In this work, we have prepared intergrowth of multiferroic compounds namely Bi4RTi3Fe0.7Co0.3O15-Bi3RTi2Fe0.7Co0.3O12−δ (BRTFCO15-BRTFCO12) (rare earth (R) = Dy, Sm, La) by solid-state reaction method. From the X-ray diffraction Rietveld refinement, the structure of the intergrowths was found to be orthorhombic in which satisfactory fittings establish the existence of three-layered (space group: b 2 c b) and four-layered compounds (space group: A21am). Analysis of magnetic measurements confirmed a larger magnetization for theSm-modified intergrowth compound (BSTFCO15-BSTFCO12) compared to Dy- and La-doped ones. The emergence of higher magnetic properties can be due to distortion in the unit cell when some Bi3+ ions are replaced with the Sm3+, bonding of Fe3+-O-Co3+ as well as a possible mixture of FexCoy-type nanoparticles that are formed generally in the synthesis of intergrowths. The changes in the magnetic state of the Aurivillius intergrowths have been reflected in the magnetoelectric (ME) coupling: higher ME coefficient (~30 mV/Cm-Oe) at lower magnetic fields and is constant up to 3 kOe. The results were corroborated by Raman spectroscopy and variation of temperature with magnetization data. The results revealed that the RE-modified intergrowth route is an effective preparative method for higher-layer Aurivillius multiferroic ceramics.
more »
« less
Magnetoelectric Properties of Aurivillius-Layered Perovskites
In the present work, we have synthesized rare-earth ion modified Bi4−xRExTi2Fe0.7Co0.3O12−δ (RE = Dy, Sm, La) multiferroic compounds by the conventional solid-state route. Analysis of X-ray diffraction by Rietveld refinement confirmed the formation of a polycrystalline orthorhombic phase. The morphological features revealed a non-uniform, randomly oriented, plate-like grain structure. The peaks evident in the Raman spectra closely corresponded to those of orthorhombic Aurivillius phases. Dielectric studies and impedance measurements were carried out. Asymmetric complex impedance spectra suggested the relaxation of charge carriers belonging to the non-Debye type and controlled by a thermally activated process. Temperature-dependent AC conductivity data showed a change of slope in the vicinity of the phase transition temperature of both magnetic and electrical coupling natures. Based on the universal law and its exponent nature, one can suppose that the conduction process is governed by a small polaron hopping mechanism but significant distortion of TiO6 octahedral. The doping of the A-sites with rare-earth element ions and changes in the concentrations of Fe and Co ions located on the B-sites manifested themselves in saturated magnetic hysteresis loops, indicating competitive interactions between ferroelectric and canted antiferromagnetic spins. The magnetic order in the samples is attributed to pair-wise interactions between adjacent Fe3+–O–Fe3+, Co2+/3+–O–Co3+/2+, and Co2+/3+–O–Fe3+ ions or Dzyaloshinskii–Moriya interactions among magnetic ions in the adjacent sub-lattices. As a result, enhanced magnetoelectric coefficients of 42.4 mV/cm-Oe, 30.3 mV/cm-Oe, and 21.6 mV/cm-Oe for Bi4−xDyxTi2Fe0.7Co0.3O12−δ (DBTFC), Bi4−xLaxTi2Fe0.7Co0.3O12−δ (LBTFC), and Bi4−xSmxTi2Fe0.7Co0.3O12−δ (SBTFC), respectively, have been obtained at lower magnetic fields (<3 kOe). The strong coupling of the Aurivillius compounds observed in this study is beneficial to future multiferroic applications.
