Rutile compounds have exotic functional properties that can be applied for various electronic applications; however, the limited availability of epitaxial substrates has restricted the study of rutile thin films to a limited range of lattice parameters. Here, rutile GeO 2 is demonstrated as a new rutile substrate with lattice parameters of [Formula: see text] and [Formula: see text]. Rutile GeO 2 single crystals up to 4 mm in size are grown by the flux method. X-ray diffraction reveals high crystallinity with a rocking curve having a full width half-maximum of 0.0572°. After mechanical polishing, a surface roughness of less than 0.1 nm was obtained, and reflection high-energy electron diffraction shows a crystalline surface. Finally, epitaxial growth of (110)-oriented TiO 2 thin films on GeO 2 substrates was demonstrated using molecular beam epitaxy. Templated by rutile GeO 2 substrates, our findings open the possibility of stabilizing new rutile thin films and strain states for the tuning of physical properties.
more »
« less
Atomically smooth films of CsSb: A chemically robust visible light photocathode
Alkali antimonide semiconductor photocathodes provide a promising platform for the generation of high-brightness electron beams, which are necessary for the development of cutting-edge probes, including x-ray free electron lasers and ultrafast electron diffraction. Nonetheless, to harness the intrinsic brightness limits in these compounds, extrinsic degrading factors, including surface roughness and contamination, must be overcome. By exploring the growth of CsxSb thin films monitored by in situ electron diffraction, the conditions to reproducibly synthesize atomically smooth films of CsSb on 3C–SiC (100) and graphene-coated TiO2 (110) substrates are identified, and detailed structural, morphological, and electronic characterization is presented. These films combine high quantum efficiency in the visible (up to 1.2% at 400 nm), an easily accessible photoemission threshold of 566 nm, low surface roughness (down to 600 pm on a 1 μm scale), and a robustness against oxidation up to 15 times greater than Cs3Sb. These properties lead us to suggest that CsSb has the potential to operate as an alternative to Cs3Sb in electron source applications where the demands of the vacuum environment might otherwise preclude the use of traditional alkali antimonides.
more »
« less
- PAR ID:
- 10595123
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- APL Materials
- Volume:
- 11
- Issue:
- 10
- ISSN:
- 2166-532X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
We report the use of suboxide molecular-beam epitaxy (S-MBE) to grow α-(AlxGa1−x)2O3 films on (110) sapphire substrates over the 0 < x < 0.95 range of aluminum content. In S-MBE, 99.98% of the gallium-containing molecular beam arrives at the substrate in a preoxidized form as gallium suboxide (Ga2O). This bypasses the rate-limiting step of conventional MBE for the growth of gallium oxide (Ga2O3) from a gallium molecular beam and allows us to grow fully epitaxial α-(AlxGa1−x)2O3 films at growth rates exceeding 1 µm/h and relatively low substrate temperature (Tsub = 605 ± 15 °C). The ability to grow α-(AlxGa1−x)2O3 over the nominally full composition range is confirmed by Vegard’s law applied to the x-ray diffraction data and by optical bandgap measurements with ultraviolet–visible spectroscopy. We show that S-MBE allows straightforward composition control and bandgap selection for α-(AlxGa1−x)2O3 films as the aluminum incorporation x in the film is linear with the relative flux ratio of aluminum to Ga2O. The films are characterized by atomic-force microscopy, x-ray diffraction, and scanning transmission electron microscopy (STEM). These α-(AlxGa1−x)2O3 films grown by S-MBE at record growth rates exhibit a rocking curve full width at half maximum of ≊ 12 arc secs, rms roughness <1 nm, and are fully commensurate for x ≥ 0.5 for 20–50 nm thick films. STEM imaging of the x = 0.78 sample reveals high structural quality and uniform composition. Despite the high structural quality of the films, our attempts at doping with silicon result in highly insulating films.more » « less
