Photodetectors operating across the near‐ to short‐wave infrared (NIR–SWIR,
- NSF-PAR ID:
- 10491418
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
Broadband photodetectors (PDs) have great applications in both industrial and scientific sectors. In this study, solution-processed broadband PDs with an “inverted” vertical photodiode device structure without incorporating transparent conductive oxides electrodes, fabricated by bulk heterojunction (BHJ) composites composed of a low optical gap conjugated polymer blended with highly electrically conductive PbS quantum dots (QDs), operated at room temperature, are reported. The low optical gap conjugated polymer incorporated with PbS QDs contributes to the spectral response from the ultraviolet (UV)-visible to the infrared (IR) range. To realize the IR spectral response and to circumvent the weak IR transparency of the transparent oxide electrodes, the implementation of a photodiode with an “inverted” vertical device structure with the Au anode and the Ba/Al bilayer semitransparent cathode passivated with the MgF 2 layer is demonstrated. Photoinduced charge carrier transfer occurring within the BHJ composite gave rise to decent photocurrent, resulting in detectivities greater than 10 12 Jones (cm Hz 1/2 /W) over the wavelength from the UV-visible to the IR range under low applied bias. Thus, our findings of the utilization of the BHJ composites and an “inverted” vertical photodiode without the incorporation of the transparent conductive oxide electrodes provide a facile way to realize broadband PDs.more » « less
-
Abstract In this work, room‐temperature‐operated ultrasensitive solution‐processed perovskite photodetectors (PDs) with near infrared (NIR) photoresponse are reported. In order to enable perovskite PDs possessing extended NIR photoresponse, novel n‐type low bandgap conjugated polymer, poly[(
N,N ′‐bis(2‐octyldodecyl)‐1,4,5,8‐naphthalene diimide‐2,6‐diyl) (2,5‐dioctyl‐3,6‐di(thiophen‐2‐yl)pyrrolo[3,4‐c ]pyrrole‐1,4‐dione‐5,5′‐diyl)] (NDI‐DPP), which has strong absorption in the NIR region, is developed and then employed in perovskite PDs. By the formation of type II band alignment between NDI‐DPP with single‐wall carbon nanotubes (SWCNTs), the NIR absorption of NDI‐DPP is exploited, which contributes to the NIR photoresponse for the perovskite PDs, where perovskite is incorporated with NDI‐DPP and SWCNTs as well. In addition, SWCNTs incorporated with perovskite active layer can offer the percolation pathways for high charge‐carrier mobility, which tremendously boosts the charge transfer in the photoactive layer, and consequently improves the photocurrent in the visible region. As a result, the perovskite PDs exhibit the responsivities of ≈400 and ≈150 mA W−1and the detectivities of over 6 × 1012Jones (1 Jones = 1 cm Hz1/2W−1) and over 2 × 1012Jones in the visible and NIR regions, respectively. This work reports the development of perovskite PDs with NIR photoresponse, which is terrifically beneficial for the practical applications of perovskite PDs. -
Abstract While only few organic photodiodes have photoresponse past 1 µm, novel shortwave infrared (SWIR) polymers are emerging, and a better understanding of the limiting factors in narrow bandgap devices is critically needed to predict and advance performance. Based on state‐of‐the‐art SWIR bulk heterojunction photodiodes, this work demonstrates a model that accounts for the increasing electric‐field dependence of photocurrent in narrow bandgap materials. This physical model offers an expedient method to pinpoint the origins of efficiency losses, by decoupling the exciton dissociation efficiency and charge collection efficiency in photocurrent–voltage measurements. These results from transient photoconductivity measurements indicate that the main loss is due to poor exciton dissociation, particularly significant in photodiodes with low‐energy charge‐transfer states. Direct measurements of the noise components are analyzed to caution against using assumptions that could lead to an overestimation of detectivity. The devices show a peak detectivity of 5 × 1010Jones with a spectral range up to 1.55 µm. The photodiodes are demonstrated to quantify the ethanol–water content in a mixture within 1% accuracy, conveying the potential of organics to enable economical, scalable detectors for SWIR spectroscopy.
-
Abstract It is a great challenge to obtain broadband response perovskite photodetectors (PPDs) due to the relatively large bandgaps of the most used methylammonium lead halide perovskites. The response range of the reported PPDs is limited in the ultraviolet–visible range. Here, highly sensitive PPDs are successfully fabricated with low bandgap (≈1.25 eV) (FASnI3)0.6(MAPbI3)0.4perovskite as active layers, exhibiting a broadband response from 300 to 1000 nm. The performance of the PPDs can be optimized by adjusting the thicknesses of the perovskite and C60layers. The optimized PPDs with 1000 nm thick perovskite layer and 70 nm thick C60layer exhibit an almost flat external quantum efficiency (EQE) spectrum from 350 to 900 nm with EQE larger than 65% under −0.2 V bias. Meanwhile, the optimized PPDs also exhibit suppressed dark current of 3.9 nA, high responsivity (
R ) of over 0.4 A W−1, high specific detectivity (D* ) of over 1012Jones in the near‐infrared region under −0.2 V. Such highly sensitive broadband response PPDs, which can work well as self‐powered conditions, offer great potential applications in multicolor light detection. -
Abstract Pyroelectric detectors are often broadband and require external filters for wavelength‐specific applications. This paper reports a tunable, narrowband, and lightweight pyroelectric infrared detector built upon a flexible membrane of As2S3−Ag−P(VDF‐TrFE) with subwavelength grating, which is capable of both on‐chip filtering and photopyroelectric energy conversion. The top surface of this hybrid membrane is a corrugated As2S3−Ag film contributing to narrowband light absorption in the near‐infrared (NIR) regime, and the bottom part is a polyvinylidene fluoride‐trifluoroethylene (PVDF‐TrFE) membrane for the conversion of the absorbed light to an electrical signal. Uniquely, applying a bias voltage to the PVDF‐TrFE membrane enables the tuning of the device's absorption and pyroelectric characteristics owing to the piezoelectrically induced mechanical bending. The resonator exhibited a resonant absorption coefficient of 80% and a full‐width‐half‐maximum of 15 nm within the NIR, a responsivity of 1.4 mV mW−1, and an equivalent noise power of 13 µW Hz−1/2at 1560 nm. By applying a 15‐V bias to the PVDF‐TrFE membrane, the absorption coefficient decreased to 18% due to the change in the grating period and incident angle. The narrowband and tunable features of the As2S3−Ag−P(VDF‐TrFE) pyroelectric detector will benefit a variety of potential applications in sensors, optical spectroscopy, and imaging.