more »
« less
- PAR ID:
- 10544750
- Publisher / Repository:
- MDPI
- Date Published:
- Journal Name:
- Crystals
- Volume:
- 14
- Issue:
- 4
- ISSN:
- 2073-4352
- Page Range / eLocation ID:
- 299
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Iron-based extended metal atom chains (EMACs) are potentially high-spin molecules with axial magnetic anisotropy and thus candidate single-molecule magnets (SMMs). We herein compare the tetrairon( ii ), halide-capped complexes [Fe 4 (tpda) 3 Cl 2 ] ( 1Cl ) and [Fe 4 (tpda) 3 Br 2 ] ( 1Br ), obtained by reacting iron( ii ) dihalides with [Fe 2 (Mes) 4 ] and N 2 , N 6 -di(pyridin-2-yl)pyridine-2,6-diamine (H 2 tpda) in toluene, under strictly anhydrous and anaerobic conditions (HMes = mesitylene). Detailed structural, electrochemical and Mössbauer data are presented along with direct-current (DC) and alternating-current (AC) magnetic characterizations. DC measurements revealed similar static magnetic properties for the two derivatives, with χ M T at room temperature above that for independent spin carriers, but much lower at low temperature. The electronic structure of the iron( ii ) ions in each derivative was explored by ab initio (CASSCF-NEVPT2-SO) calculations, which showed that the main magnetic axis of all metals is directed close to the axis of the chain. The outer metals, Fe1 and Fe4, have an easy-axis magnetic anisotropy ( D = −11 to −19 cm −1 , | E / D | = 0.05–0.18), while the internal metals, Fe2 and Fe3, possess weaker hard-axis anisotropy ( D = 8–10 cm −1 , | E / D | = 0.06–0.21). These single-ion parameters were held constant in the fitting of DC magnetic data, which revealed ferromagnetic Fe1–Fe2 and Fe3–Fe4 interactions and antiferromagnetic Fe2–Fe3 coupling. The competition between super-exchange interactions and the large, noncollinear anisotropies at metal sites results in a weakly magnetic non-Kramers doublet ground state. This explains the SMM behavior displayed by both derivatives in the AC susceptibility data, with slow magnetic relaxation in 1Br being observable even in zero static field.more » « less
-
Abstract Spin-orbit coupling is an important ingredient to regulate the many-body physics, especially for many spin liquid candidate materials such as rare-earth magnets and Kitaev materials. The rare-earth chalcogenides Equation missing<#comment/>(Ch = O, S, Se) is a congenital frustrating system to exhibit the intrinsic landmark of spin liquid by eliminating both the site disorders between Equation missing<#comment/>and Equation missing<#comment/>ions with the big ionic size difference and the Dzyaloshinskii-Moriya interaction with the perfect triangular lattice of the Equation missing<#comment/>ions. The temperature versus magnetic-field phase diagram is established by the magnetization, specific heat, and neutron-scattering measurements. Notably, the neutron diffraction spectra and the magnetization curve might provide microscopic evidence for a series of spin configuration for in-plane fields, which include the disordered spin liquid state, 120° antiferromagnet, and one-half magnetization state. Furthermore, the ground state is suggested to be a gapless spin liquid from inelastic neutron scattering, and the magnetic field adjusts the spin orbit coupling. Therefore, the strong spin-orbit coupling in the frustrated quantum magnet substantially enriches low-energy spin physics. This rare-earth family could offer a good platform for exploring the quantum spin liquid ground state and quantum magnetic transitions.more » « less
-
We present structural, magnetic, and optical properties of multiferroic hexagonal YbFeO3 thin films, deposited on single crystal (001) Al2O3 and (111) ysz substrates by a magnetron sputtering system. Interestingly, the thermal stress affects YbFeO3 films on Al2O3 and ysz very differently. Although hexagonal-YbFeO3/Al2O3 films changed from a hexagonal to an orthorhombic phase due to annealing above 1000 °C, hexagonal-YbFeO3/ysz films remained mostly unaffected even after annealing at 1200 °C. The electronic excitations of the YbFeO3 thin films are dominated by Fe3+ d to d on-site electronic excitations as well as O 2p to Fe 3d, Yb 6s, and 5d charge-transfer excitations, and these excitations for hexagonal-YbFeO3 and orthorhombic-YbFeO3 thin films are distinctly different, consistent with the crystal field environments in the hexagonal and orthorhombic phases of YbFeO3. The room temperature energy band gaps of the hexagonal-YbFeO3 and orthorhombic-YbFeO3 thin films were measured to be ∼1.95 ± 0.05 eV and ∼2.40 ± 0.05 eV, respectively.more » « less
-
Abstract An extended series of rare‐earth metal calcium germanides have been synthesized and structurally characterized. The compounds have the general formulaRE5−xCaxGe4(1.5<x<3.6;RE=rare‐earth metal; Ce, Nd, Sm, Tb−Lu) and their structures have been established from single‐crystal X‐ray diffraction methods. They crystallize with the Gd5Si4‐type in the orthorhombic space groupPnma(No. 62;Z=4; Pearson symboloP36), where the germanium atoms are interconnected into two kinds of Ge2‐dimers, formally [Ge2]6−. These studies show that Ca can be successfully incorporated into the hostRE5Ge4structure, whereby trivalent rare‐earth metal atoms can be substituted by divalent calcium atoms. Rare‐earth metal and calcium atoms are arranged in distorted trigonal prisms and cubes, centered by either Ge or Ca atoms. On one of the metal sites, the substitution is preferential and in 9 out of the 10 refined structures, the Wyckoff site 4cis found almost exclusively occupied by Ca. On the other two metal sites the substitution patterns appear to be governed by the mismatch between the size of theRE3+and Ca2+ions. This work further demonstrates the ability for the Gd5Si4structure type to accommodate the substitution of a non‐magnetic element while maintaining the global structural integrity.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.3390/cryst14040299