Title: Hysteresis parameters and magnetic anisotropy of silicate-hosted magnetite exsolutions
SUMMARY Anisotropy of remanent magnetization and magnetic susceptibility are highly sensitive and important indicators of geological processes which are largely controlled by mineralogical parameters of the ferrimagnetic fraction in rocks. To provide new physical insight into the complex interaction between magnetization structure, shape, and crystallographic relations, we here analyse ‘slice-and-view’ focused-ion-beam (FIB) nano-tomography data with micromagnetic modelling and single crystal hysteresis measurements. The data sets consist of 68 magnetite inclusions in orthopyroxene (Mg60) and 234 magnetite inclusions in plagioclase (An63) were obtained on mineral separates from the Rustenburg Layered Suite of the Bushveld Intrusive Complex, South Africa. Electron backscatter diffraction was used to determine the orientation of the magnetite inclusions relative to the crystallographic directions of their silicate hosts. Hysteresis loops were calculated using the finite-element micromagnetics code MERRILL for each particle in 20 equidistributed field directions and compared with corresponding hysteresis loops measured using a vibrating sample magnetometer (VSM) on silicate mineral separates from the same samples. In plagioclase the ratio of remanent magnetization to saturation magnetization (Mrs/Ms) for both model and measurement agree within 1.0 per cent, whereas the coercivity (Hc) of the average modelled curve is 20 mT lower than the measured value of 60 mT indicating the presence of additional sources of high coercivity in the bulk sample. The VSM hysteresis measurements of the orthopyroxene were dominated by multidomain (MD) magnetite, whereas the FIB location was chosen to avoid MD particles and thus contains only particles with diameters <500 nm that are considered to be the most important carriers of palaeomagnetic remanence. To correct for this sampling bias, measured MD hysteresis loops from synthetic and natural magnetites were combined with the average hysteresis loop from the MERRILL models of the FIB region. The result shows that while the modelled small-particle fraction only explains 6 per cent of the best fit to the measured VSM hysteresis loop, it contributes 28 per cent of the remanent magnetization. The modelled direction of maximal Mrs/Ms in plagioclase is subparallel to [001]plag, whereas Hc does not show a strong orientation dependence. The easy axis of magnetic remanence is in the direction of the magnetite population normal to (150)plag and the maximum calculated susceptibility (χ*) is parallel to [010]plag. For orthopyroxene, the maximum Mrs/Ms, maximum χ* and the easy axis of remanence is strongly correlated to the elongation axes of magnetite in the [001]opx direction. The maximum Hc is oriented along [100]opx and parallel to the minimum χ*, which reflects larger vortex nucleation fields when the applied field direction approaches the short axis. The maximum Hc is therefore orthogonal to the maximum Mrs/Ms, controlled by axis-aligned metastable single-domain states at zero field. The results emphasize that the nature of anisotropy in natural magnetite does not just depend on the particle orientations, but on the presence of different stable and metastable domain states, and the mechanism of magnetic switching between them. Magnetic modelling of natural magnetic particles is therefore a vital method to extract and process anisotropic hysteresis parameters directly from the primary remanence carriers.  more » « less
Award ID(s):
1642268
NSF-PAR ID:
10318873
Author(s) / Creator(s):
; ; ; ; ; ;
Date Published:
Journal Name:
Geophysical Journal International
Volume:
229
Issue:
3
ISSN:
0956-540X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. SUMMARY

    Quaternary lavas of the Stardalur Caldera, 20 km northeast of Reykjavik, Iceland, create a 27 300 nT magnetic anomaly visible in both ground and aeromagnetic surveys. Here, we provide a comprehensive mineralogical and rock magnetic data set to analyse NRM intensities and Koenigsberger ratios of 57 drill-core samples from the critical zone (CZ) of the anomaly high at depths between 41 and 131 m. This extends previous studies and verifies that the anomaly is due to an unusually high intensity of remanent magnetization carried by magnetite. The NRM of the CZ samples was acquired during the Olduvai subchron in a field of at most today’s strength. NRM intensities range from 20 to 128 A m–1 with a median of 55 A m–1, and an average of 61 A m–1, respectively, approximately 13–15 times higher than in typical Icelandic basalts (AIB) with an NRM intensity of 4 A m–1. Our new data set shows that the magnetite concentration throughout the CZ basalts is at most twofold higher than in AIB lavas. New data on domain state and TRM efficiency prove that these properties account for an additional factor of at most 2.3. Because magnetite is the most abundant remanence carrier in rocks on Earth, and its remanence acquisition is considered to be extremely well understood, we assert that the remaining discrepancy is a critical enigma in rock magnetism. Results from scanning electron microscopy show that a significant fraction of all CZ magnetite particles have dendritic shapes with grain sizes <1 μm, indicating rapid crystallization. Most large magnetite grains are heavily subdivided by very fine oxidation-exsolution lamellae of ilmenite, and subordinate amount of exsolved spinel as needles, blebs and blades. These common microstructures found throughout the CZ subdivide the initially homogeneous mineral into separate cubicles, here denoted as compartments. The magnetite compartments then have sizes below 1 μm. Hysteresis data, Preisach maps and FORC data consistently confirm that the coercivity distribution is dominated by values above 10 mT, such that multidomain behaviour is of little relevance in the CZ. Between 5 and 20 per cent of the IRM is carried by coercivities above 100 mT, which for magnetite indicates unusually high anisotropy effects in the individual particles. Based on the quantitative analysis of all magnetic contributions to the NRM, we can demonstrate that the average efficiency of NRM acquisition in the CZ Stardalur basalts must be at least a factor 3 higher than in typical basalts. We speculate that this is related to the observed focused compartment size distribution <1 μm, and indicates thermochemical remanence acquisition below the Curie temperature of magnetite. Yet, a detailed physical mechanism for the extreme overefficiency of NRM acquisition remains enigmatic.

