Additive manufacturing (AM) is a powerful technique for producing metallic components with complex geometry relatively quickly, cheaply and directly from digital representations; however, residual stresses induced during manufacturing can result in distortions of components and reductions in mechanical performance, especially in parts that lack rotational symmetry and, or have cross sections with large aspect ratios. Geometrically reinforced thin plates have been built in nickel–chromium alloy using laser-powder bed fusion (L-PBF) and their shapes measured using stereoscopic digital image correlation before and after release from the base-plate of the AM machine. The results show that residual stresses cause potentially severe out-of-plane deformation that can be alleviated using either an enveloping support structure, which increased the build time substantially, was difficult to remove and wasted material, or using buttress supports to the reinforced edges of the thin plate. The buttresses were quick to build and remove, minimised waste but needed careful design. Plates built in a landscape orientation required out-of-plane buttresses while those built in a portrait orientation required both in-plane and out-of-plane buttresses. In both cases, out-of-plane deformation increased on release from the baseplate but this was mitigated by incremental release which resulted in out-of-plane deformations of less than 5% of the in-plane dimensions.
Additively-manufactured parts contain residual stresses induced by manufacturing. These residual stresses can be relaxed or redistributed by thermal loading. The presence of internal stress influences the dynamic response of parts, and this is of particular interest in thin plates subject to thermoacoustic loading in hypersonic vehicles and fusion reactors.
To measure the changes in shape and modal frequencies caused by thermal loading of geometrically-reinforced thin plates that were additively manufactured in Inconel 625.
Plates were additively-manufactured in landscape and portrait orientations using laser powder bed fusion. The plates were heated to a nominal temperature of 820 ̊C, which was expected to alleviate the residual stress from the build process. Pre- and post-heating, their modal frequencies were found experimentally and pulsed-laser stereo (3D) digital image correlation was used to evaluate their modal shapes. The resultant modal frequencies and shapes were compared with those from a subtractively-manufactured plate.
It was found that the heat cycle changed the shape of the plates relative to their as-manufactured state in addition to changing their natural frequencies and modal shapes.
The change in shape induced by heating caused shifts in the natural frequencies and changes in the corresponding modal shapes. The results show quantitatively for the first time the important role that residual stresses can play in the dynamic response of geometrically-reinforced thin plates manufactured by additive and subtractive processes.
- PAR ID:
- 10567679
- Publisher / Repository:
- Springer Science + Business Media
- Date Published:
- Journal Name:
- Experimental Mechanics
- ISSN:
- 0014-4851
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
Abstract This work studies the use of laser shock peening (LSP) to improve back stress in additively manufactured (AM) 316L parts. Unusual hardening behavior in AM metal due to tortuous microstructure and strong texture poses additional design challenges. Anisotropic mechanical behavior complicates application for mechanical design because 3D printed parts will behave differently than traditionally manufactured parts under the same loading conditions. The prevalence of back-stress hardening or the Bauschinger effect causes reduced fatigue life under random loading and dissipates beneficial compressive residual stresses that prevent crack propagation. LSP is known to improve fatigue life by inducing compressive residual stress and has been applied with promising results to AM metal parts. It is here demonstrated that LSP may also be used as a tool for mitigating tensile back-stress hardening in AM parts, thereby reducing anisotropic hardening behavior and improving design use. It is also shown that the method of application of LSP to additively manufactured parts is key for achieving effective back-stress reduction. Back stress is extracted from additively manufactured dog bone samples built in both XY and XZ directions using hysteresis tensile. Both LSPed and as-built conditions are tested and compared, showing that LSPed samples exhibit a significant reduction to back stress when the laser processing is applied to the sample along the build direction. Electron backscatter diffraction (EBSD) performed under these conditions elucidates how grain morphologies and texture contribute to the observed improvement. Crystal plasticity finite element (CPFE) modeling develops insights as to the mechanisms by which this reduction is achieved in comparison with EBSD results. In particular, the difference in plastic behavior across build orientations of identified crystal planes and grain families are shown to impact the degree of LSP-induced back-stress reduction that is sustained through tensile loading.more » « less
-
more » « less
Abstract The far-from-equilibrium solidification during additive manufacturing often creates large residual stresses that induce solid-state cracking. Here we present a strategy to suppress solid-state cracking in an additively manufactured AlCrFe2Ni2high-entropy alloy via engineering phase transformation pathway. We investigate the solidification microstructures formed during laser powder-bed fusion and directed energy deposition, encompassing a broad range of cooling rates. At high cooling rates (104−106 K/s), we observe a single-phase BCC/B2 microstructure that is susceptible to solid-state cracking. At low cooling rates (102−104 K/s), FCC phase precipitates out from the BCC/B2 matrix, resulting in enhanced ductility (~10 %) and resistance to solid-state cracking. Site-specific residual stress/strain analysis reveals that the ductile FCC phase can largely accommodate residual stresses, a feature which helps relieve residual strains within the BCC/B2 phase to prevent cracking. Our work underscores the value of exploiting the toolbox of phase transformation pathway engineering for material design during additive manufacturing.
-
more » « less
Laser-directed energy deposition (DED), a metal additive manufacturing method, is renowned for its role in repairing parts, particularly when replacement costs are prohibitive. Ensuring that repaired parts avoid residual stresses and deformation is crucial for maintaining functional integrity. This study conducts experimental and numerical analyses on trapezoidal shape repairs, validating both the thermal and mechanical models with experimental results. Additionally, the study presents a methodology for creating a toolpath applicable to both the DED process and Abaqus CAE software. The findings indicate that employing a pre-heating strategy can reduce residual stresses by over 70% compared to no pre-heating. However, pre-heating may not substantially reduce final distortion. Notably, final distortion can be significantly mitigated by pre-heating and subsequently cooling to higher temperatures, thereby reducing the cooling rate. These insights contribute to optimizing DED repair processes for enhanced part functionality and longevity.
-
As additive manufacturing becomes an increasingly popular method for advanced manufacturing of components, there are many questions that need to be answered before these parts can be implemented for structural purposes. One of the most common concerns with additively manufactured parts is the reliability when subjected to cyclic loadings which has been shown to be highly sensitive to defects such as pores and lack of fusion between layers. It stands to reason that larger parts will inherently have more defects than smaller parts which may result in some sensitivity to surface area differences between these parts. In this research, Ti-6Al-4V specimens with various sizes were produced via a laser-based powder bed fusion method. Uniaxial fatigue tests based on ASTM standards were conducted to generate fatigue-life curves for comparison. Fractography on the fractured specimens was performed to distinguish failure mechanisms between specimen sets with different sizes.more » « less