processing route results in a refinement of martensite plates and more stable RA. The stabilization of austenite may be mechanical or chemical in nature, owing to deformation of austenite during primary transformation, or due to partitioning of carbon into austenite similar to quenching and partitioning steels.more » « less
-
This study focuses on the kinetic analysis of sigma phase formation in filler metal wires on Super Duplex Stainless Steel (SDSS) and Hyper Duplex Stainless Steel (HDSS). Precipitation data reveal that in the solubilized microstructure, sigma phase kinetics are more prominent in SDSS. This increased susceptibility is attributed to the greater number of nucleation sites, which is facilitated by the larger interface area/volume and the higher chromium content in the ferrite. The difference in interface area/volume is significantly more influential in determining kinetics than the composition difference, with nucleation sites playing a central role. The sigma phase transformation in both materials was modeled using the JMAK kinetic law. The JMAK plots exhibit a transition in kinetic mechanisms, evolving from discontinuous precipitation to diffusion-controlled growth. In SDSS, the JMAK values indicate “grain boundary nucleation after saturation,” followed by “thickening of large plates.” In contrast, HDSS values point to “grain edge nucleation after saturation,” followed by “thickening of large needles.” The higher kinetics in SDSS are characterized by a smaller nucleation activation energy of 56.4 kJ/mol, in contrast to HDSS's 490.0 kJ/mol. CALPHAD-based data support the JMAK results, aligning with the maximum kinetics temperature of SDSS (875 °C to 925 °C) and HDSS (900 °C to 925 °C). Therefore, the JMAK sigma phase kinetics effectively describe the experimental data and its dual kinetics behavior, even though CALPHAD-based TTT calculations often overestimate sigma formation.more » « less
-
Abstract Wire arc additive manufacturing (WAAM) is an efficient technique for producing medium to large‐size components, due to its accessibility and sustainability in fabricating large‐scale parts with high deposition rates, employing low‐cost and simple equipment, and achieving high material efficiency. Consequently, WAAM has garnered attention across various industrial sectors and experienced significant growth, particularly over the last decade, as it addresses and mitigates challenges within production markets. One of the primary limitations of WAAM is its thermal history during the process, which directly influences grain formation and microstructure heterogeneity in the resulting part. Understanding the thermal cycle of the WAAM process is thus crucial for process improvement. Typically, fabricating a part using WAAM results in a microstructure with three distinct zones along the build direction: an upper zone (thin surface layer) with fine grains, a middle zone dominated by undesirably long and large columnar grains covering more than 90% of the produced part, and a lower zone with smaller to intermediate columnar grains closer to the substrate material. These zones arise from variations in cooling rates, with the middle zone exhibiting the lowest cooling rate due to 2D conduction heat transfer. Consequently, producing a component with a microstructure comprising three different zones, with a high fraction of large and long columnar grains, significantly impacts the final mechanical properties. Therefore, controlling the size and formation of these grain zones plays a key role in improving WAAM. The aim of this work is to investigate the formation of undesired columnar grains in austenitic stainless steel 316L during WAAM and propose a simple hybrid technique by combining WAAM with a hot forging process (with or without interlayer cooling time). This approach targets the disruption of the solidification pattern of columnar grain growth during deposition progression and aims to enhance the microstructure of WAAM components.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1007/s11661-023-06991-4