     
    more » « less
  2. Abstract

    Iron mineral transformations occurring in hydrocarbon‐contaminated sites are linked to the biodegradation of the hydrocarbons. At a hydrocarbon‐contaminated site near Bemidji, Minnesota, USA, measurements of magnetic susceptibility (MS) are useful for monitoring the natural attenuation of hydrocarbons related to iron cycling. However, a transient MS, previously observed at the site, remains poorly understood and the iron mineral phases acting as reactants and products associated with this MS perturbation remain largely unknown. To address these unknowns, we acquired mineral magnetism measurements, including hysteresis loops, backfield curves, and isothermal remanent magnetizations on sediment core samples retrieved from the site and magnetite‐filled mineral packets installed within the aquifer. Our data show that the core samples and magnetite packs display decreasing magnetization with time and that this loss in magnetization is accompanied by increasing bulk coercivity consistent with decreased average grain size and/or partial oxidation. Low‐temperature magnetometry on all samples displayed behavior consistent with magnetite, but samples within the plume also show evidence of maghemitization. This interpretation is supported by the occurrence of shrinkage cracks on the surface of the grains imaged via scanning electron microscopy. Magnetite transformation to maghemite typically occurs under oxic conditions, here, we propose that maghemitization occurs within the anoxic portions of the plume via microbially mediated anaerobic oxidation. Mineral dissolution also occurs within the plume. Microorganisms capable of such anaerobic oxidation have been identified within other areas at the Bemidji site, but additional microbiological studies are needed to link specific anaerobic iron oxidizers with this loss of magnetization.

     
    more » « less
  3. SUMMARY The magnetic properties of iron-bearing minerals at above-ambient temperatures control their magnetic expression at depth in the Earth and other planets, as well as the permanent memory they retain as thermoremanence or thermochemical remanence when brought to the surface and cooled. This paper reports magnetic hysteresis parameters measured at temperatures up to the Curie point TC for natural pyrrhotite and hematite and for suites of sized magnetites, both natural and synthesized. Domain structure changes can be inferred from the ratio of saturation remanence Mrs to saturation magnetization Ms. In almost all magnetites and pyrrhotites studied, Mrs decreases more rapidly with increasing measurement temperature T than Ms, indicating thermal unblocking or vortex development in single-domain grains and addition or remobilization of domain walls at high T in multidomain grains. During cooling of a rock, iron minerals might then denucleate domains or vortices. Coercive force Hc, a measure of stability against changing magnetic fields, also decreases with increasing measurement T, usually at a rate similar to that of Mrs, but often retains a finite value near the Curie point. 
    more » « less
  4. Abstract

    Gyro‐remanent magnetization (GRM) is a frequently occurring yet unwanted remanence contamination for certain samples during alternating field (AF) demagnetization of the natural remanent magnetization. The origin and detailed properties of GRM have not yet been fully understood. In this study, systematic rock magnetic analyses were conducted on marine greigite‐bearing samples of Hole U1433A drilled by the IODP Expedition 349 from the South China Sea. Results show that GRM is mostly acquired above ~55 mT AF demagnetization and can be effectively removed by heating to ~400°C during thermal demagnetization but a secondary tail could remain until ~585°C. In addition, no apparent GRM was observed during the AF demagnetization for the 400°C thermally treated samples. These results strongly suggest that GRM is dominantly carried by single domain (SD) greigite but with minor contributions from SD magnetite. Thus, thermal treatment alone or the hybrid demagnetization (i.e., thermal demagnetization at ~400°C first then systematical AF demagnetization) can efficiently avoid the GRM acquisition and be beneficial for relative paleointensity estimation for greigite‐bearing samples. Besides, GRM carried by greigite has a low thermal stability. Our results also show AF demagnetization spectra of anhysteretic remanent magnetization (ARM) could be strongly distorted by GRM effects due to both have a preference of SD particles. Thus, the median destructive field of ARM is improper to be used as a coercivity proxy for greigite‐bearing samples. Instead, the biplot analysis of AF demagnetization of natural remanent magnetization and ARM can be used to evaluate the relative content of greigite.

     
    more » « less
  5. The influence of oleylamine (OLA) concentration on the crystallography, morphology, surface chemistry, chemical bonding, and magnetic properties of solvothermal synthesized CoFe2O4 (CFO) nanoparticles (NPs) has been thoroughly investigated. Varying OLA concentration (0.01–0.1 M) resulted in the formation of cubic spinel-structured CoFe2O4 NPs in the size-range of 20–14 (±1) nm. The Fourier transform spectroscopic analyses performed confirmed the OLA binding to the CFO NPs. The thermogravimetric measurements revealed monolayer and multilayer coating of OLA on CFO NPs, which were further supported by the small-angle X-ray scattering measurements. The magnetic measurements indicated that the maximum saturation (MS) and remanent (Mr) magnetization decreased with increasing OLA concentration. The ratio of maximum dipolar field (Hdip), coercivity (HC), and exchanged bias field (Hex) (at 10 K) to the average crystallite size (Dxrd), i.e., (Hdip/Dxrd), (HC/Dxrd), and (Hex/Dxrd), increased linearly with OLA concentration, indicating that OLA concurrently controls the particle size and interparticle interaction among the CFO NPs. The results and analyses demonstrate that the OLA-mediated synthesis allowed for modification of the structural and magnetic properties of CFO NPs, which could readily find potential application in electronics and biomedicine. 
    more » « less