Abstract A sliding electrolyte metal‐air microbattery driven by natural eye blinking motion is demonstrated as a source of electrical energy that can be integrated with smart contact lens platforms. The metal‐air battery (footprint 10 mm2) consists of a Mg anode and a Pt cathode, patterned on an insulating substrate and the battery electrolyte is a film of eye‐tear fluid that is periodically dragged on top of the electrodes during the natural eye‐blinking cycle, which activates the battery. When tested with an eye emulator, the open‐circuit voltage across the eye‐tear activated metal‐air battery (ETMAB) is 2.2 V. Impedance matching analysis reveals a maximum battery‐specific capacity of 3561 mAh g–1obtained at a discharge current density of 5 mA cm–2. The blinking activated battery exhibits the maximum generated power density of 1.3 mW cm–2at the load of 740 Ω. The blinking ETMAB delivers eight times higher energy output and more than three times longer lifetime than achievable with static ETMAB designs.
more »
« less
Power Scavenging Microsystem for Smart Contact Lenses
Abstract On‐the‐eye microsystems such as smart contacts for vision correction, health monitoring, drug delivery, and displaying information represent a new emerging class of low‐profile (≤ 1 mm) wireless microsystems that conform to the curvature of the eyeball surface. The implementation of suitable low‐profile power sources for eye‐based microsystems on curved substrates is a major technical challenge addressed in this paper. The fabrication and characterization of a hybrid energy generation unit composed of a flexible silicon solar cell and eye‐blinking activated Mg–O2metal–air harvester capable of sustainably supplying electrical power to smart ocular devices are reported. The encapsulated photovoltaic device provides a DC output with a power density of 42.4 µW cm−2and 2.5 mW cm−2under indoor and outdoor lighting conditions, respectively. The eye‐blinking activated Mg–air harvester delivers pulsed power output with a maximum power density of 1.3 mW cm−2. A power management circuit with an integrated 11 mF supercapacitor is used to convert the harvesters’ pulsed voltages to DC, boost up the voltages, and continuously deliver ≈150 µW at a stable 3.3 V DC output. Uniquely, in contrast to wireless power transfer, the power pack continuously generates electric power and does not require any type of external accessories for operation.
more »
« less
- Award ID(s):
- 1932602
- PAR ID:
- 10496248
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Small
- ISSN:
- 1613-6810
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)We report the design, fabrication, and experimental characterization of a chip-sized electromechanical micro-receiver for low-frequency, near-field wireless power transmission that employs both electrodynamic and piezoelectric transductions to achieve a high power density and high output voltage while maintaining a low profile. The 0.09 cm 3 device comprises a laser-micro-machined titanium suspension, one NdFeB magnet, two PZT-5A piezo-ceramic patches, and a precision-manufactured micro-coil with a thickness of only 1.65 mm. The device generates 520 μW average power (5.5 mW•cm -3 ) at 4 cm distance from a transmitter coil operating at 734.6 Hz and within safe human exposure limits. Compared to a previously reported piezoelectric-only prototype, this device generates ~2.5x higher power and offers 18% increased normalized power density (6.5 mW•cm -3 •mT -2 ) for potential improvement in wirelessly charging wearables and bio-implants.more » « less
-
This paper presents the design and measurement results of wireless power transfer through soil over a range of soil moisture levels for future low-cost, wireless, battery-less, and in-situ soil health monitoring technologies. A pair of packaged 6 cm-diameter coils can wirelessly transfer 0.56 mW from an external RF power source of 37 mW through a soil depth of 15 cm over a typical moisture level ranging from low 30% to 40%. An optimal frequency of 1.4 MHz and 1 MHz was chosen for an efficient operation in loamy soil and sandy soil, respectively. The demonstrated power transfer is sufficient to energize underground soil health monitoring devices. In addition, a pair of packaged 12 cm-diameter coils, taking the loss contributed by the surrounding soil into design consideration, can achieve a 130 µW power delivery with an efficiency of approximately 8% over a 30 cm air gap. It is expected that a similar performance can be achieved through a 30 cm soil depth.more » « less
-
Mid-infrared photonic integrated circuits (PICs) that combine on-chip light sources with other optical components constitute a key enabler for applications such as chemical sensing, light detection, ranging, and free-space communications. In this paper, we report the monolithic integration of interband cascade lasers emitting at 3.24 µm with passive, high-index-contrast waveguides made of chalcogenide glasses. Output from the chalcogenide waveguides exhibits pulsed peak power up to 150 mW (without roll-over), threshold current density 280 A/cm2, and slope efficiency 100 mW/A at 300 K, with a lower bound of 38% efficiency for coupling between the two waveguides. These results represent an important step toward the realization of fully integrated mid-infrared PICs.more » « less
-
Abstract For piezoelectric energy harvesters, a large volume of piezoelectric material with a high figure of merit is essential to obtain a higher power density. The work describes the growth of highly (001) oriented sputtered lead zirconate titanate (PZT) films (f≈ 0.99) exceeding 4 µm in thickness on both sides of an Ni foil to produce a bimorph structure. These films are incorporated in novel wrist‐worn energy harvesters (<16 cm2) in which piezoelectric beams are plucked magnetically using an eccentric rotor with embedded magnets to implement frequency up‐conversion. The resulting devices successfully convert low‐frequency vibration sources (i.e., from walking, rotating the wrist, and jogging) to higher frequency vibrations of the PZT beams (100–200 Hz). Measured at resonance, six beams producing an output of 1.2 mW is achieved at 0.15 G acceleration. For magnetic plucking of a wrist‐worn nonresonant device, 40–50 µW is produced during mild activity.more » « less