Abstract Feedstock powders used in binder jetting additive manufacturing include nanopowder, micropowder, and granulated powder. Two important characteristics of the feedstock powders are flowability and sinterability. This paper aims to compare the flowability and sinterability of different feedstock powders. Three powders were compared: nanopowder (with a particle size of ∼100 nm), micropowder (with a particle size of 70 μm), and granulated powder (with a granule size of ∼70 μm) made from the nanopowder by spray freeze drying. Flowability metrics employed included apparent density (AD), tap density (TD), volumetric flow rate (VFR), mass flow rate (MFR), Hausner ratio (HR), Carr index (CI), and repose angle (RA). Sinterability metrics employed included sintered bulk density (SBD), volumetric shrinkage (VS), and densification ratio (DR). Results show that the granulated powder has a higher flowability than the nanopowder and a higher sinterability than the micropowder. Moreover, different flowability metric values of the granulated powder are close to those of the micropowder, indicating that these two powers have a comparably high flowability. Similarly, different sinterability metric values of the granulated powder are close to those of the nanopowder, indicating that these two powders have a comparably high sinterability.
more »
« less
Binder Jetting Additive Manufacturing: Effect of Particle Size Distribution on Density
Abstract This paper reports a study on the effects of particle size distribution (tuned by mixing different-sized powders) on density of a densely packed powder, powder bed density, and sintered density in binder jetting additive manufacturing. An analytical model was used first to study the mixture packing density. Analytical results showed that multimodal (bimodal or trimodal) mixtures could achieve a higher packing density than their component powders and there existed an optimal mixing fraction to achieve the maximum mixture packing density. Both a lower component particle size ratio (fine to coarse) and a larger component packing density ratio (fine to coarse) led to a larger maximum mixture packing density. A threshold existed for the component packing density ratio, below which the mixing method was not effective for density improvement. Its relationship to the component particle size ratio was calculated and plotted. In addition, the dependence of the optimal mixing fraction and maximum mixture packing density on the component particle size ratio and component packing density ratio was calculated and plotted. These plots can be used as theoretical tools to select parameters for the mixing method. Experimental results of tap density were consistent with the above-mentioned analytical predictions. Also, experimental measurements showed that powders with multimodal particle size distributions achieved a higher tap density, powder bed density, and sintered density in most cases.
more »
« less
- Award ID(s):
- 1762341
- NSF-PAR ID:
- 10228717
- Date Published:
- Journal Name:
- Journal of Manufacturing Science and Engineering
- Volume:
- 143
- Issue:
- 9
- ISSN:
- 1087-1357
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
The objective of this study is to compare three different feedstock powders for the binder jetting process by characterizing their flowability and sinterability. Binder jetting additive manufacturing is a promising technology for fabricating ceramic parts with complex or customized geometries. Granulation is a promising material preparation method due to the potential high sinterability and flowability of the produced powder. However, no study has been made to systematically compare raw and granulated powders in terms of their flowing and sintering behaviors. This paper aims at filling this knowledge gap. Two raw powders (i.e., fine raw powder of 300 nm and coarse raw powder of 70 μm) and one granulated powder from spray freeze drying were compared. Different flowability metrics, including volumetric flow rate, mass flow rate, Hausner ratio, Carr index, and repose angle were measured. Different sinterability metrics, including sintered bulk density, volume shrinkage, and densification ratio were compared for all three powders. Results show that granulated powder achieved comparably high flowability to that of the coarse raw powder and also comparably high sinterability to that of the fine raw powder. Moreover, suitable metrics for the characterization of the sinterability and flowability for these three powders are recommended. This study suggests spray freeze drying produces high-quality feedstock powder for binder jetting process.more » « less
-
more » « less
Shell printing is an advantageous binder jetting technique that prints only a thin shell of the intended object to enclose the loose powder in the core. In this study, powder packing in the shell and core was investigated for the first time. By examining the density and microstructure of the printed samples, powder packing was found to be different between the shell and core. In addition, the powder particle size and layer thickness were found to affect the powder packing in the shell and core differently. At a 200 µm layer thickness, for the 10 µm and 20 µm powders, the core was less dense than the shell and had a layered microstructure. At a 200 µm layer thickness, for the 70 µm powder, the core was denser and had a homogeneous microstructure. For the 20 µm powder, by reducing the layer thickness from 200 µm to 70 µm, the core became denser than the shell, and the microstructure of the core became homogeneous. The different results could be attributed to the different scenarios of particle rearrangement between the shell and core for powders of different particle sizes and at different layer thicknesses. Considering that the core was denser and more homogeneous than the shell when the proper layer thickness and powder particle size were selected, shell printing could be a promising method to tailor density and reduce anisotropy.
-
Abstract This technical brief reports an experimental investigation on the effect of feed region density on resultant sintered density and intermediate densities (powder bed density and green density) during the binder jetting additive manufacturing process. The feed region density was increased through compaction. The powder bed density and green density were determined by measuring the mass and dimension. The sintered density was measured with the Archimedes’ method. As the relative feed region density increased from 44% to 65%, the powder bed density increased by 5.7%, green density by 8.5%, and finally sintered density by 4.5%. Statistical testing showed that these effects were significant. This study showed that compacting the powder in the feed region is an effective method to alter the density of parts made via binder jetting additive manufacturing.more » « less
-
The primary advantage of the high energy ball milling (HEBM) process is its ability to synthesize a homogeneous mixture with submicron (up to nanoscale) particle size. This approach is a viable process for particle size reduction and grain refinement of magnetic powders, which affects their domain structure and by extension the resulting magnetic properties. In this research, we designed a 9-ball milling experiment by keeping the rotational speed constant at 300rpm and varying the ball-to-powder ratio of 5:1, 8:1, and 10:1 for 6hrs, lOhrs, and 14hrs milling times. The strontium ferrite magnetic powders subjected to HEBM were analyzed for crystallite size and behavior via XRD, particle size reduction via SEM/ImageJ software/originLabPro, and magnetic performance via powder-based VSM measurement. The magnetic performance of the ball-milled strontium ferrite powders shows a good combination of appreciable increment in the S-values (a ratio of the remanence to saturation magnetization) and a considerable decline in coercivity (<10% decrease) at 6hrs of milling duration. The particle size obtained at 6hr-8:1BPR is 0.59 µm with about 44% reduction from the 1.05 µm particle size of the unmilled strontium ferrites, which is within the reported single-domain particle critical size (0.5 µm - 0.65 µm). The particle size reduction of 0.59 µm at 6hr-8: lBPR would be beneficial in enabling strong interfacial bonding when the ballmilled strontium ferrite powders are used in polymer-bonded magnets.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1115/1.4050306