Thermophotovoltaics (TPVs) are a potential technology for waste-heat recovery applications and utilize IR sensitive photovoltaic diodes to convert long wavelength photons (>800nm) into electrical energy. The most common conversion regions utilize Gallium Antimonide (GaSb) as the standard semiconductor system for TPV diodes due to its high internal quantum efficiencies (close to 90%) for infrared radiation (~1700nm). However, parasitic losses prevent high conversion efficiencies from being achieved in the final device. One possible avenue to improve the conversion efficiency of these devices is to incorporate metallic photonic crystals (MPhCs) onto the front surface of the diode. In this work, we study the effect of MPhCs on GaSb TPV diodes. Simulations are presented which characterize a specific MPhC design for use with GaSb. E-field intensity vs. wavelength and depth are investigated as well as the effect of the thickness of the PhC on the interaction time between the e-field and semiconductor. It is shown that the thickness of MPhC has little effect on width of the enhancement band, and the depth the ideal p-i-n junction is between 0.6m and 2.1um. Additionally, simulated results demonstrate an increase of E-field/semiconductor interaction time of approximately 40% and 46% for a MPhC thickness of 350nm and 450nm respectively.
more »
« less
Thermoradiative energy conversion in infrared interband cascade InAs/GaSb/AlInSb/GaSb type-II superlattice diodes
Thermoradiative energy conversion presents a means for the direct conversion of thermal energy through radiative transfer to a cold scene. However, much of the study of thermoradiative principles has been based on theory and simulations, with only sparse reports on the experimental demonstration of the concept. This work studies thermoradiative energy conversion in InAs/GaSb/AlInSb/GaSb type-II superlattice cascade devices. The devices exhibit a cutoff wavelength of 3.2 μm at 300 K, corresponding to a bandgap of 0.39 eV. Testing under a temperature-controlled chamber and scene demonstrates a maximum power density of 2.9 mW/m2 at a cell temperature of 121 °C. It is consistent with expected values for device operation limited by Shockley–Read–Hall non-radiative recombination. This result is a significant step in providing an experimental demonstration of thermoradiative energy conversion and a means to characterize cell performance, providing a foundation for further development to achieve practical values for power generation.
more »
« less
- Award ID(s):
- 2317609
- PAR ID:
- 10581689
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- APL Energy
- Volume:
- 3
- Issue:
- 2
- ISSN:
- 2770-9000
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The suppression of leakage current via surface passivation plays a critical role for GaSb‐based optoelectronic devices. In this Letter the authors carefully optimise the sulfur passivation parameters for improving the performance of GaSb p–i–n devices. Two competing processes are evaluated during the sulfur passivation process: the hydrolysis of HS–ions that aide surface passivation and the re‐oxidation, respectively. Upon the optimisation of sulfur passivation parameters and subsequent encapsulation with atomic layer deposition Al2O3, the surface resistivity significantly increased from 4.3 kΩ.cm to 28.6 kΩ.cm, leading to a 19.1 times drop in dark current at room temperature for the GaSb p–i–n structure. This Letter provides a repeatable and stable passivation approach for improving the optoelectronic performance of GaSb‐based devices.more » « less
-
Stable high-power narrow-linewidth operation of the 2.05–2.1 µm GaSb-based diode lasers was achieved by utilizing the sixth-order surface-etched distributed Bragg reflector (DBR) mirrors. The DBR multimode devices with 100 µm wide ridge waveguides generated in the continuous wave (CW) regime at 20°C. The device CW output power was limited by thermal rollover. The laser emission spectrum was defined by Bragg reflector reflectivity at all operating currents in a wide temperature range. The devices operated at DBR line with detuning from gain peak exceeding 10 meV.more » « less
-
Abstract III–V semiconductor nanocrystals are an important class of optoelectronic materials. However, the gas‐phase synthesis of these materials, especially of the stibnides, has been left relatively unexplored. In this study, we demonstrate the synthesis of free‐standing GaSb nanocrystals for the first time, using a novel gas‐phase process. We show that when elemental aerosols are used as precursors for Ga and Sb, the elements mix at the nanometer length scale as the aerosols pass through a nonequilibrium plasma reactor. At sufficiently high plasma power, the mixing produces free‐standing GaSb nanocrystals, with a small amount of excess Ga segregated at the periphery of the particles. The reaction is initiated by vaporization of elemental aerosols in the plasma despite the low‐background temperature. Ion bombardment determines the extent of vaporization of Ga and Sb and thereby controls the ensemble stoichiometry and reaction rates.more » « less
-
Abstract In this paper, we report, for the first time, a theoretical study on passive photonic devices including optical power splitters/combiners and grating couplers (GCs) operating at non-telecom wavelengths above 2 µ m in a monolithic GaSb platform. Passive components were designed to operate, in particular, at around 2.6 µ m for monolithic integration with active photonic devices on the III–V gallium antimonide material platform. The three popular types of splitters/combiners such as directional couplers, multimode interferometer-, and Y-branch-couplers were theoretically investigated. Based on our optimized design and rigorous analysis, fabrication-compatible 1 × 2 optical power splitters with less than 0.12 dB excess losses, large spectral bandwidth, and a 50:50 splitting ratio are achieved. For fiber-to-chip coupling, we also report the design of GCs with an outcoupling efficiency of ∼29% at 2.56 μ m and a 3 dB bandwidth of 80 nm. The results represent a significant step towards developing a complete functional photonic integrated circuits at mid-wave infrared wavelengths.more » « less