Title: Co-intercalation-free ether electrolytes for graphitic anodes in lithium-ion batteries
Carbonate-based electrolytes are widely used in Li-ion batteries but are limited by a small operating temperature window and poor cycling with silicon-containing graphitic anodes. The lack of non-carbonate electrolyte alternatives such as ether-based electrolytes is due to undesired solvent co-intercalation that occurs with graphitic anodes. Here, we show that fluoroethers are the first class of ether solvents to intrinsically support reversible lithium-ion intercalation into graphite without solvent co-intercalation at conventional salt concentrations. In full cells using a graphite anode, they enable 10-fold higher energy densities compared to conventional ethers, and better thermal stability over carbonate electrolytes (operation up to 60 °C) by producing a robust solvent-derived solid electrolyte interphase (SEI). As single-solvent–single-salt electrolytes, they remarkably outperform carbonate electrolytes with fluoroethylene carbonate (FEC) and vinylene carbonate (VC) additives when cycled with graphite–silicon composite anodes. Our molecular design strategy opens a new class of electrolytes that can enable next generation Li-ion batteries with higher energy density and a wider working temperature window.  more » « less
Award ID(s):
2144454 2011854
PAR ID:
10389275
Author(s) / Creator(s):
; ; ; ; ; ;
Date Published:
Journal Name:
Energy & Environmental Science
Volume:
15
Issue:
11
ISSN:
1754-5692
Page Range / eLocation ID:
4823 to 4835
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Silicon (Si) anodes are promising candidates for Li-ion batteries due to their high specific capacity and low operating potential. Implementation has been challenged by the significant Si volume changes during (de)lithiation and associated growth/regrowth of the solid electrolyte interphase (SEI). In this report, fluorinated local high concentration electrolytes (FLHCEs) were designed such that each component of the electrolyte (solvent, salt, diluent) is fluorinated to modify the chemistry and stabilize the SEI of high (30%) silicon content anodes. FLHCEs were formulated to probe the electrolyte salt concentration and ratio of the fluorinated carbonate solvents to a hydrofluoroether diluent. Higher salt concentrations led to higher viscosities, conductivities, and contact angles on polyethylene separators. Electrochemical cycling of Si-graphite/NMC622 pouch cells using the FLHCEs delivered up to 67% capacity retention after 100 cycles at a C/3 rate. Post-cycling X-ray photoelectron spectroscopy (XPS) analyses of the Si-graphite anodes indicated the FLHCEs formed a LiF rich solid electrolyte interphase (SEI). The findings show that the fluorinated local high concentration electrolytes contribute to stabilizing the Si-graphite electrode over extended cycling.

     
    more » « less
  2. Three different organic solvents (dimethylacetamide (DMAc), dimethylformamide (DMF), and dimethyl sulfoxide (DMSO)) were used to improve the solubility of LiNO 3 in a standard carbonate-based electrolyte with lithium difluoro(oxalato)borate (LiDFOB) as the salt. Together, the LiDFOB and organic-solvent solubilized LiNO 3 preferentially reduce on the surface of silicon-containing anodes to create an SEI rich in oxalates, nitrate decomposition species, and B-F species. The improved stability of the SEI throughout the first 100 cycles results in silicon and silicon/graphite composite anodes with better capacity retention than observed with standard electrolytes or fluoroethylene carbonate (FEC) containing electrolytes. This study demonstrates the feasibility of the use of non-traditional electrolyte solvents in the improvement and optimization of lithium ion-battery electrolytes. 
    more » « less
  3. Abstract

    Lithium‐ion batteries have remained a state‐of‐the‐art electrochemical energy storage technology for decades now, but their energy densities are limited by electrode materials and conventional liquid electrolytes can pose significant safety concerns. Lithium metal batteries featuring Li metal anodes, solid polymer electrolytes, and high‐voltage cathodes represent promising candidates for next‐generation devices exhibiting improved power and safety, but such solid polymer electrolytes generally do not exhibit the required excellent electrochemical properties and thermal stability in tandem. Here, an interpenetrating network polymer with weakly coordinating anion nodes that functions as a high‐performing single‐ion conducting electrolyte in the presence of minimal plasticizer, with a wide electrochemical stability window, a high room‐temperature conductivity of 1.5 × 10−4S cm−1, and exceptional selectivity for Li‐ion conduction (tLi+= 0.95) is reported. Importantly, this material is also flame retardant and highly stable in contact with lithium metal. Significantly, a lithium metal battery prototype containing this quasi‐solid electrolyte is shown to outperform a conventional battery featuring a polymer electrolyte.

     
    more » « less
  4. Abstract

    Despite significant progress in energy retention, lithium‐ion batteries (LIBs) face untenable reductions in cycle life under extreme fast‐charging (XFC) conditions, which primarily originate from a variety of kinetic limitations between the graphite anode and the electrolyte. Through quantitative Li+loss accounting and comprehensive materials analyses, it is directly observed that the operation of LIB pouch cells at 4 C||C/3 (charging||discharging) results in Li plating, disadvantageous solid‐electrolyte‐interphase formation, and solvent co‐intercalation leading to interstitial decomposition within graphite layers. It is found that these failure modes originate from the insufficient properties of conventional electrolytes, where employing a designed ester‐based electrolyte improved the capacity retention of these cells from 55.9% to 88.2% after 500 cycles when operated at the aforementioned conditions. These metrics are the result of effective mitigation of the aforementioned failure modes due to superior Li+transport and desolvation characteristics demonstrated through both experimental and computational characterization. This work reveals the vital nature of electrolyte design to XFC performance.

     
    more » « less
  5. Abstract

    Lithium‐ion batteries (LIBs) are increasingly encouraged to enhance their environmental friendliness and safety while maintaining optimal energy density and cost‐effectiveness. Although various electrolytes using greener and safer glyme solvents have been reported, the low charge voltage (usually lower than 4.0 V vs Li/Li+) restricts the energy density of LIBs. Herein, tetraglyme, a less‐toxic, non‐volatile, and non‐flammable ether solvent, is exploited to build safer and greener LIBs. It is demonstrated that ether electrolytes, at a standard salt concentration (1 m), can be reversibly cycled to 4.5 V vs Li/Li+. Anchored with Boron‐rich cathode‐electrolyte interphase (CEI) and mitigated current collector corrosion, the LiNi0.8Mn0.1Co0.1O2(NMC811) cathode delivers competitive cyclability versus commercial carbonate electrolytes when charged to 4.5 V. Synchrotron spectroscopic and imaging analyses show that the tetraglyme electrolyte can sufficiently suppress the overcharge behavior associated with the high‐voltage electrolyte decomposition, which is advantageous over previously reported glyme electrolytes. The new electrolyte also enables minimal transition metal dissolution and deposition. NMC811||hard carbon full cell delivers excellent cycling stability at C/3 with a high average Coulombic efficiency of 99.77%. This work reports an oxidation‐resilient tetraglyme electrolyte with record‐high 4.5 V stability and enlightens further applications of glyme solvents for sustainable LIBs by designing Boron‐rich interphases.

     
    more » « less