Abstract Some textured silicone breast implants with high average surface roughness (‘macrotextured’) have been associated with a rare cancer of the immune system, Breast Implant-Associated Anaplastic Large Cell Lymphoma (BIA-ALCL). Silicone elastomer wear debris may lead to chronic inflammation, a key step in the development of this cancer. Here, we model the generation and release of silicone wear debris in the case of a folded implant-implant (‘shell-shell’) sliding interface for three different types of implants, characterized by their surface roughness. The ‘smooth’ implant shell with the lowest average surface roughness tested (R a = 2.7 ± 0.6 μ m) resulted in average friction coefficients of μ avg = 0.46 ± 0.11 across 1,000 mm of sliding distance and generated 1,304 particles with an average particle diameter of D avg = 8.3 ± 13.1 μ m. The ‘microtextured’ implant shell (R a = 32 ± 7.0 μ m) exhibited μ avg = 1.20 ± 0.10 and generated 2,730 particles with D avg = 4.7 ± 9.1 μ m. The ‘macrotextured’ implant shell (R a = 80 ± 10 μ m) exhibited the highest friction coefficients, μ avg = 2.82 ± 0.15 and the greatest number of wear debris particles, 11,699, with an average particle size of D avg = 5.3 ± 3.3 μ m. Our data may provide guidance for the design of silicone breast implants with lower surface roughness, lower friction, and smaller quantities of wear debris.
more »
« less
Pro-Inflammatory Response to Macrotextured Silicone Implant Wear Debris
Abstract Macrotextured silicone breast implants are associated with several complications, ranging from seromas and hematomas to the formation of a rare type of lymphoma, known as breast implant-associated anaplastic large cell lymphoma (BIA-ALCL). The presence of silicone wear debris has been detected within the peri-implant region and fibrotic capsule and histological analyses reveal inflammatory cells surrounding debris particles. However, it is unclear how these debris particles are generated and released from macrotextured implant surfaces, and whether wear debris generation is related to implant stiffness. In this study, we created an accelerated implant aging model to investigate the formation of silicone wear debris produced from self-mated (“shell-shell”) tribological interactions. We created implant-like silicone elastomers from polydimethylsiloxane (PDMS) using Sylgard 184 base:curing agent (10:1, 12:1, and 16:1) and quantified their mechanical properties (E* = 1141 ± 472, 336 ± 20, and 167 ± 53 kPa, respectively). We created macrotextured PDMS samples using the lost-salt technique and compared their self-mated friction coefficient (< µ > = 4.8 ± 3.2, 4.9 ± 1.8, and 6.0 ± 2.3, respectively) and frictional shear stress (τ = 3.1 ± 1.3, 3.2 ± 1.7, and 2.4 ± 1.4 MPa, respectively) to those of the recalled Allergan Biocell macrotextured implant shell (E* = 299 ± 8 kPa, < µ > = 2.2, andτ = 0.8 ± 0.1). Friction coefficient and frictional shear stress were largely insensitive to variations in elastic modulus for macrotextured PDMS samples and recalled implant shells. The stiffest 10:1 PDMS macrotextured sample and the recalled implant shell both generated similar area fractions of silicone wear debris. However, the recalled implant shell released far more particles (> 10×), mainly within the range of 5 to 20 µm2in area. Bone marrow-derived macrophages (BMDMs) were treated with several concentrations of tribologically generated silicone wear debris. We observed widespread phagocytosis of wear debris particles and increasing secretion of inflammatory cytokines with increasing concentration of wear debris particles. Our investigation highlights the importance of avoiding macrotextured surfaces and mitigating wear debris generation from silicone implants to reduce chronic inflammation.
