We report on a novel TaNbZrHfTi-based high entropy alloy (HEA) which demonstrates distinctive dual-phase superconductivity. The HEA was synthesized under high pressures and high temperatures starting from a ball milled mixture of elemental metals in a large-volume Paris–Edinburgh cell with P ≈ 6 GPa and T = 2300 K. The synthesized HEA is a phase mixture of BCC (NbTa)0.45(ZrHfTi)0.55 with Tc1 = 6 K and FCC (NbTa)0.04(ZrHfTi)0.96 with Tc2 = 3.75 K. The measured magnetic field parameters for the HEA are lower critical field, Hc1(0) = 31 mT, and a relatively high upper critical field, Hc2(0) = 4.92 T. This dual-phase system is further characterized by the presence of a second magnetization peak, or the fishtail effect, observed in the virgin magnetization curves. This phenomenon, which does not distort the field-dependent magnetization hysteresis loops, suggests intricate pinning mechanisms that could be potentially tuned for optimized performance. The manifestation of these unique features in HEA superconductivity reinforces phase-dependent superconductivity and opens new avenues in the exploration of novel superconducting materials.
more »
« less
Superconductivity and phase stability of a high-entropy (NbTa)0.55(HfTiZr)0.45 alloy under high pressures
High-entropy alloys (HEAs) are a class of multi-element materials that exhibit unique structural and functional properties. This study reports on the synthesis and characterization of a superconducting HEA, (NbTa)0.55(HfTiZr)0.45 fabricated using the vacuum arc melting technique. Scanning electron microscopy and energy-dispersive x-ray spectroscopy were employed to analyze the material's morphology and composition. X-ray diffraction analysis revealed a single-phase body-centered cubic (BCC) structure with a measured nanoindentation hardness of 6.4 GPa and Young's modulus of 132 GPa. This HEA superconductor was investigated by x-ray diffraction at Beamline 13BM-C, Advanced Photon Source, and the BCC phase was stable to the highest pressure of 50 GPa. Superconductivity was characterized by four-probe resistivity measurements in a quantum design physical property measurement system, yielding a superconducting transition temperature (Tc) of 7.2 K at ambient pressure and reaching a maximum of 10.1 K at the highest applied pressure of 23.6 GPa. The combination of high structural stability enhanced superconducting performance under pressure and superior mechanical properties highlights (NbTa)0.55(HfTiZr)0.45 as a promising superconductor under extreme environments.
more »
« less
- PAR ID:
- 10596706
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- Journal of Applied Physics
- Volume:
- 137
- Issue:
- 21
- ISSN:
- 0021-8979
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
At ambient conditions, the high-entropy alloy superconductor Re0.6(NbTiZrHf)0.4 exhibits exceptional mechanical properties among high-entropy alloys, with its hexagonal phase achieving nanoindentation hardness of 18.5 GPa. We report on a unique pressure-induced structural transformation from a hexagonal phase to a body-centered cubic (BCC) phase, revealed by synchrotron x-ray diffraction measurements up to 70 GPa. This first-order transition, accompanied by a 6.1% volume collapse, occurs at 44 GPa and results in a BCC structure with random site occupancy by the five constituent elements, which is remarkably retained upon decompression to ambient conditions. The transformation proceeds via a martensiticlike, diffusionless mechanism without elemental segregation, enabled by pressure-induced electronic redistribution and atomic-scale disorder. These findings demonstrate a rare case of metastable phase retention in a chemically complex alloy and offer new insights into structure-stability relationships under pressure.more » « less
-
null (Ed.)X-ray diffraction indicates that the structure of the recently discovered carbonaceous sulfur hydride (C-S-H) room temperature superconductor is derived from previously established van der Waals compounds found in the H2S-H2 and CH4-H2 systems. Crystals of the superconducting phase were produced by a photochemical synthesis technique leading to the superconducting critical temperature Tc of 288 K at 267 GPa. X-ray diffraction patterns measured from 124 to 178 GPa, within the pressure range of the superconducting phase, are consistent with an orthorhombic structure derived from the Al2Cu-type determined for (H2S)2H2 and (CH4)2H2 that differs from those predicted and observed for the S-H system to these pressures. The formation and stability of the C-S-H compound can be understood in terms of the close similarity in effective volumes of the H2S and CH4 components, and denser carbon-bearing S-H phases may form at higher pressures. The results are crucial for understanding the very high superconducting Tc found in the C-S-H system at megabar pressures.more » « less
-
Abstract High-pressure electrical resistivity measurements reveal that the mechanical deformation of ultra-hard WB 2 during compression induces superconductivity above 50 GPa with a maximum superconducting critical temperature, T c of 17 K at 91 GPa. Upon further compression up to 187 GPa, the T c gradually decreases. Theoretical calculations show that electron-phonon mediated superconductivity originates from the formation of metastable stacking faults and twin boundaries that exhibit a local structure resembling MgB 2 (hP3, space group 191, prototype AlB 2 ). Synchrotron x-ray diffraction measurements up to 145 GPa show that the ambient pressure hP12 structure (space group 194, prototype WB 2 ) continues to persist to this pressure, consistent with the formation of the planar defects above 50 GPa. The abrupt appearance of superconductivity under pressure does not coincide with a structural transition but instead with the formation and percolation of mechanically-induced stacking faults and twin boundaries. The results identify an alternate route for designing superconducting materials.more » « less
-
In this study, phase transitions (structural and magnetic) and associated magnetocaloric properties of stoichiometric MnCoGe have been investigated as a function of annealing pressure. Metastable phases were generated by annealing at 800 °C followed by rapid cooling under pressures up to 6.0 GPa. The x-ray diffraction results reveal that the crystal cell volume of the metastable phases continuously decreases with increasing thermal processing pressure, leading to a decrease in the structural transition temperature. The magnetic and structural transitions merge and form a first-order magnetostructural transition between the ferromagnetic orthorhombic and paramagnetic hexagonal phases over a broad temperature range (>80 K) spanning room temperature, yielding considerable magnetic entropy changes. These findings demonstrate the utility of thermal processing under high pressure, i.e., high-pressure annealing, to control the magnetostructural transitions and associated magnetocaloric properties of MnCoGe without altering its chemical composition.more » « less