-
We demonstrate a-axis YBa2Cu3O7−x/PrBa2Cu3O7−x/YBa2Cu3O7−x trilayers grown on (100) LaAlO3 substrates with improved interface smoothness. The trilayers are synthesized by ozone-assisted molecular-beam epitaxy. The thickness of the PrBa2Cu3O7−x layer is held constant at 8 nm, and the thickness of the YBa2Cu3O7−x layers is varied from 24 nm to 100 nm. X-ray diffraction measurements show all trilayers to have >97% a-axis content. The rms roughness of the thinnest trilayer is <0.7 nm, and this roughness increases with the thickness of the YBa2Cu3O7−x layers. The thickness of the YBa2Cu3O7−x layers also affects the transport properties: while all samples exhibit an onset of the superconducting transition at and above 85 K, the thinner samples show wider transition widths, ΔTc. High-resolution scanning transmission electron microscopy reveals coherent and chemically sharp interfaces and that growth begins with a cubic (Y,Ba)CuO3−x perovskite phase that transforms into a-axis oriented YBa2Cu3O7−x as the substrate temperature is ramped up.more » « less
-
N-polar AlGaN is an emerging wide-bandgap semiconductor for next-generation high electron mobility transistors and ultraviolet light emitting diodes and lasers. Here, we demonstrate the growth and characterization of high-quality N-polar AlGaN films on C-face 4H-silicon carbide (SiC) substrates by molecular beam epitaxy. On optimization of the growth conditions, N-polar AlGaN films exhibit a crack free, atomically smooth surface (rms roughness ∼ 0.9 nm), and high crystal quality with low density of defects and dislocations. The N-polar crystallographic orientation of the epitaxially grown AlGaN film is unambiguously confirmed by wet chemical etching. We demonstrate precise compositional tunability of the N-polar AlGaN films over a wide range of Al content and a high internal quantum efficiency ∼74% for the 65% Al content AlGaN film at room temperature. Furthermore, controllable silicon (Si) doping in high Al content (65%) N-polar AlGaN films has been demonstrated with the highest mobility value ∼65 cm2/V-s observed corresponding to an electron concentration of 1.1 × 1017 cm−3, whereas a relatively high mobility value of 18 cm2/V-s is sustained for an electron concentration of 3.2 × 1019 cm−3, with an exceptionally low resistivity value of 0.009 Ω·cm. The polarity-controlled epitaxy of AlGaN on SiC presents a viable approach for achieving high-quality N-polar III-nitride semiconductors that can be harnessed for a wide range of emerging electronic and optoelectronic device applications.more » « less
-
In situ transport measurements on epitaxial 7.6-nm-thick Co(0001)/Al2O3(0001) films with and without Ti and TiN capping layers during O2 exposure are used to investigate the effects of surface chemistry on electron scattering at Co(0001) surfaces. The Co sheet resistance Rs increases with increasing thickness dTi and dTiN of the Ti and TiN capping layers, saturating at 8% and 31% above the uncoated Co(0001) for dTi > 0.2 nm and dTiN > 0.1 nm, respectively. This increase is attributed to electron scattering into local surface states, which is less pronounced for Ti than TiN. In situ resistance measurements taken during a continuously increasing O2 partial pressure from 0 Pa to 40 Pa indicate a relatively steep 24% increase in Rs at an exposure of ∼50 Pa s, which can be attributed to Co surface oxidation that leads to atomic level roughness and a decrease in the electron scattering specularity p. Ti and TiN cap layers with dTi ≥ 0.5 nm and dTiN ≥ 0.13 nm exhibit no resistance change upon air exposure, indicating suppression of Co oxidation. These results indicate a promising Co–Ti interface with an electron scattering specularity of p = 0.4–0.5, which is retained during oxygen exposure, while, in contrast, electron scattering at the Co–TiN interface is completely diffuse (p = 0), suggesting that Ti barrier layers facilitate higher-conductivity Co interconnects than TiN barriers, as long as the Ti layer is sufficiently thick (dTi ≥ 0.5 nm) to suppress Co oxidation.more » « less