This study provides a comprehensive analysis of the dominant deep acceptor level in nitrogen-doped beta-phase gallium oxide (β-Ga2O3), elucidating and reconciling the hole emission features observed in deep-level optical spectroscopy (DLOS). The unique behavior of this defect, coupled with its small optical cross section, complicates trap concentration analysis using DLOS, which is essential for defect characterization in β-Ga2O3. A complex feature arises in DLOS results due to simultaneous electron emission to the conduction band and hole emission to the valence band from the same defect state, indicating the formation of two distinct atomic configurations and suggesting metastable defect characteristics. This study discusses the implications of this behavior on DLOS analysis and employs advanced spectroscopy techniques such as double-beam DLOS and optical isothermal measurements to address these complications. The double-beam DLOS method reveals a distinct hole emission process at EV+1.3 eV previously obscured in conventional DLOS. Optical isothermal measurements further characterize this energy level, appearing only in N-doped β-Ga2O3. This enables an estimate of the β-Ga2O3 hole effective mass by analyzing temperature-dependent carrier emission rates. This work highlights the impact of partial trap-filling behavior on DLOS analysis and identifies the presence of hole trapping and emission in β-Ga2O3. Although N-doping is ideal for creating semi-insulating material through the efficient compensation of free electrons, this study also reveals a significant hole emission and migration process within the weak electric fields of the Schottky diode depletion region.
more »
« less
Identification and characterization of deep nitrogen acceptors in β-Ga2O3 using defect spectroscopies
The ability to achieve highly resistive beta-phase gallium oxide (β-Ga2O3) layers and substrates is critical for β-Ga2O3 high voltage and RF devices. To date, the most common approach involves doping with iron (Fe), which generates a moderately deep acceptor-like defect state located at EC-0.8 eV in the β-Ga2O3 bandgap. Recently, there has been growing interest in alternative acceptors, such as magnesium (Mg) and nitrogen (N), due to their predicted deeper energy levels, which could avoid inadvertent charge modulation during device operation. In this work, a systematic study that makes direct correlations between the introduction of N using ion implantation and the observation of a newly observed deep level at EC-2.9 eV detected by deep-level optical spectroscopy (DLOS) is presented. The concentration of this state displayed a monotonic dependence with N concentration over a range of implant conditions, as confirmed by secondary ion mass spectrometry (SIMS). With a near 1:1 match in absolute N and EC-2.9 eV trap concentrations from SIMS and DLOS, respectively, which also matched the measured removal of free electrons from capacitance-voltage studies, this indicates that N contributes a very efficiently incorporated compensating defect. Density functional theory calculations confirm the assignment of this state to be an N (0/−1) acceptor with a configuration of N occupying the oxygen site III [NO(III)]. The near ideal efficiency for this state to compensate free electrons and its location toward the midgap region of the β-Ga2O3 bandgap demonstrates the potential of N doping as a promising approach for producing semi-insulating β-Ga2O3.
more »
« less
- Award ID(s):
- 2231026
- PAR ID:
- 10595143
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- APL Materials
- Volume:
- 11
- Issue:
- 11
- ISSN:
- 2166-532X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Changes induced by irradiation with 1.1 MeV protons in the transport properties and deep trap spectra of thick (>80 μm) undoped κ-Ga2O3 layers grown on sapphire are reported. Prior to irradiation, the films had a donor concentration of ∼1015 cm−3, with the two dominant donors having ionization energies of 0.25 and 0.15 eV, respectively. The main electron traps were located at Ec−0.7 eV. Deep acceptor spectra measured by capacitance-voltage profiling under illumination showed optical ionization thresholds near 2, 2.8, and 3.4 eV. The diffusion length of nonequilibrium charge carriers for ɛ-Ga2O3 was 70 ± 5 nm prior to irradiation. After irradiation with 1.1 MeV protons to a fluence of 1014 cm−2, there was total depletion of mobile charge carriers in the top 4.5 μm of the film, close to the estimated proton range. The carrier removal rate was 10–20 cm−1, a factor of 5–10 lower than in β-Ga2O3, while the concentration of deep acceptors in the lower half of the bandgap and the diffusion length showed no significant change.more » « less
-
In this Letter, the role of background carbon in metalorganic chemical vapor deposition (MOCVD) β-Ga2O3 growth using trimethylgallium (TMGa) as the Ga precursor was investigated. The quantitative C and H incorporations in MOCVD β-Ga2O3 thin films grown at different growth rates and temperatures were measured via quantitative secondary ion mass spectroscopy (SIMS). The SIMS results revealed both [C] and [H] increase as the TMGa molar flow rate/growth rate increases or growth temperature decreases. The intentional Si incorporation in MOCVD β-Ga2O3 thin films decreases as the growth rate increases or the growth temperature decreases. For films grown at relatively fast growth rates (GRs) (TMGa > 58 μmol/min, GR > 2.8 μm/h) or relatively low temperature (<950 °C), the [C] increases faster than that of the [H]. The experimental results from this study demonstrate the previously predicted theory—H can effectively passivate the compensation effect of C in n-type β-Ga2O3. The extracted net doping concentration from quantitative SIMS {[Si]-([C]-[H])} agrees well with the free carrier concentration measured from Hall measurement. The revealing of the role of C compensation in MOCVD β-Ga2O3 and the effect of H incorporation will provide guidance on designing material synthesis for targeted device applications.more » « less
-
The characteristics of sputtered NiO for use in pn heterojunctions with Ga2O3 were investigated as a function of sputtering parameters and postdeposition annealing temperature. The oxygen/ nickel and Ni2O3/NiO ratios, as well as the bandgap and resistivity, increased as a function of O2/Ar gas flow ratio. For example, the bandgap increased from 3.7 to 3.9 eV and the resistivity increased from 0.1 to 2.9 Ω cm for the O2/Ar ratio increasing from 1/30 to 1/3. By sharp contrast, the bandgap and Ni2O3/NiO ratio decreased monotonically with postdeposition annealing temperatures up to 600 °C, but the density of films increased due to a higher fraction of NiO being present. Hydrogen is readily incorporated into NiO during exposure to plasmas, as delineated by secondary ion mass spectrometry measurements on deuterated films. The band alignments of NiO films were type II-staggered gaps with both α- and β-Ga2O3. The breakdown voltage of NiO/β-Ga2O3 heterojunction rectifiers was also a strong function of the O2/Ar flow ratio during deposition, with values of 1350 V for 1/3 and 830 V for 1/30.more » « less
-
p-type Cr2MnO4 with bandgap 3.01 eV was sputter deposited onto (2¯01) and (001) n-type or semi-insulating β-Ga2O3.The heterojunction of p-type CrMnO4 on n-type Ga2O3 is found to be type II, staggered gap, i.e., the band offsets are such that both the conduction and valence band edges of Ga2O3 are lower in energy than those of the Cr2MnO4. This creates a staggered band alignment, which can facilitate the separation of photogenerated electron-hole pairs. The valence band edge of Cr2MnO4 is higher than that of Ga2O3 by 1.82–1.93 eV depending on substrate orientation and doping, which means that holes in Cr2MnO4 would have a lower energy barrier to overcome to move into Ga2O3. Conversely, the conduction band edge of Cr2MnO4 is higher than that of Ga2O3 by 0.13–0.30 eV depending on substrate doping and orientation, which would create a barrier for electrons in Ga2O3 to move into Cr2MnO4. This heterojunction looks highly promising for p-n junction formation for advanced Ga2O3-based power rectifiers.more » « less