more »
« less
- Award ID(s):
- 2048043
- PAR ID:
- 10570207
- Publisher / Repository:
- Springer Science + Business Media
- Date Published:
- Journal Name:
- Tribology Letters
- Volume:
- 73
- Issue:
- 1
- ISSN:
- 1023-8883
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Silicone elastomer medical implants are ubiquitous in medicine, particularly for breast augmentation. However, when these devices are placed within the body, disruption of the natural biological interfaces occurs, which significantly changes the native energy-dissipation mechanisms of living systems. These new interfaces can introduce non-physiological contact pressures and tribological conditions that provoke inflammation and soft tissue damage. Despite their significance, the biotribological properties of implant-tissue and implant-extracellular matrix (ECM) interfaces remain poorly understood. Here, we developed an in vitro model of soft tissue damage using a custom-built in situ biotribometer mounted onto a confocal microscope. Sections of commercially-available silicone breast implants with distinct and clinically relevant surface roughness ([Formula: see text]m, [Formula: see text]m, and [Formula: see text]m) were mounted to spherically-capped hydrogel probes and slid against collagen-coated hydrogel surfaces as well as healthy breast epithelial (MCF10A) cell monolayers to model implant-ECM and implant-tissue interfaces. In contrast to the “smooth” silicone implants ([Formula: see text]m), we demonstrate that the “microtextured” silicone implant ([Formula: see text]m) induced higher frictional shear stress ([Formula: see text] Pa), which led to greater collagen removal and cell rupture/delamination. Our studies may provide insights into post-implantation tribological interactions between silicone breast implants and soft tissues.more » « less
-
ABSTRACT There is growing evidence that minimizing the mechanical mismatch between neural implants and brain tissue mitigates inflammatory, biological responses at the interface under long-term implant conditions. The goal of this study is to develop a brain-like soft, conductive neural interface and use an improvised, penetrating microindentation technique reported by us earlier to quantitatively assess the (a) elastic modulus of the neural interface after implantation, (b) mechanical stresses during penetration of the probe, and (c) periodic stresses at steady-state due to tissue micromotion around the probe. We fabricated poly- dimethylsiloxane (PDMS) matrices with multi-walled carbon nanotubes (MWCNTs) using two distinct but carefully calibrated cross-linking ratios, resulting in hard (elastic modulus∼484 kPa) or soft, brain-like (elastic modulus∼5.7 kPa) matrices, the latter being at least 2 orders of magnitude softer than soft neural interfaces reported so far. Subsequent loading of the hard and soft silicone based matrices with (100% w/w) low-molecular weight PDMS siloxanes resulted in further decrease in the elastic modulus of both matrices. Carbon probes with soft PDMS coating show significantly less maximum axial forces (-587 ± 51.5 µN) imposed on the brain than hard PDMS coated probes (-1,253 ± 252 µN) during and after insertion. Steady-state, physiological micromotion related stresses were also significantly less for soft- PDMS coated probes (55.5 ± 17.4 Pa) compared to hard-PDMS coated probes (141.0 ± 21.7 Pa). The penetrating microindentation technique is valuable to quantitatively assess the mechanical properties of neural interfaces in both acute and chronic conditions.more » « less
-
ABSTRACT Commercial silicone elastomers are commonly used in soft materials research due to their easily tunable mechanical properties. However, conventional polydimethylsiloxane (PDMS) elastomers with moduli below ∼100 kPa contain uncrosslinked free molecules, which play a significant role in their behavior. To utilize these materials, it is important to quantify what role these free molecules play in the mechanical response before and after their removal. We present a simple and inexpensive extraction method that enables the removal of free molecules from a lightly crosslinked sheet of Sylgard 184, a commercially available PDMS elastomer. The materials can contain a majority of free molecules yet maintain a thin and flat geometry without fractures after extraction. Subsequently, we compare the modulus, maximum stretchability, and hysteresis behavior with mixing ratios ranging from 60:1 to 30:1, before and after extraction. We show that the modulus, maximum stretchability, and dissipation increase upon extraction. Moreover, our approach offers a route to prepare crosslinked silicone elastomers with a modulus as low as ∼20 kPa without free molecules from a commercially available kit. © 2020 Wiley Periodicals, Inc. J. Polym. Sci.2020,58, 343–351more » « less
-
We present a comparative study of the tribological properties of Pd-, Pt-, and Zr-based bulk metallic glasses (BMG-Pd, BMG-Pt, and BMG-Zr, respectively) under unlubricated conditions. In particular, micro-tribometry is utilized with a 52,100 steel ball, showing that BMG-Pt exhibits a significantly higher coefficient of friction (COF) (0.58 ± 0.08) when compared with BMG-Pd (0.30 ± 0.02) and BMG-Zr (0.20 ± 0.03). Topographical roughness on and off wear scars is characterized via atomic force microscopy (AFM), with results that do not correlate with the observed frictional behavior. On the other hand, scanning electron microscopy (SEM) is utilized to reveal contrasting wear mechanisms for the three samples: while BMG-Pd and BMG-Zr exhibit predominantly abrasive wear, there is evidence of adhesive wear on BMG-Pt. Consequently, the occurrence of adhesive wear emerges as a potential mechanism behind the observation of relatively high coefficients of friction on BMG-Pt, suggesting stronger interactions with steel when compared with the other BMG samples.more » « less